Penflufen polymer particles

Patent metadata

Field	Value
Publication number	US-10798940-B2
Application number	US-201615753209-A
Country	US
Kind code	B2
Filing date	Aug 10, 2016
Priority date	Sep 2, 2015
Publication date	Oct 13, 2020
Grant date	Oct 13, 2020

Abstract

The invention relates to penflufen-containing polymer particles, to penflufen-containing compositions comprising them, to processes for preparing them, and to the use thereof for protecting technical materials, more particularly wood, wood products, and wood-plastic composites.

First claim

What is claimed is:

1. Penflufen-containing polymer particles prepared by polymerization of at least one neutral, uncharged, ethylenically unsaturated monomer of the type M1 selected from the group consisting of styrene, divinylbenzene, esters of monoethylenically unsaturated monocarboxylic and dicarboxylic acids having 3 to 8 carbon atoms with C 1 -C 20 alkanols or with C 5 -C 8 cycloalkanols in an amount of at least 60 wt %, based on the total amount of monomers used,
in the presence of:
penflufen or its salts and acid addition compounds, and
an oil-soluble radical initiator selected from the group consisting of 2,2′-azobisisobutyronitrile, 2,2′-azobis(2-methylbutyronitrile), and mixtures thereof, in an oil-in-water emulsion polymerization.

2. The penflufen-containing polymer particles as claimed in claim 1 , wherein the ethylenically unsaturated monomers are selected from the group consisting of methyl acrylate, ethyl acrylate, n-butyl acrylate, isobutyl acrylate, tert-butyl acrylate, n-hexyl acrylate, 2-ethylhexyl acrylate, 3-propylheptyl acrylate, stearyl acrylate, methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, isobutyl methacrylate, tert-butyl methacrylate, n-hexyl methacrylate and stearyl methacrylate, divinylbenzene and mixtures of these monomers.

3. The penflufen-containing polymer particles as claimed in claim 1 , wherein the ethylenically unsaturated monomers are composed of 80 to 99.9 wt% of monomers M1 and 0.1 wt% to 20 wt% of monomers M2, based on the total amount of monomers used, wherein the monomers M2 are selected from the group consisting of α,β-ethylenically unsaturated C 3 -C 8 monocarboxylic and C 4 -C 8 dicarboxylic acids, 2-(N,N,N-trimethylammonium)ethyl acrylate chloride, 2-(N,N,N-trimethylammonium)ethyl methacrylate chloride, 2-(N,N,N-trimethylammonium)ethylmethacrylamide chloride, 3-(N,N,N-trimethylammonium)propylacrylamide chloride, 3-(N,N,N-trimethylammonium)propylmethacrylamide chloride, 2-(N,N,N-trimethylammonium)ethylacrylamide chloride, and also the corresponding methosulfates and sulfates, and mixtures of these monomers.

4. The penflufen-containing polymer particles as claimed in claim 3 , wherein:
an amount of penflufen or its salts and acid addition compounds is 0.5 to 15 wt%, based on the total amount of monomers used; and
an amount of initiators is 0.1 wt% to 5 wt%, based on the total amount of monomers used.

5. The penflufen-containing polymer particles as claimed in claim 4 , wherein the amount of the initiators is 0.1 wt% to 3 wt%, based on the total amount of monomers.

6. The penflufen-containing polymer particles as claimed in claim 1 , wherein an amount of penflufen or its salts and acid addition compounds is between 0.5 to 15 wt%, based on the total amount of monomers used.

7. The penflufen-containing polymer particles as claimed in claim 1 , additionally comprising further antimicrobially active compounds selected from fungicides, bactericides, herbicides and insecticides.

8. The penflufen-containing polymer particles as claimed in claim 1 , wherein the particles have a diameter of 100 nm to 1 μm.

9. A penflufen-containing composition comprising penflufen-containing polymer particles as claimed in claim 1 , and at least one solvent or diluent.

10. A process for preparing the penflufen-containing polymer particles of claim 1 , the process comprising polymerizing the at least one ethylenically unsaturated monomer of the type M1 in the presence of:
the penflufen or its salts and acid addition compounds, and
the oil-soluble radical initiator,
in the oil-in-water emulsion polymerization.

11. The process for preparing penflufen-containing polymer particles as claimed in claim 10 , wherein the polymerization is carried out at a temperature of 50° C. to 90° C.

12. The process for preparing the penflufen-containing polymer particles as claimed in claim 10 , wherein the polymerization is conducted in the presence of C 14 - C 25 alkanes and C 14 -C 25 cycloalkanes, and mixtures thereof.

13. A method for protecting technical materials against destruction by microorganisms, the method comprising incorporating the penflufen-containing polymer particles as claimed in claim 1 into technical materials.

14. The method as claimed in claim 13 , wherein the technical material is wood, wood-plastic composites, and/or a wood product.

Assignees

• Lanxess Deutschland Gmbh

Inventors

• Uhr Hermann
• Jaetsch Thomas

Classifications

• C08F18/00

  Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an acyloxy radical of a saturated carboxylic acid, of carbonic acid or of a haloformic acid · CPC title

• C08F20/00

  Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride, ester, amide, imide or nitrile thereof · CPC title

• C08F2/22

  Emulsion polymerisation · CPC title

• C08F220/14

  Methyl esters {, e.g. methyl (meth)acrylate} · CPC title

• C08F10/00

  Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond · CPC title