Fabric print media

Patent metadata

Field	Value
Publication number	US-10906343-B2
Application number	US-201616069815-A
Country	US
Kind code	B2
Filing date	May 12, 2016
Priority date	May 12, 2016
Publication date	Feb 2, 2021
Grant date	Feb 2, 2021

Abstract

The present disclosure is drawn to a fabric print medium including a fabric substrate, a primary coating layer, and a secondary coating layer. The fabric substrate can have a first side and a second side. The primary coating layer can be applied to the first side of the fabric substrate at a thickness from 2 μm to 250 μm with a dry coat weight ranging from about 5 gsm to about 300 gsm and can include a polymeric binder and filler particles. The secondary coating layer can be applied to the primary coating layer at a thickness from 1 μm to 50 μm with a dry coat weight ranging from 0.5 gsm to 50 gsm and can include a first crosslinked polymeric network and a second crosslinked polymeric network. The primary coating layer can be two or more times thicker than the secondary coating layer.

First claim

What is claimed is:

1. A fabric print medium, comprising:
a fabric substrate including a first side and a second side;
a primary coating layer applied to the first side of the fabric substrate at a thickness from 2 μm to 250 μm with a dry coat weight ranging from about 5 gsm to about 200 gsm, the primary coating layer comprising a polymeric binder and filler particles; and
a secondary coating layer applied to the primary coating layer at a thickness from 1 μm to 50 μm with a dry coat weight ranging from 0.5 gsm to 50 gsm, the secondary coating layer comprising a first crosslinked polymeric network and a second crosslinked polymeric network, wherein the first crosslinked polymeric network and the second crosslinked polymeric network collectively make up from 80 wt % to 100 wt % of the secondary coating layer, wherein the primary coating layer is two or more times thicker than the secondary coating layer.

2. The fabric print medium of claim 1 , wherein the fabric substrate comprises wool, cotton, silk, linen, jute, flax, hemp, rayon, corn starch, tapioca, sugarcane, polyvinyl chloride, polyester, polyamide, polyimide, polyacrylic, polyacrylic polypropylene, polyethylene, polyurethane, polystyrene, polyaramid, polytetrafluoroethylene, polyethylene terephthalate, fiberglass, polytrimethylene, polycarbonate, polyester terephthalate, polybutylene terephthalate, or a combination thereof.

3. The fabric print medium of claim 1 , wherein the polymeric binder has a weight average molecular weight from 5,000 Mw to 200,000 Mw and comprises a polyacrylate, polyurethane, vinyl-urethane, acrylic urethane, polyurethane-acrylic, polyether polyurethane, polyester polyurethane, polycaprolactam polyurethane, polyether polyurethane, alkyl epoxy resin, epoxy novolac resin, polyglycidyl resin, polyoxirane resin, polyamine, styrene maleic anhydride, polystyrene-butadiene emulsion, acrylonitrile butadiene latex, starch, gelatin, casein, soy protein polymer, carboxy-methyl cellulose, hydroxyethyl cellulose, acrylic emulsion, vinyl acetate emulsion, vinylidene chloride emulsion, polyester emulsion, polyvinylpyrroilidene, polyvinyl alcohol, styrene butadiene emulsions, a derivative thereof, or a combination thereof.

4. The fabric print medium of claim 1 , wherein the primary coating layer further comprises a flame retardant and the flame retardant comprises mineral powder, organohalogenated compound, a polymeric brominated compound, metal and phosphorus containing composition, or combination thereof, and wherein the flame retardant comprises from 1 wt % to 50 wt % of the primary coating layer based on dry weight of the primary coating layer.

5. The fabric print medium of claim 1 , wherein the filler particles exhibit flame retardant properties and comprises from 5 wt % to about 95 wt % of the primary coating layer based on dry weight of the primary coating layer, wherein the filler particles have an average particle size from 0.1 μm to 20 μm, and wherein the filler particles include mineral powder, aluminum hydroxide, alumina trihydrate, magnesium hydroxide, magnesium calcium carbonate, poly-salt, ammonium polyphosphate, organochlorine, chlorendic acid derivative, chlorinated paraffin, organobromine, decabromodiphenyl ether, decabromodiphenyl ethane, polymeric brominated compound, brominated polystyrene, brominated carbonate oligomer, brominated epoxy oligomer, tetrabromophthalic anyhydride, tetrabromobisphenol A, hexabromocyclododecane, organohalogenated compound, metal oxide, phosphorus containing composition, phosphorus and halogen containing composition, nitrogen containing composition, halogen containing composition, organophosphate, or combination thereof.

