Epsilon iron oxide and method for producing the same, magnetic coating material and magnetic recording medium

Patent metadata

Field	Value
Publication number	US-10807880-B2
Application number	US-201615735410-A
Country	US
Kind code	B2
Filing date	Jun 13, 2016
Priority date	Jun 12, 2015
Publication date	Oct 20, 2020
Grant date	Oct 20, 2020

Abstract

An epsilon iron oxide has an average particle size of 10 to 18 nm, a part of the iron element being substituted with a substitutional element and has a coercive force of 14 kOe or less, wherein a coefficient of variation of the particle size is 40% or less. A method for producing the same, a magnetic coating material and a magnetic recording medium using the epsilon iron oxide, includes depositing a metal compound of a substitutional element on iron oxide hydroxide to thereby obtain iron oxide hydroxide on which the metal compound is deposited; coating the iron oxide hydroxide on which the metal compound is deposited, with silicon oxide to thereby obtain iron oxide hydroxide coated with the silicon oxide; and applying heat treatment to the silicon oxide-coated iron oxide hydroxide in an oxidizing atmosphere, wherein a part of an iron element is substituted with the substitutional element.

First claim

The invention claimed is:

1. A method for producing epsilon iron oxide, comprising:
depositing a metal compound of a substitutional element on iron oxide hydroxide to thereby obtain iron oxide hydroxide on which the metal compound is deposited;
coating the iron oxide hydroxide on which the metal compound is deposited, with silicon oxide to thereby obtain iron oxide hydroxide coated with the silicon oxide; and
applying heat treatment to the silicon oxide-coated iron oxide hydroxide in an oxidizing atmosphere,
wherein a part of an iron element is substituted with the substitutional element.

2. The method for producing epsilon iron oxide according to claim 1 , wherein the heat-treated powder obtained in the heat-treatment is further treated with an alkali aqueous solution to thereby produce epsilon iron oxide.

3. The method for producing epsilon iron oxide according to claim 1 , wherein obtaining the iron oxide hydroxide on which the metal compound is deposited further comprises:
dissolving a metal salt of the substitutional element in a suspension of the iron oxide hydroxide; and
adding an aqueous alkali solution to the suspension of the iron oxide hydroxide in which the metal salt is dissolved to thereby obtain iron oxide hydroxide on which the metal compound is deposited.

4. The method for producing epsilon iron oxide according to claim 1 , wherein the iron oxide hydroxide on which the metal compound is deposited is coated with silicon oxide and thereafter dried, to thereby obtain silicon oxide-coated iron oxide hydroxide.

5. Epsilon iron oxide in which a part of an iron element is substituted with a substitutional element, and which has an average particle size of 10 to 18 nm, and a coefficient of variation of the particle size of 40% or less,
wherein:
a value of a particle volume (1) is 500 nm 3 or more and a value of a particle volume (2) is 10000 nm 3 or less,

the particle volume (1) is the value of a volume determined by obtaining a standard deviation of a particle size distribution of the epsilon iron oxide, and spherically approximating the epsilon iron oxide particles, in which a value obtained by subtracting the value of the standard deviation from a value of an average particle size of the epsilon iron oxide is regarded as a lower limit of the particle size of the epsilon iron oxide; and
the particle volume (2) is the value of a volume determined by obtaining the standard deviation of the particle size distribution of the epsilon iron oxide, and spherically approximating the epsilon iron oxide particles, in which a value obtained by adding the value of the standard deviation to the average particle size value of the epsilon iron oxide is regarded as an upper limit of the particle size of the epsilon iron oxide.

6. The epsilon iron oxide according to claim 5 , wherein the value obtained by subtracting the value of the particle volume (1) from the value of the particle volume (2) is 5000 nm 3 or less.

7. A magnetic coating material, wherein the epsilon iron oxide of claim 5 is used.

8. A magnetic recording medium, wherein the epsilon iron oxide of claim 5 is used.

9. The method for producing epsilon iron oxide according to claim 2 , wherein obtaining the iron oxide hydroxide on which the metal compound is deposited further comprises:
dissolving a metal salt of the substitutional element in a suspension of the iron oxide hydroxide; and
adding an aqueous alkali solution to the suspension of the iron oxide hydroxide in which the metal salt is dissolved to thereby obtain iron oxide hydroxide on which the metal compound is deposited.

10. The method for producing epsilon iron oxide according to claim 2 , wherein the iron oxide hydroxide on which the metal compound is deposited is coated with silicon oxide and thereafter dried, to thereby obtain silicon oxide-coated iron oxide hydroxide.

11. The method for producing epsilon iron oxide according to claim 3 , wherein the iron oxide hydroxide on which the metal compound is deposited is coated with silicon oxide and thereafter dried, to thereby obtain silicon oxide-coated iron oxide hydroxide.

12. The method for producing epsilon iron oxide according to claim 9 , wherein the iron oxide hydroxide on which the metal compound is deposited is coated with silicon oxide and thereafter dried, to thereby obtain silicon oxide-coated iron oxide hydroxide.

13. A magnetic coating material, wherein the epsilon iron oxide of claim 6 is used.

14. A magnetic recording medium, wherein the epsilon iron oxide of claim 6 is used.

Assignees

• Univ Tokyo
• Dowa Electronics Materials Co Ltd

Inventors

• Ohkoshi Shin-Ichi
• OKA Syunsuke
• Namai Asuka
• Masada Kenji

Classifications

• C01G49/06 Primary

  Ferric oxide [Fe2O3] · CPC title

• C09C1/22

  Compounds of iron {(C09C1/0009, C09C1/0015, C09C1/0078 take precedence)} · CPC title

• C09C1/24

  Oxides of iron · CPC title

• C01P2004/51

  Particles with a specific particle size distribution · CPC title

• C01P2004/64

  Nanometer sized, i.e. from 1-100 nanometer · CPC title