Hiding by using air voids encapsulated in hollow glass spheres

Patent metadata

Field	Value
Publication number	US-10745574-B2
Application number	US-201615290512-A
Country	US
Kind code	B2
Filing date	Oct 11, 2016
Priority date	Oct 11, 2016
Publication date	Aug 18, 2020
Grant date	Aug 18, 2020

Abstract

A paint composition with improved hiding power includes water, a film-forming polymer, pigments, and a plurality of hollow glass spheres dispersed in the paint composition. Advantageously, the hollow glass spheres encapsulate air voids in coatings formed from the paint composition.

First claim

What is claimed is:

1. A paint composition comprising:
water;
a film-forming polymer that includes polyvinyl alcohol;
pigments selected from the group consisting of azo dyes, phthalocyanine, anthraquinone dyes, and combinations thereof; and
a plurality of hollow glass spheres dispersed in the paint composition, the hollow glass spheres encapsulating air voids in coatings formed from the paint composition and having an average diameter greater than or equal to 12 microns and less than or equal to 50 microns wherein the plurality of hollow glass spheres is present in an amount of 10-40 pounds of hollow glass spheres per 100 gallons of paint.

2. The paint composition of claim 1 wherein the film-forming polymer is an emulsion polymer.

3. The paint composition of claim 1 wherein the hollow glass spheres can replace a portion of the pigments or be added in addition to pigments in a standard paint composition.

4. The paint composition of claim 1 wherein the pigments include titanium oxide.

5. The paint composition of claim 1 wherein:
the film-forming polymer is present in an amount from about 25 to 60 weight percent of the total weight of the paint composition;
the pigments are present in an amount from about 5 to 40 weight percent of the total weight of the paint composition;
the plurality of hollow glass spheres is present in an amount from about 0.1 to 8 weight percent of the total weight of the paint composition; and
the balance is water.

6. The paint composition of claim 5 further comprising one or more additives selected from the group consisting of rheology modifiers, surfactants, defoamers, organic solvents, pH adjusters, dispersants, coalescents, biocides, and combinations thereof.

7. The paint composition of claim 6 wherein the additives are present in an amount from about 0.1 to 20 weight percent of the total weight of the paint composition.

8. The paint composition of claim 1 wherein the film-forming polymer is formed by one or more monomers selected from the group consisting of methacrylate, methyl acrylate, ethyl acrylate, 2-chloroethyl vinyl ether, 2-ethylhexyl acrylate, hydroxyethyl methacrylate, butyl acrylate, butyl methacrylate, trimethylolpropane triacrylate, pentafluorophenyl methacrylate, pentafluorophenyl acrylate, 1,1,1,3,3,3-hexafluoroisopropyl acrylate, bis-(2,2,2-trifluoroethyl) itaconate, bis-(1,1,1,3,3,3-hexafluoroisopropyl), 1H,1H,3H-hexafluorobutyl acrylate, 1H,1H,7H-dodecafluoroheptyl methacrylate, 2,2,2-trifluoroethyl acrylate, 2,2,2-trifluoroethyl methacrylate, aliphatic, fluorinated aliphatic, 1H,1H,2H,2H-Heptadecafluorodecyl methacrylate 532.2 acrylic, 1H,1H,2H,2H-heptadecafluorodecyl acrylate, 1H,1H,5H-octafluoropentyl acrylate, 1H,1H,3H-tetrafluoropropyl methacrylate, hexafluoro-iso-propyl, 1H,1H,3H-hexafluorobutyl methacrylate, 1H,1H,5H-octafluoropentyl methacrylate, ethylene, propylene, 1-butylene, 2 butylene, vinyl acetate, functional monomers, phosphorus-containing functional monomers, acidic group monomers, and combinations thereof.

9. The paint composition of claim 1 wherein the plurality of hollow glass spheres has the average diameter greater than or equal to 15 microns and less than or equal to 25 microns.

10. A paint composition comprising:
water;
a film-forming polymer that includes polyvinyl alcohol;
pigments; and
a plurality of hollow glass spheres dispersed in the paint composition, the hollow glass spheres encapsulating air voids in coatings formed from the paint composition and having an average diameter greater than or equal to 12 microns and less than or equal to 50 microns.

