Electrodeposited copper foil with anti-burr property

Patent metadata

Field	Value
Publication number	US-10923730-B2
Application number	US-201916353842-A
Country	US
Kind code	B2
Filing date	Mar 14, 2019
Priority date	Mar 14, 2019
Publication date	Feb 16, 2021
Grant date	Feb 16, 2021

Abstract

Electrodeposited copper foils possessing properties for manufacturing lithium ion rechargeable secondary batteries are described, including methods of making the electrodeposited copper foils, methods for making the battery, and the resultant battery. The electrodeposited copper foils have a specific burst strength in the range of 1.5 to 4.3 kPa*m 2 /g and a tensile strength in the range of 30 to 40 kgf/mm 2 . The deposited side of the electrodeposited copper foil has a surface hardness in the range of 0.2 to about 2.0 Gpa by nano indentation analysis to resist wrinkling during pressing of the active materials on the electrodeposited copper foil. The foil exhibits reduced copper burr formation and burr size after clipping.

First claim

We claim:

1. An electrodeposited copper foil having a deposited side and a drum side comprising:
a specific burst strength measured in accordance with IPC-TM-650 2.4.2 in the range of 1.5 to 4.3 kPa*m 2 /g;
a tensile strength in the range of 30.2 to 39.8 kgf/mm 2 ;
wherein the deposited side exhibits a hardness in the range of 0.2-2.0 GPa by nano indentation analysis measured at a depth of 300 nm; and,
wherein the electrodeposited copper foil exhibits a reduced copper burr property on a clipping edge of the electrodeposited copper foil, wherein the reduced copper burr property defined as the number of copper burrs per 5 cm of the clipping edge, is in the range of 0˜9, and that a maximum length of any copper burr on the clipping edge is 35 μm; and wherein the electrodeposited copper foil, after roll pressing, does not include wrinkles.

2. The electrodeposited copper foil of claim 1 further exhibiting
an elongation in the range of 5.1 to 21.4%.

3. The electrodeposited copper foil of claim 1 , wherein copper burr length is in the range of 1 μm to 35 μm.

4. A current collector for a lithium ion secondary rechargeable battery comprising the electrodeposited copper foil of claim 1 .

5. A lithium ion secondary rechargeable battery comprising the current collector of claim 4 , exhibiting a charge/discharge cycle life of more than 1000 times.

6. A rechargeable lithium ion secondary battery comprising the electrodeposited copper foil of claim 1 as a component thereof.

7. The rechargeable lithium ion secondary battery of claim 6 , wherein the battery is a laminated battery comprising alternating anode and cathode layers, with a separator layer between the alternating anode and cathode layers.

8. The rechargeable lithium ion secondary battery of claim 6 having a charge/discharge cycle life in excess of 1000 times.

9. A capacitor comprising the electrodeposited copper foil according to claim 2
wherein the capacitor further comprises at least a second copper foil; wherein the electrodeposited copper foil and the at least second copper foil are separated by a dielectric layer.

10. An electrode comprising the electrodeposited copper foil of claim 1 in combination with a pressure consolidated anode active substance.

11. The electrode of claim 10 , further comprising an electrically conductive additive.

Assignees

• Chang Chun Petrochemical Co Ltd

Inventors

• Lai Yao-Sheng
• Cheng Kuei-Sen
• Chou Jui-Chang
• Lai Chien-Ming

Classifications

• H01G11/68

  characterised by their material · CPC title

• H01M10/0525

  Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries · CPC title

• C25D3/38

  of copper · CPC title

• C25D1/04 Primary

  Wires; Strips; Foils · CPC title

• H01M4/624

  Electric conductive fillers · CPC title