Adhesion promoter for coating compositions suitable for producing surfacer coats

Patent metadata

Field	Value
Publication number	US-10870764-B2
Application number	US-201515513599-A
Country	US
Kind code	B2
Filing date	Jul 31, 2015
Priority date	Sep 24, 2014
Publication date	Dec 22, 2020
Grant date	Dec 22, 2020

Abstract

The present invention relates to a mixture (M) which can be used as curing agent and as adhesion promoter and which comprises at least two components (M1) and (M2), which are different from one another and have in each case independently of one another free and/or blocked isocyanate groups, and which optionally comprises a further component (M3) different from (M1) and (M2); component (M1) comprises at least one aliphatic polyisocyanate, and component (M2) comprises at least one aliphatic polyisocyanate having polyether units, wherein the relative weight ratio of (M1) and (M2) in (M) to one another is in a range from 25:1 to 3:1, based in each case on the solids content of (M1) and (M2), and at least one of the components (M1), (M2), and optionally (M3) present in (M) has hydrolyzable silane groups, to a use of (M) as curing agent and adhesion promoter in a coating composition, to such a coating composition, and to methods for at least partly coating a substrate with a surfacer coat and for at least partly coating a substrate with a multicoat paint system.

First claim

What is claimed is:

1. A mixture (M) comprising at least two components (M1) and (M2), which are different from one another and comprise in each case independently of one another free and/or blocked isocyanate groups, and which mixture optionally comprises a further component (M3) different from (M1) and (M2);
wherein component (M1) comprises at least one aliphatic polyisocyanate, wherein component (M1) has an NCO content in a range from 8 to 25 wt. % based on total weight of component (M1),
component (M2) comprises at least one aliphatic polyisocyanate having polyether units, the relative weight ratio of components (M1) and (M2) in the mixture (M) to one another is in a range from 25:1 to 3:1, based in each case on the solids content of components (M1) and (M2), and
wherein the mixture (M) is obtained by mixing components (M1) and (M2) and optional component (M3) and then partly reacting the isocyanate groups of components (M1) and (M2) with at least one hydrolyzable silane compound which has at least one functional group that is reactive toward isocyanate groups such that 5 to 30 mol % of all the isocyanate groups originally present in components (M1) and (M2) are reacted with the at least one hydrolyzable silane compound, such that each of components (M1) and (M2) contain a hydrolyzable silane group after reaction.

2. The mixture as claimed in claim 1 , wherein the relative weight ratio of components (M1) and (M2) in the mixture (M) to one another is in a range from 20:1 to 5:1, based in each case on the solids content of components (M1) and (M2).

3. The mixture as claimed in claim 1 , wherein a content of component (M2) in the mixture (M) is at least 5 wt %, based on the total solids content of the mixture (M).

4. The mixture as claimed in claim 1 , wherein the mixture (M) is a solvent-containing dispersion at least of components (M1) and (M2) and also optionally (M3).

5. The mixture as claimed in claim 1 , further comprising:
at least one polymeric resin (N), different from components (M1) and (M2) and (M3) of the mixture (M), and
at least one pigment (P).

6. The mixture as claimed in claim 5 , wherein the mixture comprises components (M1), (M2), and (M3) in an amount in a range from 5 to 25 wt %, based on the total weight of the mixture.

7. The mixture as claimed in claim 5 , wherein the polymeric resin (N) is selected from the group consisting of polyurethanes, polyesters, epoxy resins, poly(meth)acrylates, corresponding copolymers of these polymers, and mixtures thereof.

8. The mixture as claimed in claim 5 , wherein the mixture
comprises the at least one polymeric resin (N) in an amount in a range from 10 to 35 wt %, based on the total weight of the mixture, and
comprises the at least one pigment (P) in an amount in a range from 5 to 40 wt %, based on the total weight of the mixture.

9. The mixture as claimed in claim 5 , wherein the coating composition is suitable for at least partly coating a substrate, optionally coated at least partly at least with a primer coat, with a surfacer coat.

10. The mixture of claim 1 , wherein the free and/or blocked isocyanate group is stable at a temperature of from 18 to 23° C.

11. The mixture as claimed in claim 1 , Wherein the mixture is suitable as a curing agent and as an adhesion promoter.

12. The mixture as claimed in claim 1 , wherein mixture (M) further comprises component (M3), and wherein component (M3) has hydrolyzable silane groups.

13. The mixture as claimed in claim 1 , wherein 5 to 20 mol % of all the isocyanate groups originally present in components (M1) and (M2) are reacted with the at least one hydrolyzable silane compound.

14. The mixture as claimed in claim 1 , wherein component (M1) comprises an oligomer and/or polymer of a diisocyanate, and is selected from the group consisting of urethanes, allophanates, biurets and isocyanurates.

15. The mixture as claimed in claim 1 , wherein component (M2) comprises an oligomer and/or polymer of a diisocyanate, and is selected from the group consisting of urethanes, allophanates, biurets and isocyanurates.

16. A mixture (M) comprising at least two components (M1) and (M2), which are different from one another and comprise in each case independently of one another free and/or blocked isocyanate groups, and which mixture optionally comprises a further component (M3) different from (M1) and (M2);
wherein component (M1) comprises at least one aliphatic polyisocyanate,
component (M2) comprises at least one aliphatic polyisocyanate having polyether units, wherein component (M2) contains no uretdione groups,
the relative weight ratio of components (M1) and (M2) in the mixture (M) to one another is in a range from 25:1 to 3:1, based in each case on the solids content of components (M1) and (M2), and
wherein the mixture (M) is obtained by mixing components (M1) and (M2) and optional component (M3) and then partly reacting the isocyanate groups of components (M1) and (M2) with at least one hydrolyzable silane compound which has at least one functional group that is reactive toward isocyanate groups such that 5 to 30 mol % of all the isocyanate groups originally present in components (M1) and (M2) are reacted with the at least one hydrolyzable silane compound, such that each of components (M1) and (M2) contain a hydrolyzable silane group after reaction.

17. A method for at least partly coating a substrate, optionally at least partly coated at least with a primer coat, with a surfacer coat, the method comprising at least partly contacting the substrate with the mixture as claimed in claim 5 .

18. A method for at least partly coating a substrate with a multicoat paint system, the method comprising
optionally at least partly applying a primer coat to a substrate,
at least partly contacting the substrate, optionally at least partly coated at least with the primer coat, with the mixture as claimed in claim 8 , thereby at least partly applying a surfacer coat to the substrate optionally coated at least partly at least with the primer coat,
applying a basecoat film to the surfacer coat, and
applying a clearcoat film to the basecoat film.

19. The method of claim 18 , wherein an adhesion between the surfacer coat and the substrate is from 0 to 1.5, as measured by cross-cut testing after storage for a time of 16 hours at 40° C.

20. The method of claim 18 , wherein an adhesion between the surfacer coat and the substrate is from 0.5 to 2, as measured by cross-cut testing after 3 hours after storage for 10 days under constant humidity conditions.

Assignees

• Basf Coatings Gmbh

Inventors

• Andersen Audree
• Niemeier Manuela
• Hesener Simone

Classifications

• C08G18/62 Primary

  Polymers of compounds having carbon-to-carbon double bonds · CPC title

• C08G2150/50

  Compositions for coatings applied by spraying at least two streams of reaction components · CPC title

• C08G18/809

  containing silicon · CPC title

• C09D175/04

  Polyurethanes · CPC title

• C08G18/792

  formed by oligomerisation of aliphatic and/or cycloaliphatic isocyanates or isothiocyanates · CPC title