Honeycomb catalyst for removal of nitrogen oxides in flue and exhaust gasses and method of preparation thereof

Patent metadata

Field	Value
Publication number	US-10737258-B2
Application number	US-201615754748-A
Country	US
Kind code	B2
Filing date	Oct 26, 2016
Priority date	Oct 28, 2015
Publication date	Aug 11, 2020
Grant date	Aug 11, 2020

Abstract

A vanadium oxide based honeycomb SCR catalyst composed of a plurality of corrugated sheets stacked upon one another to form a plurality of flow through channels, the corrugated sheets are provided with an inert inner core layer and an outermost layer containing a SCR catalyst composition.

First claim

The invention claimed is:

1. A honeycomb SCR catalyst composed of a plurality of corrugated sheets stacked upon one another to form a plurality of flow-through channels,
wherein each corrugated sheet comprises an inner core layer comprising entangled non-woven fibers coated with a clay material on both sides of each of the corrugated sheets, and an outermost layer supported on both sides of the inner core layer, the outermost layer comprising an SCR catalyst composition, the inner core layer makes up between 50% and 95% of the channel walls thickness.

2. The honeycomb catalyst of claim 1 , wherein the non-woven fibers are glass fibers.

3. The honeycomb catalyst of claim 2 , wherein the inner core layer further comprises diatomaceous earth.

4. The honeycomb catalyst of claim 1 , wherein the inner core layer comprises diatomaceous earth.

5. The honeycomb catalyst of claim 1 , wherein each outermost layer has a layer thickness of between 0.05 mm and 0.6 mm.

6. The honeycomb catalyst of claim 1 , wherein the inner core layer has a layer thickness of between 0.6 mm and 1.2 mm.

7. The honeycomb catalyst of claim 1 , wherein the SCR catalyst composition comprises titania and an oxide of vanadium.

8. The honeycomb catalyst of claim 7 , wherein the oxide of vanadium is vanadium pentoxide in an amount of between 1 and 5% by weight.

9. The honeycomb catalyst of claim 7 , further comprising an oxide of tungsten.

10. The honeycomb catalyst of claim 1 further comprising a liner arranged on each of the corrugated sheets.

11. A method of preparing a honeycomb SCR catalyst with a plurality of flow-through channels comprising the steps of:
(a) providing sheets of entangled non-woven fibers;
(b) corrugating the sheets;
(c) stacking the corrugated sheets obtained in step (b) to form a honeycomb structure substrate;
(d) coating the corrugated sheets of the honeycomb structured substrate with a clay material to obtain an inner core layer in each of the corrugated sheets and drying and/or calcining the honeycomb structured substrate such that the inner core layer makes up between 50% and 95% of the channel walls thickness;
(e) coating each side of the inner core layer of each of the corrugated sheets in the honeycomb structured substrate with a catalyst coat layer comprising an SCR catalyst composition or a precursor thereof; and
(f) calcining the honeycomb structured substrate of step (e) to obtain the honeycomb SCR catalyst.

12. The method of claim 11 , wherein each corrugated sheet obtained in step (b) is lined with a liner prior to stacking.

13. The method of claim 11 , wherein the liner is coated with a clay material.

14. The method of claim 11 , wherein the non-woven fibers are glass fibers.

15. The method of claim 11 , wherein the clay material further comprises diatomaceous earth.

16. The method of claim 11 , wherein the catalyst coat layer has a layer thickness of between 0.05 mm and 0.6 mm.

17. The method of claim 11 , wherein the inner core layer has a layer thickness of between 0.6 mm and 1.2 mm.

18. The method of claim 11 , wherein the SCR catalyst composition comprises titania and an oxide of vanadium.

19. The method of claim 18 , wherein the oxide of vanadium is vanadium pentoxide applied in an amount of between 1 and 5% by weight.

20. The method of claim 18 , wherein the SCR catalyst composition further comprises an oxide of tungsten.

21. A method of preparing the honeycomb SCR catalyst of claim 1 , the method comprising the steps of:
(a) providing the sheets of entangled non-woven fibers;
(b) corrugating the sheets;
(c) stacking the corrugated sheets obtained in step (b) to form the honeycomb structure substrate;
(d) coating the corrugated sheets of the honeycomb structured substrate with the clay material to obtain the inner core layer in each of the corrugated sheets and drying and/or calcining the honeycomb structured substrate;
(e) coating each side of the inner core layer of each of the corrugated sheets in the honeycomb structured substrate with the catalyst coat layer comprising the SCR catalyst composition or a precursor thereof; and
(f) calcining the honeycomb structured substrate of step (e) to obtain the honeycomb SCR catalyst.

Assignees

• Umicore Ag & Co Kg

Inventors

• Abrams Billie Lynn
• Castellino Francesco

Classifications

• B01J23/30 Primary

  Tungsten · CPC title

• B01D53/8628

  Processes characterised by a specific catalyst · CPC title

• B01J35/56 Primary

  Foraminous structures having flow-through passages or channels, e.g. grids or three-dimensional [3D] monoliths · CPC title

• B01J35/57

  Honeycombs · CPC title

• B01D53/9418

  for removing nitrogen oxides by selective catalytic reduction [SCR] using a reducing agent in a lean exhaust gas · CPC title