Polymer binder for lithium battery and method of manufacturing

Patent metadata

Field	Value
Publication number	US-10840502-B2
Application number	US-201715442278-A
Country	US
Kind code	B2
Filing date	Feb 24, 2017
Priority date	Feb 24, 2017
Publication date	Nov 17, 2020
Grant date	Nov 17, 2020

Abstract

Provided is an anode active material layer for a lithium battery. The anode active material layer comprises multiple anode active material particles and an optional conductive additive that are bonded together by a binder comprising a high-elasticity polymer having a recoverable or elastic tensile strain no less than 10% when measured without an additive or reinforcement in the polymer and a lithium ion conductivity no less than 10 −5 S/cm at room temperature. The anode active material preferably has a specific lithium storage capacity greater than 372 mAh/g (e.g. Si, Ge, Sn, SnO 2 , Co 3 O 4 , etc.).

First claim

We claim:

1. An anode active material layer for a lithium battery, said anode active material layer comprising multiple anode active material particles and an optional conductive additive that are bonded together by a binder comprising a high-elasticity polymer having a recoverable tensile strain from 5% to 700% when measured without an additive or reinforcement in said polymer and a lithium ion conductivity no less than 10 −5 S/cm at room temperature, wherein said high-elasticity polymer contains a cross-linked network of polymer chains having an ether linkage, nitrile-derived linkage, benzo peroxide-derived linkage, propylene oxide linkage, cyano-resin linkage, triacrylate monomer-derived linkage, tetraacrylate monomer-derived linkage, or a combination thereof in said cross-linked network of polymer chains, or said high-elasticity polymer contains a cross-linked network of polymer chains selected from nitrile-containing polyvinyl alcohol chains, cyanoresin chains, pentaerythritol tetraacrylate chains, pentaerythritol triacrylate chains, ethoxylated trimethylolpropane triacrylate (ETPTA) chains, ethylene glycol methyl ether acrylate (EGMEA) chains, or a combination thereof.

2. The anode active material layer of claim 1 , wherein said anode active material is selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo 2 O 4 ; (f) prelithiated versions thereof; (g) particles of Li, Li alloy, or surface-stabilized Li having at least 60% by weight of lithium element therein; and (h) combinations thereof.

3. The anode active material layer of claim 2 , wherein said Li alloy contains from 0.1% to 10% by weight of a metal element selected from Zn, Ag, Au, Mg, Ni, Ti, Fe, Co, V, or a combination thereof.

4. The anode active material layer of claim 1 , wherein said anode active material contains a prelithiated Si, prelithiated Ge, prelithiated Sn, prelithiated SnO x , prelithiated SiO x , prelithiated iron oxide, prelithiated VO 2 , prelithiated Co 3 O 4 , prelithiated Ni 3 O 4 , or a combination thereof, wherein x=1 to 2.

5. The anode active material layer of claim 1 , wherein said anode active material is in a form of nano particle, nano wire, nano fiber, nano tube, nano sheet, nano belt, nano ribbon, nano disc, nano platelet, or nano horn having a thickness or diameter from 0.5 nm to 100 nm.

6. The anode active material layer of claim 5 , wherein said anode active material has a dimension less than 20 nm.

7. The anode active material layer of claim 1 , wherein one or a plurality of said particles is coated with a layer of carbon or graphene.

8. The anode active material layer of claim 1 , wherein said conductive additive is selected from a graphite, graphene, or carbon, or a combination thereof.

9. The anode active material layer of claim 8 , wherein said graphite or carbon material is selected from polymeric carbon, amorphous carbon, chemical vapor deposition carbon, coal tar pitch, petroleum pitch, meso-phase pitch, carbon black, coke, acetylene black, activated carbon, fine expanded graphite particle with a dimension smaller than 100 nm, artificial graphite particle, natural graphite particle, or a combination thereof.

10. The anode active material layer of claim 5 , wherein said nano particle, nano wire, nano fiber, nano tube, nano sheet, nano belt, nano ribbon, nano disc, nano platelet, or nano horn is coated with or embraced by a conductive protective coating selected from a carbon material, graphene, electronically conductive polymer, conductive metal oxide, or conductive metal coating.

