Abstract

The present invention relates to a method for manufacturing of a laminated cellulose-based liquid or semi-liquid food packaging material, wherein the laminated packaging material has a bulk material layer comprising a low-density cellulose spacer layer, an outside module comprising a substrate layer having a print surface and an inside material module comprising a barrier layer or barrier coating. The invention further relates the laminated packaging materials obtained by the method and to a packaging container for liquid food packaging, comprising the laminated packaging material or being made from the laminated packaging material obtained by the method.

First claim

The invention claimed is:

1. Method of manufacturing a laminated cellulose-based liquid or semi-liquid food packaging material, for heat sealing into packaging containers having mechanical strength and barrier properties, the method comprising
a) providing a web of a center module of bulk material comprising a cellulose spacer layer, which has a density below 850 kg/m 3 , a grammage from 60 to 250 g/m 2 , and is containerboard material having a Short Compression Test Index value of at least 30 Nm/g in the machine direction, as determined in accordance with ISO 9895 and ISO 536,
b) providing a web of an outside material module, comprising a paper facing layer having a printable or printed surface directed towards an outer side of the outside material module, the outside material module being intended for that side of the center module of bulk material, which is to be directed to an outside of the packaging container made from the laminated packaging material,
c) laminating an outside of the web of the center module of bulk material and the web of the outside material module to each other,
d) adding print to the outside material module,
e) providing a web of an inside material module, comprising a paper facing layer and a barrier coating, the inside material module being intended for that side of the bulk material, which is to be directed to an inside of the packaging container made from the laminated packaging material,
f) laminating the web of the inside material module and the inside of the web of the center module of bulk material to each other,
g) applying an outermost, transparent and liquid-tight protective layer on an outside of the outside material module,
h) applying an outermost thermoplastic, liquid-tight and heat sealable layer on an inside of the inside material module,
i) thus obtaining a web of a laminated cellulose-based liquid- or semi-liquid food packaging material,
wherein the spacer layer constitutes a center of a sandwich structure within the laminated packaging material, the sandwich structure having the paper facing layer of the web of the outside material module arranged on at least one side of the spacer layer and interacting with the paper facing layer of the web of the inside material module arranged on an other side of the spacer layer, the paper facing layer of the web of the outside material module and the paper facing layer of the web of the inside material module having lower thickness and a higher Young's modulus than the spacer layer.

2. Method as claimed in claim 1 , wherein the center module of bulk material also comprises an integrated paper facing layer directly adjacent the spacer layer on an inside of the spacer layer.

3. Method as claimed in claim 1 , wherein the center module of bulk material comprises a paper facing layer directly adjacent on an outside of the spacer layer.

4. Method as claimed in claim 2 , wherein the paper facing layer of the center module of bulk material has a grammage from 20 to 100 g/m 2 , a density from 600 to 1500 kg/m 3 and a Young's modulus from 1 to 10 GPa.

5. Method as claimed in claim 1 , wherein the inside material module comprises a polymer film having the barrier coating, the polymer film being laminated to an inside surface of the bulk material by an intermediate bonding layer or adhesive.

6. Method as claimed in claim 1 , wherein the paper facing later of the web of the outside material module includes the printable surface, and the printable surface is a clay-coated white paper surface or a metallised film or metallised paper surface.

7. Method as claimed in claim 1 , wherein the outside material module is laminated to the bulk material by applying an aqueous adhesive composition at an amount from 0.5 to 4 g/m 2 to one of the surfaces to be laminated to each other and pressing them together.

8. Method as claimed in claim 1 , wherein the inside material module is laminated to the bulk material by applying an aqueous adhesive composition at an amount from 0.5 to 4 g/m 2 to one of the surfaces to be laminated to each other and pressing them together.

9. Laminated packaging material obtained by the method as claimed in claim 1 .

10. Packaging container comprising the laminated packaging material obtained by the method as claimed in claim 1 .

11. Method as claimed in claim 1 , wherein the barrier coating is a liquid-film coated barrier comprising a polymer selected from the group consisting of vinyl alcohol-based polymers, acrylic acid or methacrylic acid based polymers (PAA, PMAA), polysaccharides, cellulose nanofibrils (CNF), nanocrystalline cellulose (NCC), chitosan or other cellulose derivatives, hemicelluloses, water dispersible polyvinylidenechloride (PVDC) or water dispersible polyesters, or combinations of two or more thereof.

12. Method as claimed in claim 11 , wherein the liquid-film coated barrier is PVOH or water dispersible EVOH.

13. Method as claimed in claim 11 , wherein the liquid-film coated barrier is is a starch or starch derivative.

14. Method as claimed in claim 1 , wherein the barrier coating is applied by physical vapour deposition or chemical vapour deposition onto a surface of the paper facing layer.

15. Method of manufacturing a laminated cellulose-based liquid or semi-liquid food packaging material, for heat sealing into packaging containers having mechanical strength and barrier properties, the method comprising
a) providing a web of a center module of bulk material comprising a cellulose spacer layer, which has a density below 850 kg/m 3 , a grammage from 60 to 250 g/m 2 , and is a containerboard material having a Short Compression Test Index value of at least 30 Nm/g in the machine direction, as determined in accordance with ISO 9895 and ISO 536,
b) providing a web of an outside material module, comprising a first paper facing layer having a printable or printed surface directed towards an outer side of the outside material module, the outside material module being intended for that side of the center module of bulk material, which is to be directed to an outside of the packaging container made from the laminated packaging material,
c) laminating an outside of the web of the center module bulk of material and the web of the outside material module to each other by applying an aqueous adhesive composition at an amount from 0.5 g/m 2 to 4 g/m 2 to a surface of the web of the center module of bulk material or the web of the outside material module and then pressing the web of the center module of bulk material and the web of the outside material module together,
d) adding print to the outside material module,
e) providing a web of an inside material module, comprising a second paper facing layer and a barrier coating, the inside material module being intended for that side of the bulk material, which is to be directed to an inside of the packaging container made from the laminated packaging material,
f) laminating the web of the inside material module and an inside of the web of the center module of bulk material to each other by applying an aqueous adhesive composition at an amount from 0.5 g/m 2 to 4 g/m 2 to a surface of the web of the center module of bulk material or the web of the inside material module and then pressing the web of the center module of bulk material and the web of the inside material module together,
g) applying an outermost, transparent and liquid-tight protective layer on an outside of the outside material module,
h) applying an outermost thermoplastic, liquid-tight and heat sealable layer on an inside of the inside material module,
i) thus obtaining a web of a laminated cellulose

Assignees

• Tetra Laval Holdings & Finance

Inventors

• Toft Nils
• Nyman Ulf
• Frisk Peter
• Collaud Alain
• Öhman Peter

Classifications

• B32B7/02

  Physical, chemical or physicochemical properties · CPC title

• B32B7/022

  Mechanical properties · CPC title

• B65D85/72

  for edible or potable liquids, semiliquids, or plastic or pasty materials · CPC title

• B65D65/40

  Applications of laminates for particular packaging purposes {(B65D1/0215, B65D1/28, B65D3/22, B65D5/0281, B65D5/563, B65D9/30, B65D29/02, B65D31/02, B65D75/26, B65D77/2024, B65D81/1275, B65D81/3811, B65D81/3823, B65D81/3834, B65D81/3846, B65D81/3858, B65D81/3874, B65D81/3886, B65D81/3897 take precedence; laminates per se or laminated packages characterised by the composition or)} · CPC title

• B32B2439/70

  Food packaging · CPC title