11. The paint composition of claim 10 wherein the film-forming polymer is an emulsion polymer.

12. The paint composition of claim 11 wherein the emulsion polymer is acrylic polymer, vinyl acrylic copolymer, ethylene-vinyl acetate copolymer, styrene-acrylic copolymer, or polyvinyl alcohol.

13. The paint composition of claim 10 wherein the hollow glass spheres can replace a portion of the pigments or be added in addition to pigments in a standard paint composition.

14. The paint composition of claim 10 wherein the pigments include titanium oxide.

15. The paint composition of claim 10 wherein the plurality of hollow glass spheres is present in an amount of 5 to 65 pounds of hollow glass spheres per 100 gallons of paint.

16. The paint composition of claim 10 wherein the plurality of hollow glass spheres is present in an amount of 10-40 pounds of hollow glass spheres per 100 gallons of paint.

17. The paint composition of claim 10 wherein:
the film-forming polymer is present in an amount from about 25 to 60 weight percent of the total weight of the paint composition;
the pigments are present in an amount from about 5 to 40 weight percent of the total weight of the paint composition;
the plurality of hollow glass spheres is present in an amount from about 0.1 to 8 weight percent of the total weight of the paint composition; and
the balance is water.

18. The paint composition of claim 17 further comprising one or more additives selected from the group consisting of rheology modifiers, surfactants, defoamers, organic solvents, pH adjusters, dispersants, coalescents, biocides, and combinations thereof.

19. The paint composition of claim 18 wherein the additives are present in an amount from about 0.1 to 20 weight percent of the total weight of the paint composition.

20. The paint composition of claim 10 wherein the film-forming polymer is formed by one or more monomers selected from the group consisting of methacrylate, methyl acrylate, ethyl acrylate, 2-chloroethyl vinyl ether, 2-ethylhexyl acrylate, hydroxyethyl methacrylate, butyl acrylate, butyl methacrylate, trimethylolpropane triacrylate, pentafluorophenyl methacrylate, pentafluorophenyl acrylate, 1,1,1,3,3,3-hexafluoroisopropyl acrylate, bis-(2,2,2-trifluoroethyl) itaconate, bis-(1,1,1,3,3,3-hexafluoroisopropyl), 1H,1H,3H-hexafluorobutyl acrylate, 1H,1H,7H-dodecafluoroheptyl methacrylate, 2,2,2-trifluoroethyl acrylate, 2,2,2-trifluoroethyl methacrylate, aliphatic, fluorinated aliphatic, 1H,1H,2H,2H-Heptadecafluorodecyl methacrylate 532.2 acrylic, 1H,1H,2H,2H-heptadecafluorodecyl acrylate, 1H,1H,5H-octafluoropentyl acrylate, 1H,1H,3H-tetrafluoropropyl methacrylate, hexafluoro-iso-propyl, 1H,1H,3H-hexafluorobutyl methacrylate, 1H,1H,5H-octafluoropentyl methacrylate, ethylene, propylene, 1-butylene, 2 butylene, vinyl acetate, functional monomers, phosphorus-containing functional monomers, acidic group monomers, and combinations thereof.

21. The paint composition of claim 10 wherein the plurality of hollow glass spheres has the average diameter greater than or equal to 15 microns and less than or equal to 25 microns.

22. The paint composition of claim 10 wherein the pigments are selected from the group consisting of azo dyes, phthalocyanine, anthraquinone dyes, and combinations thereof.

Assignees

• Behr Process Corp

Inventors

• Tarng Ming-Ren
• Yen Ying-Chieh
• Shi Jinzhen
• Cantrell Roanic Greydon
• Xue Chenming

Classifications

• C09D7/70 Primary

  characterised by shape, e.g. fibres, flakes or microspheres · CPC title

• C09D129/04

  Polyvinyl alcohol; Partially hydrolysed homopolymers or copolymers of esters of unsaturated alcohols with saturated carboxylic acids · CPC title

• C08K2003/2241

  Titanium dioxide · CPC title

• C09D5/024

  characterised by the additives · CPC title

• C09D129/02

  Homopolymers or copolymers of unsaturated alcohols (C09D129/14 takes precedence) · CPC title