6. The fabric print medium of claim 1 , wherein the filler particles include alumina trihydrate.

7. The fabric print medium of claim 1 , wherein the primary coating layer includes air voids within the primary coating layer generated by injecting a primary coating composition that is used to form the primary coating layer with air bubbles prior to application to the fabric substrate.

8. The fabric print medium of claim 1 , wherein the first crosslinked polymeric network and the second crosslinked polymeric network are different and independently comprises polyacrylate, polyurethane, vinyl-urethane, acrylic urethane, polyurethane-arcylic, polyether polyurethane, polyester polyurethane, polycaprolactam polyurethane, polyether polyurethane, alkyl epoxy resin, epoxy novolac resin, polyglycidyl resin, polyoxirane resin, polyamine, styrene maleic anhydride, a derivative thereof, or a combination thereof.

9. The fabric print medium of claim 1 , wherein the first crosslinked polymeric network and the second crosslinked polymeric network are further crosslinked to each other.

10. The fabric print medium of claim 1 , wherein the secondary coating layer further comprises from 1 wt % to 20 wt % of a wax and the wax comprises synthetic wax, petroleum wax, vegetable wax, animal wax, mineral wax, paraffin wax, microcrystalline wax, polyethylene wax, or a combination thereof.

11. A method of preparing the fabric print medium of claim 1 , comprising:
applying a primary coating composition to the first side of the fabric substrate to form the primary coating layer thereon, the primary coating composition having a viscosity range from about 1,000 cps to about 50,000 cps; and
applying a secondary coating composition to the primary coating layer to form the secondary coating layer thereon.

12. The method of claim 11 , further comprising injecting air into the primary coating composition a density ranging from 0.3 g/cm 3 to 0.8 g/cm 3 prior to applying the primary coating composition to the first side to generate and retain air voids in the primary coating layer after drying.

13. The method of claim 11 , further comprising applying pressure using pressure nips or off-line calender to the fabric media after applying the primary coating composition, and wherein the step of applying the primary coating composition and the secondary coating composition comprises a floating knife process, a knife on roll mechanism process, or a transfer coating process.

14. A fabric print medium, comprising:
a fabric substrate comprising a first side and a second side;
a primary coating layer applied to the first side and the second side of the fabric substrate at an independent thickness from 2 μm to 250 μm with an independent dry coat weight ranging from about 5 gsm to about 200 gsm, the primary coating layer independently comprising a polymeric binder and filler particles; and
a secondary coating layer applied to the primary coating layer on both the first side and the second side at an independent thickness from 1 μm to 50 μm with an independent dry coat weight ranging from 0.5 gsm to 50 gsm, the secondary coating layer independently comprising a first crosslinked polymeric network and a second crosslinked polymeric network, wherein the first crosslinked polymeric network and the second crosslinked polymeric network collectively make up from 80 wt % to 100 wt % of the secondary coating layer,
wherein the primary coating layer is two or more times thicker than the secondary coating layer on both sides.

15. The fabric print medium of claim 14 , wherein the primary coating layer on both sides includes air voids generated by injecting a primary coating composition that is used to form the primary coating layers with air bubbles prior to application to the fabric substrate.

16. The fabric print medium of claim 1 , wherein the first crosslinked polymeric network and the second crosslinked polymeric network collectively m

Assignees

• Hewlett Packard Development Co

Inventors

• Zhou Xiaoqi
• Pirayesh Francois K
• Courtenay Silke

Classifications

• D06P1/5214

  Polymers of unsaturated compounds containing no COOH groups or functional derivatives thereof · CPC title

• D06N3/144

  with polyurethane and polymerisation products, e.g. acrylics, PVC · CPC title

• B41M5/5281

  Polyurethanes or polyureas · CPC title

• D06N3/042

  Acrylic polymers (D06N3/045 takes precedence) · CPC title

• B32B27/20

  using fillers, pigments, thixotroping agents · CPC title