Warm forming process and apparatus for transverse bending of an extruded aluminum beam to warm form a vehicle structural component

Patent metadata

Field	Value
Publication number	US-10835942-B2
Application number	US-201715686837-A
Country	US
Kind code	B2
Filing date	Aug 25, 2017
Priority date	Aug 26, 2016
Publication date	Nov 17, 2020
Grant date	Nov 17, 2020

Abstract

A method for warm forming an aluminum beam, such as an aluminum component for a vehicle, includes providing an extruded aluminum beam with a hollow cross-sectional shape. A portion of a forming die is heated to a desired temperature, so as to heat a portion of the aluminum beam in the die to a temperature below the artificial aging temperature of the aluminum beam. The heated aluminum beam is deformed to a desired shape with the die in a direction transverse to a length of the aluminum beam.

First claim

The invention claimed is:

1. A method for warm forming an aluminum beam, said method comprising:
extruding an aluminum beam to an extruded length with a hollow cross-sectional shape, wherein the aluminum beam comprises a 7000 series aluminum alloy;
after extruding the aluminum beam, naturally aging the aluminum beam at a temperature below 40 degrees Celsius for at least 24 hours prior to deforming the aluminum beam;
after naturally aging the aluminum beam, placing the aluminum beam in a die without solutionizing the aluminum beam at any time after extrusion;
heating a portion of the die;
conductively heating a first portion of the aluminum beam with the heated portion of the die to a desired temperature below an artificial aging temperature of the aluminum beam, wherein the desired temperature is greater than 37 degrees Celsius and less than 150 degrees Celsius; and
deforming the first portion of the aluminum beam from an extruded shape to a desired shape with the die in a direction transverse to the extruded length of the aluminum beam, wherein the die deforms the aluminum beam in a transverse direction to reduce an enclosed area of the hollow cross-sectional shape at the first portion of the aluminum beam.

2. The method of claim 1 , wherein the first portion comprises an end section of the aluminum beam.

3. The method of claim 1 , wherein the artificial aging temperature of the aluminum beam is greater than 150 degrees Celsius.

4. The method of claim 1 , wherein a second portion of the aluminum beam is not deformed by the die.

5. The method of claim 1 , wherein the aluminum beam is naturally aged at a temperature above 0 degrees Celsius.

6. The method of claim 1 , wherein the hollow cross-sectional shape of the aluminum beam includes a leg that extends across the enclosed area of the aluminum beam and continuously along the extruded length of the aluminum beam.

7. The method of claim 6 , wherein when the die deforms the hollow cross-sectional shape of the aluminum beam to reduce the enclosed area, the leg is deformed to a non-linear shape at the first portion of the aluminum beam.

8. The method of claim 1 , wherein the aluminum beam comprises a curvature formed along a longitudinal section of the extruded length of the aluminum beam to define a convex outer wall, and wherein the first portion of the die forms the desired shape into the convex outer wall.

9. A method for warm forming an aluminum beam, said method comprising:
providing an extruded aluminum beam that comprises a 7000 series aluminum alloy;
naturally aging the extruded aluminum beam for at least 24 hours prior to deforming the extruded aluminum beam;
after naturally aging the extruded aluminum beam, placing the extruded aluminum beam in a die without solutionizing the aluminum beam at any time after extrusion and prior to placement in the die;
conductively heating a portion of the extruded aluminum beam with a heated portion of the die above a threshold temperature of 37 degrees Celsius and below I 50 degrees Celsius; and
deforming the heated portion of the extruded aluminum beam from an extruded shape to a desired shape with the die in a direction transverse to an extruded length of the extruded aluminum beam.

10. The method of claim 9 , wherein the heated portion of the extruded aluminum beam does not exceed an artificial aging temperature of the extruded aluminum beam.

11. The method of claim 10 , wherein the artificial aging temperature is greater than 150 degrees Celsius.

12. The method of claim 9 , wherein the extruded aluminum beam comprises a cross-sectional shape taken transverse to the extruded length of the extruded aluminum beam that has an enclosed interior area extending along the extruded length of the tubular beam.

13. The method of claim 9 , wherein the extruded aluminum beam comprises a curvature formed along a longitudinal section of the extruded length of the aluminum beam to define a convex outer wall, and wherein, upon heating the die and the longitudinal section of the aluminum beam, a depression is formed into the convex outer wall with the die.

14. The method of claim 9 , wherein the natural aging of the extruded aluminum beam is at room temperature for at least 24 hours prior to deforming the desired shape into the extruded aluminum beam.

15. The method of claim 12 , wherein the cross-sectional shape includes a leg extending across a hollow area of the extruded aluminum beam and continuously along the extruded length of the extruded aluminum beam.

16. The method of claim 15 , wherein the leg is deformed to a non-linear shape as a result of deforming the heated portion of the aluminum beam with the die.

Assignees

• Shape Corp

Inventors

• Weykamp Helen
• Mckellar Kenneth E
• Devries David

Classifications

• B21D7/06

  in press brakes or between rams and anvils or abutments; Pliers with forming dies · CPC title

• B21D7/16

  Auxiliary equipment, e.g. for heating or cooling of bends · CPC title

• B21D53/88

  other parts for vehicles, e.g. cowlings, mudguards · CPC title

• B21C23/002

  Extruding materials of special alloys so far as the composition of the alloy requires or permits special extruding methods of sequences · CPC title

• B21D35/005

  characterized by the material of the blank or the workpiece (B21D26/053 takes precedence) · CPC title