Laminated packaging material, packaging containers manufactured therefrom and a method for manufacturing the laminate material

Patent metadata

Field	Value
Publication number	US-10836147-B2
Application number	US-201816616830-A
Country	US
Kind code	B2
Filing date	May 31, 2018
Priority date	May 31, 2017
Publication date	Nov 17, 2020
Grant date	Nov 17, 2020

Abstract

The present invention relates to a laminated liquid food packaging material, comprising a cellulose-based bulk material layer and outer layers of thermoplastic polymers on both sides, having a décorative print pattern arranged beneath one of the outer thermoplastic polymer layers. The invention further relates to the method for manufacturing the laminated packaging material and to a packaging container for liquid food packaging, comprising the laminated packaging material.

First claim

The invention claimed is:

1. Laminated packaging material for packaging of liquid food, comprising a cellulose-based bulk material layer possessing an outer side, an outermost transparent and protective thermoplastic polymer layer arranged on an outside of the bulk material layer that is to be directed to the exterior of a packaging container made from the laminated packaging material, a decorative print pattern arranged between the bulk material layer and the outermost transparent and protective thermoplastic polymer layer, and visible through the outermost transparent and protective thermoplastic polymer layer, an innermost heat sealable and liquid-tight thermoplastic polymer layer, to be in direct contact with the liquid food in the packaging container, wherein the bulk material layer is a containerboard, which has been calendered to a Bendtsen outside surface roughness value lower than 200 ml air/min, and has an SCT index greater than 30 Nm/g in MD as determined in accordance with ISO 9895 and ISO 536 the outside surface of the containerboard having the Bendtsen outside surface roughness value lower than 200 ml air/min being the surface facing towards the outermost transparent and protective thermoplastic polymer layer, and wherein the laminated packaging material further comprises a cellulose-based print substrate paper, having an outside print surface carrying the decorative print pattern, the print substrate paper being adhered to the outer side of the bulk material layer by way of 1-4 g/m 2 adhesive, dry weight, the print substrate paper having a surface weight of 100 g/m 2 or lower (ISO 536), the outside print surface having a Bendtsen surface roughness value lower than 100 ml air/min (ISO 8791-2).

2. Laminated packaging material as claimed in claim 1 , wherein a gas barrier film or foil comprising an oxygen barrier layer or coating is laminated on an inner side of the bulk material layer, between the bulk material layer and the innermost thermoplastic polymer layer.

3. Laminated packaging material as claimed in claim 1 , wherein the bulk material layer has Bendtsen outside surface roughness lower than 150 ml air/min, before the bulk material layer is laminated to the print substrate paper.

4. Laminated packaging material as claimed in claim 1 , wherein the outside print surface has a Bendtsen surface roughness value of below 80 ml air/min.

5. Laminated packaging material as claimed in claim 1 , wherein the print substrate paper has a surface weight of lower than 80 g/m 2 .

6. Laminated packaging material as claimed in claim 1 , wherein the outside print surface has a Cobb value from 20 to 30 g/m 2 water.

7. Laminated packaging material as claimed in claim 1 , wherein the print substrate paper has a density higher than 650 kg/m 3 , a surface weight of 100 g/m 2 or lower (ISO 536), a tensile strength index (GM) of at least 40 Nm/g and a tear strength index (GM) of at least 6.0 mNm 2 /g, and comprising at least one sizing agent at from 0.1 to 0.4 wt-%, the outside print surface having a Bendtsen surface roughness value lower than 100 ml air/min (ISO 8791-2), and a Cobb value greater than 20 g/m 2 and lower than 30 g/m 2 (water).

8. Laminated packaging material as claimed in claim 1 , wherein the print substrate paper is a paper selected from the group consisting of MG (Machine Glazed) paper, MF (Machine Finished) paper, LWC (Light-weight coated) paper, Flexible Packaging paper, digital printing paper and ink jet printing paper.

9. Laminated packaging material as claimed in claim 1 , wherein the outside print surface of the print substrate paper is metallised and has a Bendtsen surface roughness value lower than 100 ml air/min.

