Method of fabricating metal oxide film

Patent metadata

Field	Value
Publication number	US-10818442-B2
Application number	US-201816220238-A
Country	US
Kind code	B2
Filing date	Dec 14, 2018
Priority date	Dec 27, 2017
Publication date	Oct 27, 2020
Grant date	Oct 27, 2020

Abstract

A method of fabricating a metal oxide film includes sequentially laminating a carbon film and a metal oxide film including nano-sized metal oxide nanoparticles on a porous fuel membrane to form a preliminary composite structure and reducing the metal oxide film to form a composite structure by combusting the porous fuel membrane while applying a voltage to the preliminary composite structure.

First claim

What is claimed is:

1. A method of fabricating a metal oxide film, comprising:
sequentially laminating a carbon film and a metal oxide film including nano-sized metal oxide nanoparticles on a porous fuel membrane as a substrate made of a fuel material to form a preliminary composite structure; and
reducing the metal oxide film to form a composite structure by combusting the porous fuel membrane while applying a voltage to the preliminary composite structure.

2. The method according to claim 1 , wherein the sequentially laminating a carbon film and a metal oxide film including nano-sized metal oxide nanoparticles on a porous fuel membrane to form a preliminary composite structure comprises:
dispersing a carbon nanotube or a graphene in a first dispersing agent solution to prepare a carbon-containing solution;
dispersing the metal oxide nanoparticles in a second dispersing agent solution to prepare a nanoparticle solution;
forming a carbon film on the porous fuel membrane using vacuum filtration of the carbon-containing solution;
forming the metal oxide film on the carbon film using vacuum filtration of the nanoparticle solution; and
evaporating the first dispersing agent solution and the second dispersing agent solution in the metal oxide film, the carbon film, and the porous fuel membrane to form the preliminary composite structure.

3. The method according to claim 1 , wherein in the reducing the metal oxide film to form a composite structure by combusting the porous fuel membrane while applying a voltage to the preliminary composite structure, a combustion wave combusts the porous fuel membrane to heat the metal oxide nanoparticles,
a DC current applied to the preliminary composite structure induces arc discharge on a surface of the carbon film to evaporate the metal oxide nanoparticles, and
the metal oxide nanoparticles are reduced to control a structure thereof while the metal oxide nanoparticles are cooled after generation of the combustion wave.

4. The method according to claim 1 , wherein the porous fuel membrane is nitrocellulose.

5. The method according to claim 1 , wherein the metal oxide nanoparticles include MnO 2 , and
a reduced metal oxide includes at least one of Mn 2 O 3 , Mn 3 O 4 , and MnO.

6. The method according to claim 1 , wherein each of the metal oxide nanoparticles has a diameter of 10 nanometers to 200 nanometers.

7. The method according to claim 1 , wherein each of the metal oxide nanoparticles has a spherical shape, and
a reduced metal oxide has a rod shape or a rounded polyhedral shape.

8. The method according to claim 7 , wherein a nanostructure having the rod shape has a length of 50 nanometers to 700 nanometers and a thickness of 5 nanometers to 50 nanometers.

9. The method according to claim 1 , wherein the carbon film is a filtration substrate made of a carbon nanotube or a graphene.

10. The method according to claim 1 , wherein the voltage is a direct current (DC) voltage or an alternating current (AC) voltage.

Assignees

• Univ Korea Res & Bus Found

Inventors

• Choi Won-Joon
• Yeo Tae-Han
• Shin Dong-Joon

Classifications

• Y02E60/10

  Energy storage using batteries · CPC title

• H01M4/0471

  involving thermal treatment, e.g. firing, sintering, backing particulate active material, thermal decomposition, pyrolysis · CPC title

• H01M4/0421

  involving vapour deposition · CPC title

• H01M4/0416

  involving impregnation with a solution, dispersion, paste or dry powder (H01M4/0438 takes precedence) · CPC title

• H01G11/46 Primary

  Metal oxides · CPC title