Process for preparing a polymer composition, and polymer composition obtainable by said process

Patent metadata

Field	Value
Publication number	US-10844172-B2
Application number	US-201615744263-A
Country	US
Kind code	B2
Filing date	Jul 22, 2016
Priority date	Jul 29, 2015
Publication date	Nov 24, 2020
Grant date	Nov 24, 2020

Abstract

The invention relates to a process for preparing a polymer composition, comprising a blending step wherein a first polymer (component A1) and at least one further component are dosed into and mixed in a mixing apparatus, and wherein the first polymer A1 is a granulate polyamide material directly obtained by direct solid state polymerization of a diammonium dicarboxylate salt prepared by fluidized bed spray granulation. The invention also relates to a dry-blend obtainable by said process.

First claim

The invention claimed is:

1. A process for preparing a polymer composition comprising the steps of:
(a) preparing a diammonium dicarboxylate salt solution by dissolving a diamine and a dicarboxylic acid in water or in an aqueous solvent;
(b) preparing a diammonium dicarboxylate salt granulate material by fluidized bed spray granulation of the diammonium dicarboxylate salt solution obtained in step (a);
(c) preparing a first polymer A1 by direct solid state polymerization of the diammonium dicarboxylate salt granulate material obtained from step (b), thereby obtaining the first polymer A1 as a granulate polyamide material, and thereafter
(d) preparing the polymer composition by dosing the first polymer A1 directly obtained from step (c) and at least one further component in a mixing apparatus and blending the granulate polyamide material of the first polymer A1 directly obtained from step (c) and the at least one further component in the mixing apparatus.

2. The process according to claim 1 , wherein the mixing apparatus is a melt-mixing apparatus;
the process comprises a melt-mixing step, wherein the polymer granulate material is dosed into the melt-mixing apparatus and melted in the melt-mixing apparatus to form a polymer melt;
the one or more further components are dosed before, during or after melting of the granulate polyamide material, into the melt mixing apparatus and mixed with the polymer melt, thereby forming a melt-blend of molten polymer with the one or more further components mixed or dispersed therein; and wherein
the melt-blend is discharged from the melt-mixing apparatus and cooled, thereby obtaining the blend in the form of a solid composite material.

3. The process according to claim 2 , wherein the melt-mixing apparatus is an extruder.

4. The process according to claim 2 , wherein the melt-blend is discharged by extruding the melt-blend through a die with one or more orifices, thereby forming polymeric strands.

5. The process according to claim 2 , wherein the melt-blend is discharged by extruding the melt-blend through a die with a die slit, thereby forming a polymer sheet or polymer film.

6. The process according to claim 2 , wherein the melt-blend is discharged by extruding the melt-blend into a mold with a three-dimensional cavity, cooling and solidifying the melt-blend in the mold, thereby forming a three-dimensional part and discharging the three-dimensional part from the mold.

7. The process according to claim 2 , wherein the granulate polyamide material is mixed and melt-blended with a second polyamide polymer, miscible with the granulate polyamide material, resulting in a copolymer between the second polyamide and the granulate polyamide material being formed in the extruder.

8. The process according to claim 1 , wherein the granulate polyamide material has a particle size distribution with a median particle size in the range of 200-1000 μm, measured by laser granulometry with the method according to ISO 13320-1 at 20° C.

9. The process according to claim 1 , wherein the granulate polyamide material comprises a semi-aromatic polyamide, an aliphatic polyamide, an aromatic polyamide, or any copolyamide or any mixture thereof.

10. The process according to claim 1 , wherein the at least one further component comprises a second polymer component and/or at least one additive selected from the group consisting of reinforcing agents, reinforcing fillers, flame retardants, flame retardant synergists, stabilizers, pigments, colorants, processing aids, and auxiliary additives used in polyamide moulding compositions.

Assignees

• Dsm Ip Assets Bv

Inventors

• Van Dijk Hans Klaas
• Baltussen Michiel Gerardus Henricus Maria

Classifications

• C08G69/46

  Post-polymerisation treatment · CPC title

• C08J3/005

  Processes for mixing polymers · CPC title

• C08G69/30 Primary

  Solid state polycondensation · CPC title

• B29C48/022

  characterised by the choice of material · CPC title

• B29K2077/00

  Use of {PA, i.e.} polyamides, e.g. polyesteramides {or derivatives thereof}, as moulding material · CPC title