Compositions containing NBR-based microgels

Patent metadata

Field	Value
Publication number	US-10844181-B2
Application number	US-201615548269-A
Country	US
Kind code	B2
Filing date	Jan 5, 2016
Priority date	Feb 5, 2015
Publication date	Nov 24, 2020
Grant date	Nov 24, 2020

Abstract

Particulate compositions solid at 20° C. and comprising at least one copolymer based on at least the following comonomers a) to d)
a) conjugated diene, b) α,β-unsaturated nitrile, c) at least one polyfunctional radically polymerizable comonomer and d) at least one carboxyl-, hydroxyl-, epoxy- and/or amino-group-functional radically polymerizable comonomer,

which possess an average particle diameter of the primary particles of 5 to 500 nm, characterized in that these compositions possess a pourability to EN DIN 6186:1998 (funnel diameter 15 mm) of not more than 33 s.

First claim

What is claimed is:

1. Particulate compositions comprising at least one copolymer comprising copolymer units based on at least the following comonomers
a) conjugated diene,
b) α,β-unsaturated nitrile,
c) at least one polyfunctional radically polymerizable comonomer, and
d) at least one comonomer selected from the group consisting of carboxyl-, hydroxyl-, epoxy- and amino-group-functional radically polymerizable comonomer,
wherein the compositions are solid at 20° C., comprise spray dried primary particles that have an average particle diameter of 5 to 500 nm, and have a pourability to EN DIN 6186:1998 (funnel diameter 15 mm) of not more than 33 s, and wherein the particulate composition contains a release agent.

2. The particulate compositions according to claim 1 , wherein the amount of copolymer units based on the conjugated diene, is 10 to 98.5 wt %, based on the total amount of all copolymer units.

3. The particulate compositions according to claim 1 , wherein the amount of copolymer units based on the α,β-unsaturated nitriles is 0.5 to 60 wt %, based on the total amount of all copolymer units.

4. The particulate compositions according to claim 1 , wherein the amount of copolymer units based on component c) is 0.5 to 10 wt %, based on the total amount of all copolymer units.

5. The particulate compositions according to claim 1 , wherein the amount of copolymer units based on component d) is 0.5 to 20 wt %, based on the total amount of all copolymer units.

6. The particulate compositions according to claim 1 , wherein the polyfunctional, radically polymerizable comomoner is selected from monomers which have two or more functional, radically polymerizable groups.

7. The particulate compositions according to claim 1 , wherein the comonomer d) is selected from the group consisting of acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, amine-functionalized (meth)acrylates, secondary aminoalkyl (meth)acrylic esters, (meth)acrylamides, hydroxy-functionalized (meth)acrylates, polyethylene glycol (meth)acrylates, epoxy-functional monomers, and alkyl, alkoxyalkyl, hydroxyalkyl, cycloalkyl, alkylcycloalkyl, and aryl monoesters or diesters of α,β-unsaturated dicarboxylic acids, it being possible for the esters to be mixed esters in the case of the diesters, and mixtures thereof.

8. The particulate compositions according to claim 1 , wherein the release agent comprises up to 20 wt % of the composition.

9. A method of producing the particulate compositions according to claim 1 , the method comprising:
subjecting components a) to d) to an emulsion polymerization to form polymer particles; and
subsequently spray-drying the polymer particles, and
adding a release agent.

10. An additive for thermoset compositions, the additive comprising the particulate compositions according to claim 1 .

11. Thermoset compositions comprising:
A) a particulate composition according to claim 1 , and
B) a thermosetting polymer.

12. A method for producing the thermoset compositions according to claim 11 , the method comprising:
a) dispersing the particulate composition in one or more reactants capable of forming the thermosetting polymer, or a solution thereof, which optionally comprise plastics additives,
b) optionally adding further components, and
c) curing the resulting dispersion.

13. Shaped articles, coating material, joining material, or adhesive comprising the thermoset compositions according to claim 11 .

14. The particulate compositions according to claim 1 , wherein:
the powder has a dynamic viscosity of greater than 1000 Pas at 20° C. under 1 bar atmospheric pressure;
the amount of copolymer units based on the conjugated diene, is 10 to 98.5 wt %, based on the total amount of all copolymer units;
the amount of copolymer units based on the α,β-unsaturated nitriles is 0.5 to 60 wt %, based on the total amount of all copolymer units;
the amount of copolymer units based on component c) is 0.5 to 10 wt %, based on the total amount of all copolymer units; and
the amount of copolymer units based on component d) is 0.5 to 20 wt %, based on the total amount of all copolymer units.

