Solvent cement formulations

Patent metadata

Field	Value
Publication number	US-10865331-B2
Application number	US-201716074542-A
Country	US
Kind code	B2
Filing date	Feb 3, 2017
Priority date	Feb 5, 2016
Publication date	Dec 15, 2020
Grant date	Dec 15, 2020

Abstract

Provided are solvent cement formulations comprising some or all of tetrahydrofuran, cyclohexanone, methyl ethyl ketone, acetone, a thermoplastic resin, silica, and, a solvent soluble acrylic copolymer associative thickener. The disclosed formulations contain a reduced complement of volatile organic compounds (VOCs) relative to conventional cement formulations, yet are capable of meeting the requirements for regular-, medium-, and heavy-duty applications. The use of specialized associative thickener components confers a required degree of viscosity while enabling a reduction in the concentration of VOCs, such as tetrahydrofuran.

First claim

What is claimed:

1. A solvent cement formulation comprising:
0-19% tetrahydrofuran;
21-49% cyclohexanone;
7-21% methyl ethyl ketone;
21-36% acetone;
8-15% polyvinyl chloride;
0.5-5% silica; and,
0.01-0.4% of a solvent soluble acrylic copolymer associative thickener,
wherein the percent value of all named components do not exceed 100.

2. The solvent cement formulation according to claim 1 comprising:
0-17% tetrahydrofuran;
23-47% cyclohexanone;
9-23% methyl ethyl ketone
23-34% acetone
10-13% polyvinyl chloride
1-4% silica; and,
0.02-0.4% of said thickener.

3. The solvent cement formulation according to claim 1 comprising:
40-49% cyclohexanone;
7-21% methyl ethyl ketone;
21-36% acetone;
8-15% polyvinyl chloride;
0.5-5% silica; and,
0.01-0.4% of said thickener,

wherein said formulation does not include any tetrahydrofuran.

4. The solvent cement formulation according to claim 1 comprising:
11-19% tetrahydrofuran;
21-29% cyclohexanone;
11-20% methyl ethyl ketone;
26-34% acetone;
8-15% polyvinyl chloride;
0.5-5% silica; and,
0.01-0.08% of said thickener.

5. The solvent cement formulation according to claim 1 comprising:
about 15% tetrahydrofuran;
about 25% cyclohexanone;
about 16% methyl ethyl ketone;
about 30% acetone;
about 11.5 to about 12% polyvinyl chloride;
about 2 to about 2.5% silica; and,
about 0.03% of said thickener.

6. The solvent cement formulation according to claim 1 having an initial viscosity of at least 1700 cP.

7. The solvent cement formulation according to claim 1 having an initial viscosity of about 1700 cP to about 7000 cP.

8. The solvent cement formulation according to claim 1 having a lap shear strength of at least 280 psi after two hours of curing time, at least 500 psi after 16 hours of curing time, and at least 950 psi after 72 hours of curing time.

9. A method for bonding a first plastic component to a second plastic component, the method comprising:
applying a solvent cement to a surface of the first plastic component, and,
contacting the surface of the first plastic component to a surface of the second plastic component,
the solvent cement being formed from the solvent cement formulation according to claim 1 .

10. A section of plastic piping comprising a first plastic component that is bonded to a second plastic component by a solvent cement formulation according to claim 1 .

Assignees

• Oatey Co

Inventors

• Parhar Amrit
• Perez Willie

Classifications

• C08J2427/00

  Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers · CPC title

• C08J2427/06

  Homopolymers or copolymers of vinyl chloride · CPC title

• C08L33/08

  Homopolymers or copolymers of acrylic acid esters · CPC title

• C08J5/125

  Adhesives in organic diluents · CPC title

• C08J2355/02

  Acrylonitrile-Butadiene-Styrene [ABS] polymers · CPC title