Powder-based additive manufacturing process

Patent metadata

Field	Value
Publication number	US-10899074-B2
Application number	US-201816764524-A
Country	US
Kind code	B2
Filing date	Dec 13, 2018
Priority date	Dec 20, 2017
Publication date	Jan 26, 2021
Grant date	Jan 26, 2021

Abstract

The invention relates to an additive manufacturing process (3D printing) using particles having a meltable polymer. The meltable polymer comprises a thermoplastic polyurethane polymer which has a melting range (DSC, Differential Scanning calorimetry; second heating at heating rate 5 K/min) of 160 to 270° C. and a Shore D hardness according to DIN ISO 7619-1 of 50 or more and which, at a temperature T, has a melt volume rate (melt volume rate (MVR)) according to ISO 1133 of 5 to 15 cm/10 min and a change of the MVR, when this temperature T increases by 20° C., of greater than or equal to 90 cm3/10 min. The invention also relates to an item which can be obtained by means of the method.

First claim

The invention claimed is:

1. A method of producing an article, comprising:
applying a layer of particles to a target surface, wherein at least some of the particles include a fusible polymer;
introducing energy into a selected portion of the layer corresponding to a cross section of the article in a chamber to bond the particles in the selected portion to form a bonded portion; and
repeating the steps of applying and introducing energy for a multitude of layers to bond the bonded portions of adjacent layers in order to form the article;
wherein the fusible polymer comprises a thermoplastic polyurethane polymer having:
a melting range of 160° C. to 270° C. based on differential scanning calorimetry of a second heating run at a heating rate of 20 K/m in,
a Shore D hardness of 50 or more based on DIN ISO 7619-1,
a melt volume flow rate at a temperature T of 5 to 15 cm 3 /10 min based on ISO 1133, and
a change in the melt volume flow rate of ≥90 cm 3 /10 min in the event of an increase of temperature T by 20° C.

2. The method as claimed in claim 1 , wherein introducing energy into a selected portion of the layer corresponding to a cross section of the article to bond the particles in the selected portion comprises:
irradiating the selected portion of the layer corresponding to a cross section of the article with an energy beam to bond the particles in the selected portion.

3. The method as claimed in claim 1 , wherein introducing energy into a selected portion of the layer corresponding to a cross section of the article to bond the particles in the selected portion comprises:
applying a liquid to a selected portion of the layer corresponding to a cross section of the article, wherein said liquid increases the absorption of energy in regions of the layer with which it comes into contact relative to regions with which it does not come into contact;
irradiating the layer so that the particles in regions of the layer contacted with the liquid are bonded to one another and the particles in regions of the layer not contacted by the liquid are not bonded to one another.

4. The method as claimed in claim 1 , wherein the particles applied are at least intermittently heated or cooled.

5. The method as claimed in claim 1 , wherein the thermoplastic polyurethane polymer has a Shore hardness of ≥50 Shore D to ≤85 Shore D based on DIN ISO 7619-1.

6. The method as claimed in claim 1 , wherein the fusible polymer comprises a further polymer selected from the group consisting of polyester, ABS, polycarbonate, and a combination of at least two of these.

7. The method as claimed in claim 6 , wherein the fusible polymer is a blend comprising the polyurethane polymer and ABS, wherein the polyurethane polymer has a melting point of ≥160° C. based on differential scanning calorimetry of a second heating run at heating rate 20 K/min and a proportion of the ABS in the blend is ≥1% by weight to ≤40% by weight, based on a total weight of the blend.

8. The method as claimed in claim 6 , wherein the fusible polymer is a blend comprising the polyurethane polymer and a polyester, wherein the polyurethane polymer has a melting point of ≥160° C. based on differential scanning calorimetry of a second heating run at heating rate 20 K/min and a proportion of polyester in the blend is ≤1% by weight to ≤40% by weight, based on a total weight of the blend.

9. The method as claimed in claim 6 , wherein the fusible polymer is a blend comprising the polyurethane polymer and a polycarbonate based on bisphenol A and/or bisphenol TMC, wherein the polyurethane polymer has a melting point of ≥160° C. based on differential scanning calorimetry of a second heating run at heating rate 20 K/min and a proportion of polycarbonate in the blend is ≥1% by weight to ≤40% by weight, based on a total weight of the blend.

10. The method as claimed in claim 1 , wherein at least some of the particles include the fusible polymer and a further polymer and/or an inorganic particles.

11. The method as claimed in claim 1 , further comprising subjecting the article to an aftertreatment comprising: mechanical smoothing of the surface, controlled local heating, heating of the entire article, controlled local cooling, cooling of the entire article, contacting of the article with steam, contacting of the article with the vapor of an organic solvent, irradiating the article with electromagnetic radiation, immersing the article into a liquid bath, or a combination of at least two of these.

12. The method as claimed in claim 1 , wherein the particles are at least partly suspended in a liquid phase after applying the layer of particles to the target surface.

13. The method as claimed in claim 1 , wherein a portion of the particles that includes the fusible polymer retains their original flowability after storage at 150° C. under a nitrogen atmosphere for 8 hours.

14. A thermoplastic pulverulent composition, comprising pulverulent thermoplastic polyurethane obtained from a reaction of the following components:
a) at least one organic diisocyanate;
b) at least one compound having groups reactive toward isocyanate groups and having a number-average molecular weight of 500 g/mol to 6000 g/mol and a number-average functionality of a sum total of the components b) of 1.8 to 2.5;
c) at least one chain extender having a number-average molecular weight of 60 to 450 g/mol and a number-average functionality of the sum total of the chain extenders c) of 1.8 to 2.5;

in the presence of
d) optionally catalysts;
e) optionally auxiliaries and/or additives; and
f) optionally one or more chain terminators;

wherein the thermoplastic polyurethane has a melting range of 160 to 270° C. based on differential scanning calorimetry of a second heating run at heating rate 5 K/min, a Shore D hardness of 50 or more based on DIN ISO 7619-1, a melt volume flow rate at a temperature T of 5 to 15 cm 3 /10 min based on ISO 1133, and a change in melt volume flow rate of ≥90 cm 3 /10 min in the event of an increase in temperature T by 20° C., and
wherein the thermoplastic pulverulent composition is for production of articles in a powder based additive manufacturing method comprising:
applying a layer of particles to a target surface, wherein at least some of the particles include a fusible polymer, and wherein the fusible polymer comprises the thermoplastic polyurethane;
introducing energy into a selected portion of the layer corresponding to a cross section of the article in a chamber to bond the particles in the selected portion to form a bonded portion; and
repeating the steps of applying and introducing energy for a multitude of layers to bond the bonded portions of adjacent layers in order to form the article.

Assignees

• Covestro Deutschland Ag

Inventors

• Achten Dirk
• Buesgen Thomas
• Kessler Michael
• Reichert Peter
• Mettmann Bettina

Classifications

• B22F10/66

  by mechanical means · CPC title

• B22F10/64

  by thermal means (control of energy beam parameters for post heating B22F10/364) · CPC title

• B22F10/62

  by chemical means · CPC title

• B22F12/41

  characterised by the type, e.g. laser or electron beam · CPC title

• B22F10/28

  Powder bed fusion, e.g. selective laser melting [SLM] or electron beam melting [EBM] · CPC title