15. The particulate compositions according to claim 14 , wherein:
the conjugated diene comprises (C 4 -C 6 ) conjugated dienes;
the α,β-unsaturated nitrile comprises (C 3 -C 5 )-α,β-unsaturated nitriles;
the polyfunctional radically polymerizable comonomer comprises monomers having 2, 3 or 4 polymerizable C═C double bonds; and
the carboxyl-, hydroxyl-, epoxy- and/or amino-group-functional radically polymerizable comonomer comprises acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, amine-functionalized (meth)acrylates, acrolein, N-vinyl-2-pyrrolidone, N-vinylimidazole, 2-vinylpyridine, 4-vinylpyridine, N-allylurea, N-allylthiourea, (meth)acrylamides, hydroxy-functionalized (meth)acrylates, polyethylene glycol (meth)acrylates, polypropylene glycol (meth)acrylates, epoxy-functional monomers, monoesters or diesters of α,β-unsaturated dicarboxylic acids, and mixtures thereof.

16. The particulate compositions according to claim 14 , wherein:
the conjugated diene comprises 1,3-butadiene, isoprene, 2,3-dimethylbutadiene, piperylene, or mixtures thereof;
the α,β-unsaturated nitrile comprises acrylonitrile, methacrylonitrile, ethacrylonitrile, or mixtures thereof;
the polyfunctional radically polymerizable comonomer comprises diisopropenylbenzene, divinylbenzene, divinyl ether, divinyl sulfone, diallyl phthalate, triallyl cyanurate, triallyl isocyanurate, 1,2-polybutadiene, N,N′-m-phenylenemaleimide, 2,4-tolylenebis(maleimide), triallyl trimellitate, acrylamides methylene-bisacrylamide, hexamethylene-1,6-bisacrylamide, diethylenetriaminetrismethacrylamide, bis(methacrylamidopropoxy)ethane, 2-acrylamidoethyl acrylate, and polyfunctional acrylates, methacrylates and itaconates of polyhydric C 2 to C 10 alcohols selected from ethylene glycol, 1,2-propanediol, 1,4-butanediol, hexanediol, polyethylene glycol having 2 to 20, especially 2 to 8, oxyethylene units, neopentyl glycol, bisphenol A, glycerol, trimethylolpropane, pentaerythritol and sorbitol with unsaturated polyesters formed from aliphatic diols and polyols, and mixtures thereof; and
the carboxyl-, hydroxyl-, epoxy- and/or amino-group-functional radically polymerizable comonomer comprises acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, aminoethyl (meth)acrylate, aminopropyl (meth)acrylate, aminobutyl (meth)acrylate, tert-butylamino(C 2 -C 4 )alkyl (meth)acrylate, acrolein, N-vinyl-2-pyrrolidone, N-vinylimidazole, 2-vinylpyridine, 4-vinylpyridine, N-allylurea and N-allylthiourea, (meth)acrylamide, singly or doubly N-substituted (meth)acrylamides, hydroxyethyl methacrylate (HEMA), hydroxypropyl (meth)acrylate, hydroxybutyl (meth)acrylate, hydroxy- or methoxypolyethylene glycol methacrylate, polypropylene glycol (meth)acrylates, glycidyl (meth)acrylate, or ethyl, n-propyl, isopropyl, n-butyl, tert-butyl, n-pentyl or n-hexyl monoesters or diesters, C 3 -C 8 alkoxyalkyl monoesters or diesters, C 2 -C 8 hydroxyalkyl monoesters or diesters, C 6 -C 12 cycloalkyl monoesters or diesters, C 7 -C 10 alkylcycloalkyl monoesters or diesters, C 6 -C 14 aryl monoesters or diesters, it being possible for the esters also to be mixed esters in the case of the diesters, and mixtures thereof.

17. The particulate compositions according to claim 1 , wherein:
the conjugated diene comprises butadiene, and the amount of copolymer units based on the butadiene, is 25 to 85 wt %, based on the total amount o

Assignees

• Arlanxeo Deutschland Gmbh

Inventors

• Schmidt Udo
• Kohl Christopher
• Zhou Jiawen
• Fruh Thomas

Classifications

• C09J109/02

  Copolymers with acrylonitrile · CPC title

• C09D109/02

  Copolymers with acrylonitrile · CPC title

• C08L9/02

  Copolymers with acrylonitrile · CPC title

• C08J3/122

  Pulverisation by spraying · CPC title

• C08F2500/24

  Polymer with special particle form or size · CPC title