Polymer composition for caps and closures

Patent metadata

Field	Value
Publication number	US-10889708-B2
Application number	US-201716324070-A
Country	US
Kind code	B2
Filing date	Aug 10, 2017
Priority date	Aug 11, 2016
Publication date	Jan 12, 2021
Grant date	Jan 12, 2021

Abstract

Caps and closures comprising high density polyethylene, polyolefin elastomer and polypropylene wherein the amount of high density polyethylene is more than 50% by weight of the total amount of high density polyethylene, polyolefin elastomer and polypropylene and wherein the total amount of high density polyethylene, polyolefin elastomer and polypropylene is 100% by weight.

First claim

The invention claimed is:

1. Caps and closures comprising:
a high density polyethylene, a polyolefin elastomer, and a polypropylene wherein the amount of high density polyethylene is more than 50% by weight of the total amount of the high density polyethylene, the polyolefin elastomer and the polypropylene,
wherein the total amount of high density polyethylene, polyolefin elastomer and polypropylene is 100% by weight, and
wherein the polyolefin elastomer is an ethylene-alpha olefin copolymer derived from two monomers consisting of ethylene and an alpha olefin containing 4-10 carbon atoms.

2. The caps and closures according to claim 1 , comprising the high density polyethylene in a range between ≥52% by weight and ≤100% by weight.

3. The caps and closures according to claim 1 , comprising the polypropylene in a range between >0.1% by weight and ≤40% by weight.

4. The caps and closures according to claim 1 , comprising the polyolefin elastomer in a range between >0.1% by weight and ≤40% by weight.

5. The caps and closures according to claim 1 , comprising the high density polyethylene in a range between >50% by weight and <100% by weight and the polypropylene in a range between >0.1% by weight and ≤40% by weight and the polyolefin elastomer in a range between >0.1% by weight and ≤40% by weight.

6. The caps and closures according to claim 1 , comprising the high density polyethylene in a range between >55% by weight and <100% by weight and the polypropylene in a range between ≥5% by weight and ≤35% by weight and the polyolefin elastomer in a range between ≥2% by weight and ≤20% by weight.

7. The caps and closures according to claim 1 , comprising the high density polyethylene in a range between ≥55% by weight and <80% by weight and the polypropylene in a range between ≥10% by weight and ≤30% by weight and the polyolefin elastomer in a range between ≥5% by weight and ≤20% by weight.

8. The caps and closures according to claim 1 , wherein an MFI of the high density polyethylene ranges between ≥0.1 and ≤30 g/10 min (measured according to ISO 1133 at 190 degrees Celsius and 2.16 kg) and/or a density of the high density polyethylene ranges between ≥950 and ≤958 kg/m 3 (measured according to ISO 1183).

9. The caps and closures according to claim 1 , wherein an MFI of the high density polyethylene ranges between ≥0.6 and ≤15 g/10 min (measured according to ISO 1133 at 190 degrees Celsius and 2.16 kg) and/or a density of the high density polyethylene ranges between >950 and <955 kg/m 3 (measured according to ISO 1183).

10. The caps and closures according to claim 1 , wherein an MFI of polypropylene ranges between 0.3 and 100 g/10 min (measured according to ISO1133 at 230 degrees Celsius and 2.16 kg) and/or a density of polypropylene ranges between ≥900 and ≤920 kg/m 3 (measured according to ISO 1183).

11. The caps and closures according to claim 1 , wherein an MFI of the polypropylene ranges between 0.3 and 10 g/10 min (MFI is determined according to ISO 1133 at 230 degrees Celsius and 2.16 kg) and/or a density of the polypropylene ranges between >902 and <906 kg/m 3 (measured according to ISO 1183).

12. The caps and closures according to claim 1 , wherein an MFI of the polyolefin elastomer ranges between ≥0.5 and ≤30 g/10 min (measured according to ASTM D1238 at 190 degrees Celsius and 2.16 kg) and/or a density of the polyolefin elastomer ranges between ≥857 and ≤880 kg/m 3 (measured according to ASTM D1505).

13. The caps and closures according to claim 1 , wherein the ethylene-alpha olefin copolymer is ethylene-octene copolymer.

14. The caps and closures according to claim 1 , wherein the polypropylene is impact polypropylene.

15. The caps and closures according to claim 1 , wherein an amount of high density polyethylene is higher than an amount of the polypropylene and wherein this is based on the wt % of the high density polyethylene and the wt % of the polypropylene and/or the amount of the polypropylene is higher than the amount of the polyolefin elastomer and wherein this is based on the wt % of the polypropylene and the wt % of the polyolefin elastomer.

16. The caps and closures according to claim 1 , wherein an MFI of the polyolefin elastomer ranges between ≥0.6 and ≤10 g/10 min (measured according to ASTM D1238 at 190 degrees Celsius and 2.16 kg) and/or a density of the polyolefin elastomer ranges between ≥865 and ≤870 kg/m 3 (measured according to ASTM D1505).

17. The caps and closures according to claim 1 , wherein an MFI of the polyolefin elastomer ranges between ≥0.6 and ≤10 g/10 min (measured according to ASTM D1238 at 190 degrees Celsius and 2.16 kg) and a density of the polyolefin elastomer ranges between ≥865 and ≤870 kg/m 3 (measured according to ASTM D1505).

18. The caps and closures according to claim 1 , comprising
the high density polyethylene in a range between ≥55% by weight and ≤70% by weight;
the polypropylene in a range between >5% by weight and <35% by weight; and

the polyolefin elastomer in a range between ≥2% by weight and ≤20% by weight.

19. The caps and closures according to claim 18 , comprising
the polypropylene in a range between >10% by weight and <30% by weight; and
the polyolefin elastomer in a range between ≥5% by weight and ≤20% by weight.

20. Caps and closures comprising:
a high density polyethylene in a range between >55% by weight and <80% by weight,
a polyolefin elastomer in a range between ≥5% by weight and ≤20% by weight, and
a polypropylene in a range between ≥10% by weight and ≤30% by weight,
each based on the total amount of the high density polyethylene, the polyolefin elastomer and the polypropylene, wherein the total amount of high density polyethylene, polyolefin elastomer and polypropylene is 100% by weight, and
wherein the polyolefin elastomer is ethylene-octene copolymer.

Assignees

• Sabic Global Technologies Bv

Inventors

• Tandler Renate Francisca
• Sevriens Antonius
• Hildebrandt Haika Johanna
• Sthijns Johannes Petrus Joseph Gerardus
• Rasquin Philippe
• Lovera Deliani

Classifications

• B65D41/00 Primary

  Caps, e.g. crown caps or crown seals, i.e. members having parts arranged for engagement with the external periphery of a neck or wall defining a pouring opening or discharge aperture; Protective cap-like covers for closure members, e.g. decorative covers of metal foil or paper (clamping or other pressure-applying devices for securing or retaining closure members B65D45/00) · CPC title

• C08L23/06

  Polyethylene · CPC title

• C08F2500/08

  Low density, i.e. < 0.91 g/cm3 · CPC title

• C08F210/06

  Propene · CPC title

• C08L23/142 Primary

  at least partially crystalline copolymers of propene with other olefins · CPC title