Interference pigments

Patent metadata

Field	Value
Publication number	US-10822497-B2
Application number	US-201615086750-A
Country	US
Kind code	B2
Filing date	Mar 31, 2016
Priority date	Feb 9, 2004
Publication date	Nov 3, 2020
Grant date	Nov 3, 2020

Abstract

The present invention relates to interference pigments based on transparent, low-refractive-index, flake-form substrates which have a high-refractive-index coating consisting of TiO2 having a layer thickness of 20-200 nm and optionally an outer protective layer, and to the use thereof in paints, coatings, printing inks, security printing inks, plastics, button pastes, ceramic materials, glasses, for seed coloring, as dopants in the laser marking of plastics and papers, as additive for the laser welding of plastics, as additive for coloring in the foods and pharmaceuticals sectors, and in cosmetic formulations and for the preparation of pigment compositions and dry preparations.

First claim

The invention claimed is:

1. An interference pigment, which consists of a low-refractive-index, transparent, flake substrate having only one high-refractive-index coating consisting essentially of TiO 2 having a layer thickness of 70-160 nm and optionally further coated with an outer protective layer,
wherein the pigment exhibits a color flop from the short wave color green at a steep viewing angle to the long wave color red at a flat viewing angle,
wherein the substrate has an average thickness of 0.2 to 0.8 μm and a size in the other two dimensions of between 5 and 60 μm,
wherein the standard deviation of the thickness of the substrate flakes is 15%, based on their average thickness, and
wherein the TiO 2 is in the rutile modification and optionally contains an amount of tin oxide sufficient to provide it in the rutile modification.

2. An interference pigment according to claim 1 , wherein the standard deviation of the thickness of the flake substrate is ≤10%, based on their average thickness.

3. An interference pigment according to claim 1 , wherein the transparent flake is an SiO 2 flake, Al 2 O 3 flake, natural or synthetic mica flake or a glass flake.

4. An interference pigment according to claim 3 , wherein the transparent flake is an SiO 2 flake.

5. A process for the production of the interference pigment of claim 1 , comprising, coating the substrate by a wet-chemical method by hydrolytic decomposition of a titanium metal salt in aqueous medium or by thermal decomposition by a CVD or PVD process.

6. A pigment composition comprising one or more binders, optionally one or more additives and one or more interference pigments according to claim 1 .

7. A dry preparation in the form of pellets, granules, chips, or briquettes, comprising one or more interference pigments according to claim 1 .

8. The interference pigment of claim 1 , wherein the substrate has a refractive index of ≤1.8.

9. A paint, button paste, coating, printing ink, security printing ink, plastic, ceramic material, glass, seed coating, dopant for the laser marking of plastics and papers, additive for the laser welding of plastics, additive for food or pharmaceutical coloring, or cosmetic, which comprises an interference pigment of claim 1 .

10. The interference pigment of claim 1 , wherein the pigment has no outer protective layer.

11. The interference pigment of claim 1 , wherein the pigment has an outer protective layer.

12. An interference pigment, which consists of a low-refractive-index, transparent, SiO 2 flake substrate having only one high-refractive-index coating consisting essentially of TiO 2 having a layer thickness of 20-200 nm and optionally further coated with an outer protective layer,
wherein the pigment exhibits a color flop from green at a steep viewing angle to red at a flat viewing angle,
wherein the substrate has an average thickness of 0.1 to 1 μm and a size in the other two dimensions of between 5 and 60 μm,
wherein the standard deviation of the thickness of the substrate flakes is 15%, based on their average thickness, and
wherein the TiO 2 is in the rutile modification and optionally contains an amount of tin oxide sufficient to provide it in the rutile modification.

13. An interference pigment according to claim 1 , wherein the thickness of the high-refractive-index coating is matched to the average thickness of the flake substrate.

14. The interference pigment of claim 12 , wherein the high-refractive-index coating consisting essentially of TiO 2 has a layer thickness of 50 to 180 nm.

15. The interference pigment of claim 12 , wherein the high-refractive-index coating consisting essentially of TiO 2 has a layer thickness of 70 to 160 nm.

16. The pigment composition of claim 6 , which comprises at least one additive selected from absorbents, astringents, antimicrobial substances, antioxidants, antiperspirants, antifoaming agents, antidandruff active ingredients, antistatics, biological additives, bleaching agents, chelating agents, deodorants, emollients, emulsifiers, emulsion stabilisers, dyes, humectants, film formers, odour substances, flavour substances, insect repellents, preservatives, anticorrosion agents, cosmetic oils, solvents, oxidants, vegetable constituents, buffer substances, reducing agents, surfactants, propellent gases, opacifiers, UV filters, UV absorbers, denaturing agents, viscosity regulators, perfumes and vitamins.

17. An interference pigment, which consists of a low-refractive-index, transparent, SiO 2 flake substrate having only one high-refractive-index coating consisting essentially of TiO 2 having a layer thickness of 70-160 nm and optionally further coated with an outer protective layer,
wherein the pigment exhibits a color flop from the short wave color green at a steep viewing angle to the long wave color red at a flat viewing angle,
wherein the substrate has an average thickness of 0.2 to 0.8 μm and a size in the other two dimensions of between 5 and 60 μm,
wherein the standard deviation of the thickness of the substrate flakes is 10%, based on their average thickness,
wherein the thickness of the high-refractive-index coating is matched to the average thickness of the flake substrate, and
wherein the TiO 2 is in the rutile modification and optionally contains an amount of tin oxide sufficient to provide it in the rutile modification.

Assignees

• Merck Patent Gmbh

Inventors

• Schmidt Christoph
• Delp Tanja
• Schoen Sabine

Classifications

• C09C2200/102

  the core consisting of glass or silicate material like mica or clays, e.g. kaolin · CPC title

• C09C2200/1062

  the core consisting of an organic compound, e.g. Liquid Crystal Polymers [LCP], Polymers or natural pearl essence · CPC title

• C01P2004/54

  Particles characterised by their aspect ratio, i.e. the ratio of sizes in the longest to the shortest dimension · CPC title

• C01P2004/61

  Micrometer sized, i.e. from 1-100 micrometer · CPC title

• C09C2200/1004

  the core comprising at least one inorganic oxide, e.g. Al2O3, TiO2 or SiO2 · CPC title