Metal effect pigments with high chroma and high brilliancy, method for the production and use thereof

Patent metadata

Field	Value
Publication number	US-10759941-B2
Application number	US-201515536945-A
Country	US
Kind code	B2
Filing date	Dec 21, 2015
Priority date	Dec 19, 2014
Publication date	Sep 1, 2020
Grant date	Sep 1, 2020

Abstract

The invention relates to a metal effect pigment including a metallic substrate in platelet form and a coating applied thereto, wherein the coating includes a spacer layer. The invention further relates to a process for production of and to the use of the metal effect pigment.

First claim

The invention claimed is:

1. A metal effect pigment comprising a metallic platelet-shaped substrate and a coating applied to the substrate, wherein the coating comprises:
a) optionally a layer 1 which comprises or consists of at least one of tin oxide, tin hydroxide or tin oxide hydrate,
b) a layer 2 comprising at least one of metal oxide, metal hydroxide or metal oxide hydrate, and
c) a layer 3 comprising at least one of metal oxide, metal hydroxide or metal oxide hydrate,
and wherein at least one of layers 2 or 3 comprises at least two different metal ions and layers 2 and 3 are interrupted by a spacer layer,
wherein the spacer layer has connections and cavities and wherein the spacer layer has a network density of <85%, wherein the network density is defined as the number of connections or spacers per number of lines in %, determined from a grid of parallel lines drawn at 50 nm intervals at a 90° angle from a baseline drawn onto each scanning electron micrograph of a traverse section along the surface of a longer side of the metallic substrate.

2. The metal effect pigment according to claim 1 , wherein the network density of the spacer layer ranges from 1% to 75%.

3. The metal effect pigment according to claim 1 , wherein the network density of the spacer layer ranges from 1% to 63%.

4. The metal effect pigment according to claim 1 , wherein the network density of the spacer layer ranges from 1% to 49%.

5. The metal effect pigment as claimed in claim 1 , wherein the at least two different metal ions of layer 2 and/or 3 are selected from the group of metals consisting of Ti, Fe, Sn, Mn, Zr, Ca, Sr, Ba, Ni, Sb, Ag, Zn, Cu, Ce, Cr, and Co.

6. The metal effect pigment as claimed in claim 1 , wherein the metallic substrate selected from the group consisting of aluminum platelets, copper platelets, zinc platelets, iron platelets, titanium platelets, stainless steel platelets, silver platelets, alloys and mixtures of the above-listed metals.

7. The metal effect pigment as claimed in claim 1 , wherein the effect pigment comprises further layers of high and low refractive index and optionally at least one further spacer layer.

8. The metal effect pigment as claimed in claim 1 , wherein the at least one spacer layer has a mean height h a in each case from a range from 5 nm to 120 nm.

9. The metal effect pigment as claimed in claim 1 , wherein the at least one spacer layer is arranged essentially parallel to the surface of the non-metallic substrate in platelet form.

10. The metal effect pigment as claimed in claim 1 , wherein the space layer is distributed over the entire metal effect pigment, and has an area proportion of cavities from a range from 51% to 99% and an area proportion of connections from a range from 1% to 49%, measured using scanning electron of transverse sections.

11. An article comprising at least one metal effect pigment as claimed in claim 1 .

12. The metal effect pigment according to claim 1 ,
wherein the spacer layer has a standard deviation of the relative height of σh Rma in a range of 0.2 to 18%, wherein the relative height h Rma is defined as the ratio of the height h ma to the layer thickness of the overall coating and h ma refers to the sum total of the layer thickness of optional layer 1 , layer 2 and half the height ha of the spacer layer.

13. The metal effect pigment according to claim 12 , wherein the mean height of the spacer layer is determined by the following method:
the effect pigments are applied in a lacquer and cross sections are prepared and scanning electron micrographs analyzed thereof comprising the steps:
establishing the upper and lower substrate surfaces as baselines which are the longer side of the nonmetallic substrate in platelet form in each case and drawing the baselines onto the scanning electron micrograph of the transverse section,
analyzing the scanning electron micrographs of the transverse sections with the aid of the AxioVision 4.6.3 image processing software (from Zeiss),
drawing a sufficient number of parallel lines at 50 nm intervals at a 90° angle with respect to the upper and lower baselines corresponding to the two surfaces of the substrate in platelet form establishing a grid over the effect pigment shown in the scanning electron micrograph of a transverse section ( FIG. 4 ) using a magnification of at least 50 000-fold, based on Polaroid 545 (4″×5″),
proceeding from the respective baseline of the metallic substrate in platelet form, in the direction of the respective layer 3 or the respective outermost layer, the points of intersection between the parallel lines arranged at right angles to the respective baseline with the respective interfaces of the optional layer 1 with layer 2 , of layer 2 with the spacer layer, of the spacer layer with layer 3 , and of layer 3 with the environment or with any further layer applied, is recorded;
determining the thicknesses of layers 2 and 3 , the layer thickness of the overall coating, the layer thickness of further layers optionally present, and the height h a of the spacer layer by formation of differences, wherein the layer thickness of layer 2 is calculated from the difference between the respective measured points of intersection at the respective interfaces of layer 2 with the spacer layer and of either optional layer 1 or the baseline with layer 2 if the nonmetallic substrate has not been covered with further layers beforehand, and the layer thickness of layer 3 is calculated from the difference between the respective measured points of intersection at the respective interfaces of layer 3 with the environment or with any further layer applied and of the spacer layer with layer 3 and the height h a is calculated from the difference between the respective measured points of intersection of spacer layer with layer 3 and layer 2 with the spacer layer,

wherein the height h a is determined by forming the arithmetic mean by conducting this procedure to at least 100 of the parallel lines arranged at right angles to the baselines.

14. The metal effect pigment according to claim 12 , wherein the standard deviation σh Rma of the relative height is within a range from 0.3% to 15%.

Assignees

• Eckart Gmbh

Inventors

• Grüner Michael
• Kaupp Günter
• Schneider Ralph

Classifications

• C09C2200/1054

  the core consisting of a metal · CPC title

• C09C1/62

  Metallic pigments or fillers {(C09C1/0015 takes precedence)} · CPC title

• C09C2200/301

  Thickness of the core · CPC title

• C01P2006/63

  a* (red-green axis) · CPC title

• C09C2220/106

  comprising only a drying or calcination step of the finally coated pigment · CPC title