Method for producing ethanolamines and/or ethyleneamines

Patent metadata

Field	Value
Publication number	US-10836704-B2
Application number	US-201716469782-A
Country	US
Kind code	B2
Filing date	Dec 7, 2017
Priority date	Dec 15, 2016
Publication date	Nov 17, 2020
Grant date	Nov 17, 2020

Abstract

Preparing ethanolamines/ethyleneamines in the presence of an amination catalyst prepared by reducing a calcined catalyst precursor containing one or more metals of groups 8, 9, 10 and/or 11 and low basicity achieved by: a) coprecipitating catalyst precursor and active composition additionally contains alkali metals or alkaline earth metals; b) the catalyst precursor is prepared by impregnating a support material or precipitative application onto a support material containing alkali metals, Be, Ca, Ba, Sr, hydrotalcite, chrysotile or sepiolite; c) the catalyst precursor is prepared by impregnating a support material or precipitative application onto a support material and the active composition of the catalyst support contains one or more of alkali metals and alkaline earth metals; d) the catalyst precursor is calcined at temperatures of 600° C. or more; or e) the catalyst precursor is prepared by a combination of a) and d), b) and d), or c) and d).

First claim

The invention claimed is:

1. A process for preparing ethanolamines and/or ethyleneamines in the gas phase by reacting ethylene glycol (MEG) with ammonia in the presence of an amination catalyst which is prepared by reducing a calcined catalyst precursor comprising an active composition, where the active composition comprises one or more active metals selected from the group consisting of the elements of groups 8, 9, 10 and 11 of the Periodic Table of the Elements and optionally one or more added catalyst elements selected group consisting of the metals and semimetals of groups 3 to 7 and 12 to 17, the element P and the rare earth elements, wherein
a) the catalyst precursor is prepared by coprecipitation and the active composition additionally comprises one or more basic elements selected from the group consisting of the alkali metals and alkaline earth metals, and the total amount of the basic elements is in the range from 2.5% to 80% by weight, based on the total mass of the catalyst precursor after calcination; or
b) the catalyst precursor is prepared by precipitative application or impregnation of the active composition onto a support material, wherein the support material after calcination comprises one or more basic elements selected from the group consisting of the alkali metals, Be, Ca, Ba and Sr or one or more minerals selected from the group consisting of hydrotalcite, chrysotile and sepiolite; or
c) the catalyst precursor is prepared by precipitative application or impregnation of the active composition onto a support material and the active composition of the catalyst support after calcination additionally comprises one or more basic elements selected from the group consisting of the alkali metals and the alkaline earth metals, and the total amount of the basic elements is in the range from 2.5% to 80% by weight, based on the total mass of the catalyst precursor after calcination; or
d) the catalyst precursor is calcined at temperatures of 900° C. or more; or
e) the catalyst precursor is prepared by a combination of variants a) and d) or by a combination of variants b) and d) or by a combination of variants c) and d);
wherein the acidity of the calcined catalyst precursor is less than 0.2 mmol/g NH 3 , measured by temperature-programmed desorption of ammonia.

2. The process according to claim 1 , wherein MEG and NH 3 are reacted in the gas phase at a pressure in the range from 0.5 to 3 MPa and at a temperature in the range from 200 to 350° C.

3. The process according to claim 1 , wherein the reaction is effected by contacting a gas stream comprising MEG and NH 3 in a fixed bed reactor with the amination catalyst, and the gas hourly space velocity (GHSV) which is contacted with the amination catalyst is 1000 to 30 000 h −1 .

4. The process according to claim 1 , wherein ethylene glycol and ammonia are reacted over the amination catalyst in the presence of hydrogen.

5. The process according to claim 4 , wherein the proportion by volume of hydrogen in the gas stream which is contacted with the amination catalyst is in the range from 5% to 25% by volume.

6. The process according to claim 1 , wherein the catalyst precursor is calcined in variant d) at a temperature in the range from 900 to 1200° C.

7. The process according to claim 6 , wherein the catalyst precursor is calcined in variant d) at a temperature in the range from 900 to 1100° C.

8. The process according to claim 1 , wherein the catalyst precursor is prepared by variants b) or c) and comprises the active metal Cu.

9. The process according to claim 1 , wherein the catalyst precursor comprises one or more added catalyst elements selected from the group consisting of Zr and Zn.

10. The process according to claim 1 , wherein the basic elements in variants a) and c) of claim 1 comprise one or more elements selected from the group consisting of K, Mg, Ca, Cs, and Ba and/or wherein the active composition of the catalyst precursor of variant d) further comprises one or more basic elements selected from the group consisting of K, Mg, Ca, Cs, and Ba.

11. The process according to claim 1 , wherein the catalyst precursor in variants b) and d) of claim 1 comprises a support material which is a mixed oxide of CaO and ZnO.

12. The process according to claim 1 , wherein the catalyst precursor is prepared by precipitative application or impregnation and comprises
2.5% to 60% by weight of Cu;
2.5% to 60% by weight of Zn and/or 0.1% to 10% by weight of Zr; and
2.5 to 60% by weight of Ca,
based in each case on the total mass of the catalyst precursor after calcination.

13. The process according to claim 11 , wherein the catalyst precursor is prepared by precipitative application or impregnation and comprises 40% to 95% by weight, based on the total mass of the catalyst precursor after calcination, of the mixed oxide according to claim 12 , and where the composition of the catalyst precursor is 1% to 20% by weight of Cu, 20% to 60% by weight of Zn, 0.1% to 10% by weight of Zr and 10% to 60% by weight of Ca, based in each case on the total mass of the catalyst precursor after calcination.

14. The process according to claim 7 , wherein the catalyst precursor is prepared by a combination of variants a) and d) or by a combination of variants b) and d) or by a combination of variants c) and d).

Assignees

• Basf Se

Inventors

• Schroeter Marie Katrin
• Gordillo Alvaro
• Parvulescu Andrei-Nicolae
• Melder Johann-Peter
• Lizandara Pueyo Carlos
• Bechtel Juergen
• Heidemann Thomas
• Schunk Stephan A
• Mueller Ulrich

Classifications

• B01J35/40

  characterised by dimensions, e.g. grain size (in a colloidal state B01J35/23; crystallite size B01J35/77) · CPC title

• C07C213/02

  by reactions involving the formation of amino groups from compounds containing hydroxy groups or etherified or esterified hydroxy groups · CPC title

• B01J37/03

  Precipitation; Co-precipitation · CPC title

• B01J37/08 Primary

  Heat treatment {(B01J37/0009, B01J37/0018 take precedence)} · CPC title

• B01J2523/00

  Constitutive chemical elements of heterogeneous catalysts · CPC title