Liquid composition and terminal-fitted electric wire

Patent metadata

Field	Value
Publication number	US-10808200-B2
Application number	US-201615574937-A
Country	US
Kind code	B2
Filing date	May 11, 2016
Priority date	May 25, 2015
Publication date	Oct 20, 2020
Grant date	Oct 20, 2020

Abstract

A liquid composition which has an excellent coating property at room temperature and is retained on a surface to be coated after application on the surface, and a terminal-fitted electric wire having an increased corrosion resistance using the same. The liquid composition contains a high-consistency material, a low-viscosity liquid having a kinetic viscosity of 100 mm 2 /s or lower measured at 40° C. in accordance with JIS K2283, and an adduct containing an acidic phosphate ester containing one or more kinds of compounds represented by General Formulae (1) and (2), and a metal,

P(═O)(—OR 1 )(—OH) 2   (1),

P(═O)(—OR 1 ) 2 (—OH)  (2),

where R 1 represents a hydrocarbon group having 4 to 30 carbon atoms.

First claim

The invention claimed is:

1. A liquid composition comprising:
a high-consistency material having a consistency ranging from 50 to 475 when measured at 25° C. in accordance with JIS K2220;
a volatile low-viscosity liquid having a kinetic viscosity of 100 mm 2 /s or lower measured at 40° C. in accordance with JIS K2283, wherein the low-viscosity liquid comprises at least one of a hydrocarbon organic solvent having carbon atoms of 30 or less, an ester organic solvent, an ether organic solvent, a ketone organic solvent, a halogenated hydrocarbon organic solvent, or a volatile oil having a specific gravity of less than 0.8017 at 15° C. and a flash point of −10° C. or higher and lower than 200° C.; and
an adduct comprising:
an acidic phosphate ester comprising one or more kinds of compounds represented by General Formulae (1) and (2); and
a metal,
P(═O)(—OR 1 )(—OH) 2   (1)

P(═O)(—OR 1 ) 2 (—OH)  (2),

where R 1 represents a hydrocarbon group having 4 to 30 carbon atoms.

2. The liquid composition according to claim 1 , wherein the high-consistency material is a grease comprising:
a base oil; and
a thickening agent.

3. The liquid composition according to claim 2 , wherein the thickening agent is a metal soap type or a non-soap urea or bentonite type.

4. The liquid composition according to claim 1 , wherein a content of the low-viscosity liquid is within a range of 10 to 90 mass %.

5. The liquid composition according to claim 1 , wherein R 1 has one or more branched chain structures, or one or more carbon-carbon double bond structures in the structure of the hydrocarbon group having 4 to 30 carbon atoms.

6. The liquid composition according to claim 1 , wherein the metal that forms the adduct with the acidic phosphate ester comprises at least one metal selected from the group consisting of alkali metals, alkaline earth metals, aluminum, titanium, and zinc.

7. The liquid composition according to claim 1 , wherein the adduct comprising the acidic phosphate ester and the metal has a molecular weight of 3000 or lower.

8. The liquid composition according to claim 1 , wherein a mass ratio of the high-consistency material and the adduct comprising the acidic phosphate ester and the metal is within a range of 98:2 to 30:70.

9. The liquid composition according to claim 1 , having a pH of four or higher.

10. The liquid composition according to claim 1 , wherein the composition forms a high-consistency film on a metal surface when applied on the surface, the film comprising:
the high-consistency material; and
the adduct comprising the acidic phosphate ester and the metal.

11. The liquid composition according to claim 1 , wherein the hydrocarbon organic solvent has carbon atoms of 20 or less.

12. The liquid composition according to claim 1 , wherein a boiling point of the hydrocarbon organic solvent is between 80° C. and 250° C.

13. The liquid composition according to claim 1 , wherein the volatile low-viscosity liquid has a kinematic viscosity of 1.46 mm 2 /s or lower measured at 40° C. in accordance with JIS K2283.

14. A terminal-fitted electric wire comprising an electric connecting section between a terminal metal fitting and an electric wire conductor, the electric connecting section covered with a high-consistency film comprising the liquid composition according to claim 1 .

Assignees

• Autonetworks Technologies Ltd
• Univ Kyushu

Inventors

• Nakashima Kazuo
• Hosokawa Takehiro
• Hase Tatsuya
• Rachi Hironobu
• Hirai Hiroki
• Ono Junichi
• Ootsuka Takuji
• Nomura Hideki
• Mizoguchi Makoto

Classifications

• C10M169/02 Primary

  Mixtures of base-materials and thickeners · CPC title

• C10M129/70

  of monocarboxylic acids · CPC title

• H01R4/70

  Insulation of connections (end caps H01R4/22) · CPC title

• C10N2010/06

  Groups 3 or 13 · CPC title

• C10N2030/12

  Inhibition of corrosion, e.g. anti-rust agents or anti-corrosives · CPC title