Abstract

Disclosed herein is a printing method for forming a three dimensional article. The method includes providing a first 3D structural material; depositing a metal nanoparticle ink composition on a surface of the first 3D structural material; annealing the metal nanoparticle ink composition at a temperature of between 60° C. and 100° C. to form the conductive article on the first 3D structural material; and optionally forming a second 3D structural material over the conductive article.

First claim

What is claimed is:

1. A method of forming a three-dimensional (3D) article comprising a conductive article, the method comprising:
providing a first 3D structural material;
depositing a metal nanoparticle ink composition on a surface of the first 3D structural material;
annealing the metal nanoparticle ink composition at a temperature of between 60° C. and 100° C. to form the conductive article on the first 3D structural material;
optionally forming a second 3D structural material over the conductive article; and
melting the first 3D structural material and/or the optional second 3D structural material, thereby forming a free-standing conductive article.

2. The method of claim 1 , wherein the metal nanoparticle ink composition comprises:
an ink vehicle; and
a plurality of metal nanoparticles dispersed in the ink vehicle, the metal nanoparticles including two or more organic stabilizing groups attached thereto, an alkyl moiety of the first organic stabilizing group having a longer carbon chain length than the alkyl moiety of the second organic stabilizing group, the first organic stabilizing group being selected from the group consisting of decylamine, undecylamine, dodecylamine, tridecylamine, tetradecylamine and mixtures thereof, and the second organic stabilizing group being selected from group consisting of butylamine, pentylamine, hexylamine, heptylamine, octylamine, nonylamine, decylamine and mixtures thereof.

3. The method of claim 2 , wherein the metal nanoparticles have a size ranging from about 0.5 nm to about 100 nm, as measured by TEM.

4. The method of claim 2 , wherein the metal nanoparticles comprise at least one metal selected from the group consisting of Al, Ag, Au, Pt, Pd, Cu, Co, Cr, In and Ni.

5. The method of claim 2 , wherein the ink vehicle comprises a first solvent and a second solvent, the first solvent being nonpolar and having a boiling point above 160° C. at 1 atmosphere pressure, and the second solvent having a boiling point above 230° C. at 1 atmosphere pressure, the second solvent being an aromatic hydrocarbon and having a higher boiling point than the first solvent.

6. The method of claim 5 , wherein the first solvent is a saturated or unsaturated C 10 to C 20 hydrocarbon having at least one cyclic group and the second solvent is a C 10 to C 18 arylcycloalkane.

7. The method of claim 5 , wherein the first solvent is a compound selected from the group consisting of bicyclohexane, decalin, naphthalene and combinations thereof, and the second solvent is phenylcyclohexane.

8. The method of claim 1 , wherein the first 3D structural material and the optional second 3D structural material are formed by a process comprising:
providing a phase change material;
heating the phase change material to a jetting temperature;
jetting the phase change material in layers on top of one another, wherein each layer is allowed to cool and/or solidify before jetting a subsequent layer; and
forming the first 3Dstructural material and the optional second 3D structural material from the cool and/or solidified layers.

9. The method of claim 8 , wherein the phase change material comprises a crystalline compound and an amorphous compound.

10. The method of claim 8 , wherein the crystalline compound is selected from the group consisting of dibenzyl hexane-1,6-diyldicarbamate, distearyl terepthalate, polyethylene wax, di-phenylethyl-(L)-tartarate, stereoisomers thereof and mixtures thereof.

11. The method of claim 8 , wherein the amorphous compound is selected from the group consisting of triglycerides of hydrogenated abietic acid, Abitol E succinic acid, Abitol E tartaric acid, dimenthol tartrate, t-Butylcyclohexyl-Cyclohexyl Tartrate, trimenthol citrate, and mixtures thereof.

12. The method of claim 8 , wherein cooling and/or solidifying the jetted layer takes from about 1 to about 10 seconds.

13. The method of claim 8 , wherein the phase change material having a viscosity of about 10 4 cps to about 10 6 cps at a temperature of about 30° C.

14. The method of claim 8 , wherein the viscosity of the phase change material is not altered after the annealing step.

15. A method of forming a three-dimensional (3D) article comprising an embedded conductive article, the method comprising:
providing a first 3D structural material;
depositing a conductive metal ink composition on a surface of the first 3D structural material;
annealing the conductive metal ink composition at a temperature of between 60° C. and 100° C. to form the conductive article on the first 3D structural material;
forming a second 3D structural material over the conductive article, thereby embedding the conductive article therein; and
melting the first 3D structural material and/or the optional second 3D structural material, thereby forming a free-standing conductive article.

16. The method of claim 15 , wherein the metal nanoparticle ink composition comprises:
an ink vehicle; and
a plurality of metal nanoparticles dispersed in the ink vehicle, the metal nanoparticles including both a first organic stabilizing group and a second organic stabilizing group attached thereto, an alkyl moiety of the first organic stabilizing group having a longer carbon chain length than the alkyl moiety of the second organic stabilizing group, the first organic stabilizing group being selected from the group consisting of decylamine, undecylamine, dodecylamine, tridecylamine, tetradecylamine and mixtures thereof, and the second organic stabilizing group is selected from group consisting of butylamine, pentylamine, hexylamine, heptylamine, octylamine, nonylamine, decylamine and mixtures thereof.

17. The method of claim 15 , wherein both the first 3D structural material and the second 3D structural material comprise a phase change material, the phase change material comprises a crystalline compound and an amorphous compound.

18. A method of forming a free-standing conductive article, comprising the steps of:
providing a first 3D structural material;
depositing a conductive metal ink composition on a surface of the first 3D structural material;
annealing the conductive metal ink composition at a temperature of between 60° C. and 100° C. to form the conductive article on the first 3D build material; and
melting the first 3D structural material, thereby forming a free-standing conductive article.

19. The method of claim 18 , wherein the metal nanoparticle ink composition comprises:
an ink vehicle; and
a plurality of metal nanoparticles dispersed in the ink vehicle, the metal nanoparticles including two or more organic stabilizing groups attached thereto, the two or more organic stabilizing groups being selected from the group consisting of butylamine, pentylamine, hexylamine, heptylamine, octylamine, nonylamine, decylamine, undecylamine, dodecylamine, tridecylamine, tetradecylamine, hexadecylamine, diaminopentane, diaminohexane, diaminoheptane, diaminooctane, diaminononane, diaminodecane, diaminooctane, dipropylamine, dibutylamine, dipentylamine, dihexylamine, diheptylamine, dioctylamine, dinonylamine, didecylamine, methylpropylamine, ethylpropylamine, propylbutylamine, ethylbutylamine, ethylpentylamine, propylpentylamine, butylpentylamine, tributylamine and trihexylamine.

Assignees

• Xerox Corp

Inventors

• Goredema Adela
• Smithson Chad S
• Chretien Michelle N
• Abraham Biby Esther
• Jamali Hojjat Seyed

Classifications

• B22F1/10

  Metallic powder containing lubricating or binding agents; Metallic powder containing organic material · CPC title

• B22F1/0545

  Dispersions or suspensions of nanosized particles · CPC title

• B22F10/14

  by jetting of binder onto a bed of metal powder · CPC title

• B22F2998/10

  Processes characterised by the sequence of their steps · CPC title

• C09D11/52

  Electrically conductive inks · CPC title