10. Laminated packaging material as claimed in claim 1 , wherein the outside print surface of the print substrate paper is natural brown.

11. Liquid food packaging container comprising the laminated packaging material as defined in claim 1 .

12. Method for manufacturing a laminated packaging material for packaging of liquid food, the method comprising
a) providing a first web of a cellulose-based bulk material layer, being a calendered containerboard having a Bendtsen outside surface roughness value lower than 200 ml air/min, and an SCT index greater than 30 Nm/g in MD as determined in accordance with ISO 9895 and ISO 536, the outside surface of the containerboard having the Bendtsen outside surface roughness value lower than 200 ml air/min being the surface directed to an exterior of a packaging container made from the laminated material,
b) providing a second web of a cellulose-based print substrate paper, having a surface weight of 100 g/m 2 or lower (ISO 536), and an outside print surface to carry a decorative print pattern, with a Bendtsen surface roughness value lower than 100 ml air/min (ISO 8791-2),
c) applying an aqueous adhesive composition comprising an adhesive polymer at an amount from 1 to 4 g/m 2 , dry content, onto at least one of the outside of the first web and the inside of the second web, the inside of the second wet being the surface directed to an interior of said packaging container made from the aminated material,
d) forwarding the first and second webs, from step c), towards a pressure roller nip to join and laminate the first and second webs together by the interjacent aqueous adhesive composition while passing the nip, and while the aqueous adhesive composition is partly absorbed into a surface of at least one of the first and second webs,
e) printing a décorative print pattern onto the outside print surface of the print substrate paper,
f) laminating an innermost heat sealable thermoplastic polymer layer on the inner side of the first web of the bulk material layer, opposite the side of the print substrate paper, the innermost heat sealable thermoplastic polymer layer being the surface in contact with the liquid food in said packaging container made from the laminated material,
g) laminating an outermost, transparent and protective thermoplastic polymer layer on the outer side of the second web of the print substrate paper that is opposite the side of the bulk material layer.

13. Method as claimed in claim 12 , wherein step e) is carried out before steps c) and d), such that the print substrate paper is first printed with the décorative print pattern onto the outside print surface in a separate printing operation.

14. Method as claimed in claim 12 , further comprising laminating a gas barrier film or foil comprising an oxygen barrier layer or coating on an inner side of the bulk material layer so that the gas barrier film or foil is between the bulk material layer and the innermost thermoplastic polymer layer.

15. Method as claimed in claim 12 , wherein the bulk material layer is calendered to the Bendtsen outside surface roughness value lower than 200 ml air/min in a separate step before step a) at a nip load from 80 to 120 kN/m and a surface temperature above 200° C., and at a calendaring speed from 500 to 1200 m/min.

16. Method as claimed in claim 12 , wherein the laminating of the outermost, transparent and protective thermoplastic polymer layer on the outer side of the web of the print substrate paper occurs before the laminating of the innermost heat sealable thermoplastic polymer layer on the inner side of the web of the bulk material layer, and the printing of the décorative print pattern onto the print surface of the print substrate paper occurs before the laminating of the outermost, transparent and protective thermoplastic polymer layer on the outer side of the web of the print substrate paper.

17. Laminated packaging

Assignees

• Tetra Laval Holdings & Finance

Inventors

• Toft Nils
• Jonasson Katarina
• Öhman Peter
• Horvath Andrew

Classifications

• B32B29/002

  as the main or only constituent of a layer, which is next to another layer of the same or of a different material (next to a layer of a particular substance B32B9/06; next to a bituminous or tarry layer B32B11/06; next to a water-setting substance layer B32B13/08; next to a metal layer B32B15/12; next to a glass layer B32B17/065; next to a layer formed of natural mineral fibres or particles B32B19/046; next to a wood layer B32B21/06; next to a cellulosic plastic layer B32B23/06; next to a natural or synthetic rubber layer B32B25/06; next to a synthetic resin layer B32B27/10) · CPC title

• B32B2255/26

  Polymeric coating · CPC title

• B32B27/36

  comprising polyesters · CPC title

• B32B2307/7244

  Oxygen barrier · CPC title

• B32B2250/04

  4 layers · CPC title