Wet friction material production methods

Patent metadata

Field	Value
Publication number	US-10844919-B2
Application number	US-201916363685-A
Country	US
Kind code	B2
Filing date	Mar 25, 2019
Priority date	Mar 25, 2019
Publication date	Nov 24, 2020
Grant date	Nov 24, 2020

Abstract

A method of producing a friction material. The method includes mixing silica containing filler particles and a liquid binder to form a binder-filler liquid mixture. The method also includes saturating a fibrous base material with the binder-filler liquid mixture to form a saturated fibrous base material. The method further includes curing the saturated fibrous base material at a predetermined temperature for a predetermined time to cure the saturated fibrous base material to form the friction material.

First claim

What is claimed is:

1. A method of producing a friction material, the method comprising:
mixing silica containing filler particles and a liquid binder to form a binder-filler liquid mixture;
saturating a fibrous base material with the binder-filler liquid mixture to form a saturated fibrous base material, the saturated fibrous base material having a first surface region and a second surface region opposing the first surface region;
applying silica containing filler particles to the first and/or second surface regions of the saturated fibrous base material to form a surface region impregnated saturated fibrous base material; and
curing the surface region impregnated saturated fibrous base material at a predetermined temperature for a predetermined time to cure the surface region impregnated saturated fibrous base material to form the friction material having a first concentration of the silica containing filler particles in a first friction material surface region and a second concentration of the silica containing filler particles in a second friction material surface region, each of the first and second friction material surface regions have a thickness in a range of 50 to 150 μm, the first or second concentration is 30 to 50 weight % silica containing filler particles based on a total weight of the friction material in the first friction material surface region or the second friction material surface region, and a bulk region extending between the first and second friction material surface regions and the bulk region having a concentration of 1 to 10 weight % silica containing filler particles based on a total weight of the friction material in the bulk region.

2. The method of claim 1 , wherein the first and second concentrations are 40 to 50 weight %.

3. The method of claim 1 , wherein the saturating step is performed by immersing the fibrous base material into a bath of the binder-filler liquid mixture.

4. The method of claim 1 , wherein the silica containing filler particles are present in the binder-filler liquid mixture in a concentration of 30 to 60 weight % of a total weight of the binder-filler liquid mixture.

5. The method of claim 1 , wherein the binder is a phenolic resin.

6. The method of claim 1 , wherein the silica containing filler particles are diatomaceous earth particles.

7. The method of claim 1 , wherein the fibrous base material is a substantially pure fibrous base material not including any filler material.

8. A method of producing a friction material, the method comprising:
saturating a fibrous base material with a liquid binder to form a saturated fibrous base material, the saturated fibrous base material having a first surface region and a second surface region opposing the first surface region;
applying silica containing filler particles to the first and/or second surface regions of the saturated fibrous base material to form a surface region impregnated saturated fibrous base material; and
curing the surface region impregnated saturated fibrous base material at a predetermined temperature for a predetermined time to cure the surface region impregnated saturated fibrous base material to form the friction material having a first concentration of the silica containing filler particles in a first friction material surface region and a second concentration of the silica containing filler particles in a second friction material surface region, each of the first and second friction material surface regions have a thickness in a range of 50 to 150 μm, the first or second concentration is 30 to 50 weight % silica containing filler particles based on a total weight of the friction material in the first friction material surface region or the second friction material surface region, and a bulk region extending between the first and second friction material surface regions and the bulk region having a concentration of 1 to 10 weight % silica containing filler particles based on a total weight of the friction material in the bulk region.

9. The method of claim 8 , wherein the first or second concentration is 40 to 50 weight %.

10. The method of claim 8 , wherein the bulk region has a concentration of 1 to 5 weight %.

11. The method of claim 8 , wherein the applying step includes entraining the silica containing filler particles in a gas stream to form an entrained gas stream and applying the entrained gas stream to the first and/or second surface regions of the saturated fibrous base material to form the surface region impregnated saturated fibrous base material.

12. The method of claim 8 , wherein the applying step includes placing the saturated fibrous base material and the silica containing filler particles under vacuum conditions and applying the silica containing filler particles to the first and/or second surface regions of the saturated fibrous base material under vacuum conditions to form the surface region impregnated saturated fibrous base material.

13. The method of claim 8 , wherein the applying step includes scattering the silica containing filler particles over the first and/or second surface regions of the saturated fibrous base material to form the surface region impregnated saturated fibrous base material.

14. The method of claim 8 , wherein the applying step includes applying the silica containing filler particles to the first and/or second surface regions of the saturated fibrous base material at a predetermined pressure to form the surface region impregnated saturated fibrous base material.

15. The method of claim 8 , wherein the fibrous base material is a substantially pure fibrous base material not including any filler material.

Assignees

• Schaeffler Technologies Ag

Inventors

• Bakan Murat
• Farahati Rashid

Classifications

• F16D57/04

  with blades causing a directed flow, e.g. Föttinger type · CPC title

• B60T1/087

  in hydrodynamic, i.e. non-positive displacement, retarders · CPC title

• F16D2200/0091

  Impregnating a mat of fibres with a binder · CPC title

• F16D2200/0065

  Inorganic, e.g. non-asbestos mineral fibres · CPC title

• F16D2200/0056

  Elastomers · CPC title