Abstract

A resistance spot welding method able to form a welded joint having delayed fracture resistance, includes, in order, applying a pressing force P1 (kN) to the plurality of steel sheets by welding electrodes while supplying a supplied current I1 (kA), while applying the pressing force P1, supplying a current Ic (kA) during a cooling time tc (s), repeating two times or more a pressure force raising and lowering cycle of supplying a supplied current I2 (kA) to the welding electrodes while applying a pressing force P2 (kN) to the plurality of steel sheets by the welding electrodes during a pressing time tf (s), then immediately applying a pressing force P3 (kN) during a pressing time ti (s), applying the pressing force P2 during the pressing time tf, and releasing the pressing force and ending the supply of current, satisfying 0≤Ic<I1, 0.3≤I2/I1<1.0, P2/P1≥2, tf≤0.2, P3<P2, and ti≤0.2.

First claim

The invention claimed is:

1. A method of resistance spot welding a plurality of steel sheets with at least overlapping welding locations,
the plurality of steel sheets including at least one steel sheet with a tensile strength of 980 MPa or more,
the method comprising the steps of, in order,
applying a pressing force P1 (kN) to the plurality of steel sheets by welding electrodes while supplying a current I1 (kA);
supplying a current Ic (kA) during a cooling time tc (s), while applying the pressing force P1;
repeating two times or more a pressure force raising and lowering cycle of supplying a current I2 (kA) to the welding electrodes while applying a pressing force P2 (kN) to the plurality of steel sheets by the welding electrodes during a pressing time tf (s), then immediately applying a pressing force P3 (kN) during a pressing time ti (s);
applying the pressing force P2 during the pressing time tf; and
releasing the pressing force and ending the supply of current I2 (kA),
wherein the supplied current Ic satisfies the following formula (1), the supplied current I2 satisfies the following formula (2), the pressing force P2 satisfies the following formula (3), the pressing time tf satisfies the following formula (4), the pressing force P3 satisfies the following formula (5), and the pressing time ti satisfies the following formula (6):
0≤ Ic<I 1  (1)

0.3≤ I 2/ I 1<1.0  (2)

P 2/ P 1≥1.2  (3)

tf≤ 0.2  (4)

P 3< P 2  (5)

ti≤ 0.2  (6).

Assignees

• Nippon Steel & Sumitomo Metal Corp
• Nippon Steel Corp

Inventors

• Furusako Seiji

Classifications

• B23K2103/04

  Steel {or steel} alloys · CPC title

• B23K2101/34

  Coated articles {; Surface treated articles} · CPC title

• B23K2101/18

  Sheet panels · CPC title

• B23K2101/006

  Vehicles · CPC title

• B23K11/241

  Electric supplies (B23K11/248 takes precedence) · CPC title