Cold work tool and method for manufacturing same

Patent metadata

Field	Value
Publication number	US-10844456-B2
Application number	US-201615523780-A
Country	US
Kind code	B2
Filing date	Mar 1, 2016
Priority date	Mar 26, 2015
Publication date	Nov 24, 2020
Grant date	Nov 24, 2020

Abstract

Provided are: a cold work tool having excellent wear resistance; and a method for manufacturing the cold work tool. A cold work tool which has an ingredient composition that can be prepared into a martensite structure by quenching and which has a martensite structure, wherein the hardness of the cold work tool is 58 HRC or more, the area ratio of a carbide having an equivalent circle diameter of 5 μm or more in the cross-sectional structure of the cold work tool is 4.0% by area or more, and the carbon solid solution fraction, which is expressed by the ratio of the mass ratio of the amount of carbon that is present in the form of a solid solution in the structure of the cold work tool to the mass ratio of the amount of carbon that is contained in the whole of the cold work tool, is 75.0% or more. A method for manufacturing a cold work tool, which is suitable for manufacturing the aforementioned cold work tool.

First claim

The invention claimed is:

1. A cold work tool having a composition comprising: by mass,
C: 1.30 to 2.40%
Cr: 11.0 to 15.0%
Mo and W alone or in combination in an amount of (Mo+½W): 0.50 to 3.00%
V: 0.10 to 1.50%
Si: not more than 2.00%
Mn: not more than 1.50%
P: not more than 0.050%
S: not more than 0.0500%
optionally Ni: 0 to 1.00%
optionally Nb: 0 to 1.50%, and
the balance of Fe and impurities,
and having a martensitic structure,
wherein the tool has a hardness of not lower than 58 HRC,
wherein an area ratio of carbides having a circle equivalent diameter of not less than 5 μm in a cross-sectional structure of the tool is not lower than 4.0 area %, and
wherein a carbon solid solution ratio is not less than 75.0%, where the carbon solid solution ratio is defined as a ratio, by mass, of an amount of carbon solid-soluted in the structure of the tool to a total amount of carbon included in the tool.

2. The cold work tool according to claim 1 , wherein the carbon solid solution ratio is not less than 80.0%.

3. The cold work tool according to claim 1 , comprising 1.30 to 1.80% of carbon, by mass.

4. A method for manufacturing a cold work tool according to claim 1 , comprising:
a casting step of pouring a molten steel into a mold wherein the steel has the composition and the molten steel has a temperature of 90° C. to 110° C. above a melting point, and cooling the poured molten steel at a cooling rate such that the steel passes a solid-liquid phase coexistence region within 60 minutes to produce a raw material;
a hot working step of subjecting the raw material to hot working, and cooling the hot-worked raw material to a temperature generating a martensitic transformation to produce a steel including martensitic transformed from a structure of the raw material;
an annealing step of subjecting the steel to annealing to produce a cold work tool material; and
a quenching and tempering step of subjecting the cold work tool material to quenching and tempering to produce a cold work tool having a martensitic structure and having a hardness of not lower than 58 HRC.

Assignees

• Hitachi Metals Ltd

Inventors

• Shouji Tatsuya
• Shinji Yukio
• Kuroda Katsufumi

Classifications

• C21D8/02

  during manufacturing of plates or strips (C21D8/12 takes precedence) · CPC title

• C22C38/24

  with vanadium · CPC title

• C22C38/22

  with molybdenum or tungsten · CPC title

• C21D2211/008

  Martensite · CPC title

• C21D7/13 Primary

  by hot working · CPC title