11. The anode active material layer of claim 10 , wherein said nano particle, nano wire, nano fiber, nano tube, nano sheet, nano belt, nano ribbon, nano disc, nano platelet, or nano horn is pre-intercalated or pre-doped with lithium ions to form a prelithiated anode active material having an amount of lithium from 0.1% to 54.7%% by weight of said prelithiated anode active material.

12. The anode active material layer of claim 1 , wherein said high-elasticity polymer has a lithium ion conductivity no less than 10 −4 S/cm.

13. The anode active material layer of claim 1 , wherein said high-elasticity polymer has a lithium ion conductivity no less than 10 −3 S/cm.

14. The anode active material layer of claim 1 , wherein said high-elasticity polymer is a neat polymer having no additive or filler dispersed therein.

15. The anode active material layer of claim 1 , wherein said high-elasticity polymer contains from 0.1% to 50% by weight of a lithium ion-conducting additive dispersed therein, or contains therein from 0.1% by weight to 10% by weight of a reinforcement nano filament selected from carbon nanotube, carbon nano-fiber, graphene, or a combination thereof.

16. The anode active material layer of claim 1 , wherein said high-elasticity polymer forms a mixture with an elastomer selected from natural polyisoprene, synthetic polyisoprene, polybutadiene, chloroprene rubber, polychloroprene, butyl rubber, styrene-butadiene rubber, nitrile rubber, ethylene propylene rubber, ethylene propylene diene rubber, epichlorohydrin rubber, polyacrylic rubber, silicone rubber, fluorosilicone rubber, perfluoroelastomers, polyether block amides, chlorosulfonated polyethylene, ethylene-vinyl acetate, thermoplastic elastomer, protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, or a combination thereof.

17. The anode active material layer of claim 1 , wherein said high-elasticity polymer is mixed with a lithium ion-conducting additive to form a composite wherein said lithium ion-conducting additive is dispersed in said high-elasticity polymer and is selected from Li 2 CO 3 , Li 2 O, Li 2 C 2 O 4 , LiOH, LiX, ROCO 2 Li, HCOLi, ROLi, (ROCO 2 Li) 2 , (CH 2 OCO 2 Li) 2 , Li 2 S, Li X SO y , or a combination thereof, wherein X=F, Cl, I, or Br, R=a hydrocarbon group, x=0-1, y=1-4.

18. The anode active material layer of claim 1 , wherein said high-elasticity polymer is mixed with a lithium ion-conducting additive to form a composite wherein said lithium ion-conducting additive is dispersed in said high-elasticity polymer and is selected from lithium perchlorate, LiClO 4 , lithium hexafluorophosphate, LiPF 6 , lithium borofluoride, LiBF 4 , lithium hexafluoroarsenide, LiAsF 6 , lithium trifluoro-metasulfonate, LiCF 3 SO 3 , bis-trifluoromethyl sulfonylimide lithium, LiN(CF 3 SO 2 ) 2 , lithium bis(oxalato)borate, LiBOB, lithium oxalyldifluoroborate, LiBF 2 C 2 O 4 , lithium oxalyldifluoroborate, LiBF 2 C 2 O 4 , lithium nitrate, LiNO 3 , Li-Fluoroalkyl-Phosphates, LiPF 3 (CF 2 CF 3 ) 3 , lithium bisperfluoro-ethysulfonylimide, LiBETI, lithium bis(trifluoromethanesulphonyl)imide, lithium bis(fluorosulphonyl)imide, lithium trifluoromethanesulfonimide, LiTFSI, an ionic liquid-based lithium salt, or a combination thereof.

19. The anode active material layer of claim 1 , wherein said high-elasticity polymer is mixed with an electron-

Assignees

• Nanotek Instruments Inc
• Global Graphene Group Inc

Inventors

• Pan Baofei
• He Hui
• Zhamu Aruna
• Jang Bor Z

Classifications

• Y02E60/10

  Energy storage using batteries · CPC title

• Y02P70/50

  Manufacturing or production processes characterised by the final manufactured product · CPC title

• H01M2300/0091

  in the form of mixtures · CPC title

• H01M2300/0082

  Organic polymers · CPC title

• H01M12/08

  composed of a half-cell of a fuel-cell type and a half-cell of the secondary-cell type · CPC title