System for forming elastomeric compositions for application to metal

Patent metadata

Field	Value
Publication number	US-10731052-B2
Application number	US-201615551084-A
Country	US
Kind code	B2
Filing date	Feb 10, 2016
Priority date	Feb 16, 2015
Publication date	Aug 4, 2020
Grant date	Aug 4, 2020

Abstract

A system for forming an elastomeric composition for application to a substrate includes an isocyanate component and an isocyanate-reactive component. The isocyanate component includes a polymeric polyisocyanate and optionally an isocyanate-terminated prepolymer. The isocyanate-reactive component is reactive with the isocyanate component and includes a polyol component and a polyetheramine. The polyol component is a mixture of (a) a hydrophobic polyol; (b) a polyether polyol different than the hydrophobic polyol and having a weight average molecular weight greater than 500 g/mol; and (c) a polyaminopolyol. The elastomeric composition is formed as the reaction product of the isocyanate component and the isocyanate-reactive component and may be applied as an elastomeric coating layer on a substrate such as a steel pipe. The steel pipe having the applied elastomeric coating layer satisfies the standard for use in the water supply industry as set forth in AWWA C222.

First claim

What is claimed is:

1. A system for forming an elastomeric composition for application to a substrate, the system comprising:
an isocyanate component comprising a polymeric polyisocyanate, said isocyanate component comprising from 35.5 to 40 weight percent of the total weight of said system; and
an isocyanate-reactive component comprising a polyol component and a polyetheramine, said polyol component comprising a mixture of:
(a) a hydrophobic polyol;
(b) a polyether polyol different than said hydrophobic polyol, said polyether polyol having a weight average molecular weight greater than 500 g/mol; and
(c) a polyaminopolyol.

2. The system according to claim 1 , wherein said polymeric polyisocyanate comprises polymeric diphenylmethane diisocyanate.

3. The system according to claim 1 , wherein said isocyanate component further comprises an isocyanate-terminated prepolymer present in said isocyanate component in an amount from about 25 to about 75 parts based on 100 parts by weight of said isocyanate component.

4. The system according to claim 1 , wherein said hydrophobic polyol comprises a natural oil polyol.

5. The system according to claim 4 , wherein the natural oil polyol comprises castor oil.

6. The system according to claim 1 , wherein said polyether polyol has a weight average molecular weight of from 500 to 650 g/mol.

7. The system according to claim 6 , wherein said polyether polyol is derived from the catalyzed addition reaction of propylene oxide in the absence of ethylene oxide.

8. The system according to claim 6 , wherein said polyether polyol has an average functionality of from 3.5 to 4.0.

9. The system according to claim 6 , wherein said polyether polyol comprises from 1.8 to 5 weight percent of the total weight of said system.

10. The system according to claim 1 , wherein said isocyanate-reactive component further comprises polytetramethylene ether glycol obtained by the polymerization of tetrahydrofuran.

11. The system according to claim 10 , wherein said polytetramethylene ether glycol comprises from 4 to 10 weight percent of the total weight of said system.

12. The system according to claim 1 , wherein said isocyanate-reactive component further comprises polytetramethylene ether glycol obtained by the polymerization of tetrahydrofuran and having a weight average molecular weight of from 650 to 2000 g/mol.

13. The system according to claim 1 , wherein said polyaminopolyol comprises ethylene diamine and propylene oxide based polyether polyol tetrol.

14. The system according to claim 1 , wherein said polyaminopolyol comprises from 4 to 10 weight percent of the total weight of said system.

15. The system according to claim 1 , wherein said polyetheramine comprises from 4 to 10 weight percent of the total weight of said system.

16. The system according to claim 1 comprising, based on 100 parts by weight of said system:
35.5 to 40 parts by weight of said isocyanate component;
25 to 37 parts by weight of castor oil as said hydrophobic polyol;
1.8 to 5 parts by weight of a polyether polyol derived from the catalyzed addition reaction of propylene oxide, said polyether polyol having a weight average molecular weight of from 500 to 650 and an average functionality from 3.5 to 4.0; and
4 to 10 parts by weight of polytetramethylene ether glycol obtained by the polymerization of tetrahydrofuran and having a weight average molecular weight of from 650 to 2000 g/mol;
4 to 10 parts by weight of said polyaminopolyol; and
4 to 10 parts by weight of said polyetheramine.

