Ultrafiltration membranes and methods of making

Patent metadata

Field	Value
Publication number	US-10751669-B2
Application number	US-201514645631-A
Country	US
Kind code	B2
Filing date	Mar 12, 2015
Priority date	Jun 30, 2006
Publication date	Aug 25, 2020
Grant date	Aug 25, 2020

Abstract

The present invention is an integral multilayered composite membrane having at least one ultrafiltration layer made by cocasting or sequentially casting a plurality of polymer solutions onto a support to form a multilayered liquid sheet and immersing the sheet into a liquid coagulation bath to effect phase separation and form a multilayered composite membrane having at least one ultrafiltration layer.

First claim

What is claimed:

1. A multilayered, flat sheet, composite membrane produced from at least two polymer solutions, the flat sheet membrane having at least one asymmetric ultrafiltration layer in which particles having a 20 to 100 nanometer (nm) diameter are retained and at least one asymmetric microporous layer in which particles larger than 0.1 μm are retained, wherein the polymer solutions include a first polymer solution that forms the at least one ultrafiltration layer and a second polymer solution that forms the at least one microporous layer, wherein the multilayered membrane has an integral transition zone between the at least one ultrafiltration layer and the at least one microporous layer, wherein the transition zone is a region comprising a gradient of pore sizes between the at least one ultrafiltration layer to the at least one microporous layer.

2. The multilayered, flat sheet, composite membrane according to claim 1 , wherein the ultrafiltration layer comprises a skinned, asymmetric ultrafiltration membrane layer.

3. The multilayered, flat sheet, composite membrane according to claim 1 , wherein the second polymer solution has a lower critical solution temperature (LCST).

4. The multilayered, flat sheet, composite membrane according to claim 1 , wherein both the first polymer solution and the second polymer solution have a lower critical solution temperature (LCST).

5. The multilayered, flat sheet, composite membrane according to claim 4 , wherein the LCST of the first polymer solution is higher than the LCST of the second polymer solution.

6. The multilayered, flat sheet, composite membrane according to claim 1 , wherein the polymers for the first and second polymer solutions are independently selected from the group consisting of polyvinylidene fluoride, nylons, polyamides, polyimides, polyetherimides, polyethersulfones, polysulfones, polyarylsulfones, cellulose, regenerated cellulose, cellulose esters, polystyrenes, acrylic polymers methacrylic polymers, copolymers acrylic methacrylic polymers, and combinations thereof.

7. The multilayered, flat sheet, composite membrane according to claim 1 , wherein the ultrafiltration layer is 2 to 100 microns thick and the microporous layer is 50-200 microns thick.

8. The multilayered, flat sheet, composite membrane according to claim 1 , wherein the ultrafiltration layer is 2 to 50 microns thick.

9. The multilayered, flat sheet, composite membrane according to claim 1 , wherein the microporous layer is 80 to 150 microns thick.

10. The multilayered, flat sheet, composite membrane according to claim 1 , wherein the membrane is 90 to 120 microns thick.

11. The multilayered, flat sheet, composite membrane according to claim 1 , wherein the polymer solution that forms the at least one ultrafiltration layer has a polymer content of 15% to 30% polymer solids.

12. The multilayered, flat sheet, composite membrane according to claim 1 , wherein the polymer solution that forms the at least one microporous layer has a polymer content of 10% to 20% polymer solids.

13. The multilayered, flat sheet, composite membrane according to claim 1 , wherein the ultrafiltration membrane layer has pores sized to retain a parvo virus.

Assignees

• Emd Millipore Corp

Inventors

• Tkacik Gabriel
• Goddard Philip
• Kools Willem
• Satav Nitin

Classifications

• B01D67/00165

  Composition of the coagulation baths · CPC title

• B01D2325/022

  Asymmetric membranes · CPC title

• B01D67/0013

  Casting processes · CPC title

• B01D69/1213 Primary

  Laminated layers · CPC title

• B01D2323/12

  Specific ratios of components used · CPC title