17. The system according to claim 1 , wherein the molar ratio of NCO groups in said isocyanate component to active hydrogens in said isocyanate-reactive component is from 1:1 to 1.10:1.

18. An elastomeric composition obtained by reacting said isocyanate component with said isocyanate-reactive component of said system according to claim 1 .

19. An article comprising a substrate and an elastomeric coating layer adhered thereon, said elastomeric coating layer comprising an elastomeric composition according to claim 18 .

20. The article according to claim 19 , wherein said substrate comprises a metal pipe having an exterior surface and an interior surface, and wherein said elastomeric coating composition is applied to at least one of said exterior surface and said interior surface to form an elastomeric coating layer adhered thereon, and wherein said steel pipe having said applied elastomeric coating layer satisfies the standard for use in the water supply industry as set forth in AWWA C222.

21. A process of coating a substrate comprising applying a layer of said elastomeric composition according to claim 18 onto a surface of the substrate to form an elastomeric coating layer.

22. A process of forming an elastomeric composition comprising:
mixing together said isocyanate component with said isocyanate-reactive component of said system according to claim 1 ; and
reacting said isocyanate component with said isocyanate-reactive component to form the elastomeric composition.

23. A system for forming an elastomeric composition for application to a substrate, the system comprising based on 100 parts by weight of said system:
35.5 to 40 parts by weight of an isocyanate component comprising a polymeric polyisocyanate; and
an isocyanate-reactive component comprising a polyol component and 4 to 10 parts by weight of a polyetheramine based on 100 parts by weight of said isocyanate-reactive component, said polyol component comprising a mixture of:
(a) 25 to 37 parts by weight of a hydrophobic polyol which is castor oil;
(b) 1.8 to 5 parts by weight of a polyether polyol derived from a catalyzed addition reaction of propylene oxide, said polyether polyol having a weight average molecular weight of from 500 to 650 and an average functionality of from 3.5 to 4.0;
(c) 4 to 10 parts by weight of a polyaminopolyol; and
(d) 4 to 10 parts by weight of polytetramethylene ether glycol obtained by the polymerization of tetrahydrofuran and having a weight average molecular weight of from 650 to 2000 g/mol.

24. A system for forming an elastomeric composition for application to a substrate, the system comprising:
an isocyanate component comprising a polymeric polyisocyanate and an isocyanate-terminated prepolymer wherein said isocyanate-terminated prepolymer is present in said isocyanate component in an amount of from about 25 to about 75 parts by weight based on 100 parts by weight of said isocyanate component; and
an isocyanate-reactive component comprising a polyol component and a polyetheramine, said polyol component comprising a mixture of:
(a) a hydrophobic polyol;
(b) a polyether polyol different that said hydrophobic polyol, said polyether polyol having a weight average molecular weight of greater than 500 g/mol; and
(c) a polyaminopolyol.

25. A system for forming an elastomeric composition for application to a substrate, the system comprising:
an isocyanate component comprising a polymeric polyisocyanate; and
an isocyanate-reactive component comprising a polyol component and a polyetheramine, said polyol component comprising a mixture of:
(a) a hydrophobic polyol;
(b) a polyether polyol different than said hydrophobic polyol, said polyether polyol having a weight average molecular weight of greater than 500 g/mol;
(c) a polyaminopolyol; and
(d) a polytetramethylene ether glycol obtained by the polymerization of tetrahydrofuran, said p

Assignees

• Basf Se

Inventors

• Caillouette Lyle
• Phelps David R
• Smith Stephen
• Gust Karl

Classifications

• C09D175/04

  Polyurethanes · CPC title

• C08G18/7671 Primary

  containing only one alkylene bisphenyl group · CPC title

• C08G18/66

  Compounds of groups C08G18/42, C08G18/48, or C08G18/52 · CPC title

• C08G18/482

  Mixtures of polyethers containing at least one polyether containing nitrogen · CPC title

• C08G18/4816

  mixtures of two or more polyetherpolyols having at least three hydroxy groups · CPC title