Method for producing granular polyarylene sulfide, method for increasing average particle size of granular polyarylene sulfide, method for enhancing particle strength of granular polyarylene sulfide, and granular polyarylene sulfide

Patent metadata

Field	Value
Publication number	US-10731005-B2
Application number	US-201716074915-A
Country	US
Kind code	B2
Filing date	Mar 24, 2017
Priority date	Mar 31, 2016
Publication date	Aug 4, 2020
Grant date	Aug 4, 2020

Abstract

The present invention provides a method for producing granular polyarylene sulfide (PAS) with increased average particle size and enhanced particle strength, a method for increasing the average particle size of granular PAS, a method for enhancing the particle strength of granular PAS, and granular PAS. The method for producing PAS according to the present invention includes: step 1: a preparation step of preparing a mixture containing an organic amide solvent, a sulfur source, water, a dihalo aromatic compound, and an alkali metal hydroxide; step 2: a pre-stage polymerization step of initiating a polymerization reaction by heating the mixture to produce a prepolymer having a dihalo aromatic compound conversion ratio of not less than 50% in the presence of less than an equimolar amount of an alkali metal hydroxide per 1 mol of the sulfur source; step 3: a post-stage polymerization step of continuing the polymerization reaction in the presence of not less than an equimolar amount of an alkali metal hydroxide per 1 mol of the sulfur source to obtain a reaction product mixture; and step 4: a cooling step of cooling the reaction product mixture after the post-stage polymerization step; wherein step 4 is performed in the presence of at least one type of auxiliary agent such as a carboxylate.

First claim

The invention claimed is:

1. A method for producing granular polyarylene sulfide by polymerizing a sulfur source and a dihalo aromatic compound in an organic amide solvent, the method comprising:
step 1: a preparation step of preparing a mixture containing an organic amide solvent, a sulfur source, water, a dihalo aromatic compound, and an alkali metal hydroxide;
step 2: a pre-stage polymerization step of initiating a polymerization reaction by heating the mixture to produce a prepolymer having a dihalo aromatic compound conversion ratio of not less than 50% in the presence of less than an equimolar amount of an alkali metal hydroxide per 1 mol of the sulfur source;
step 3: a post-stage polymerization step of continuing the polymerization reaction in the presence of not less than an equimolar amount of an alkali metal hydroxide per 1 mol of the sulfur source to obtain a reaction product mixture; and
step 4: a cooling step of cooling the reaction product mixture after the post-stage polymerization step;
wherein step 4 is performed in the presence of at least one type of auxiliary agent selected from the group consisting of carboxylates, alkali metal chlorides, organic sulfonates, alkali metal sulfates, alkali earth metal oxides, alkali metal phosphates, and alkali earth metal phosphates;
wherein an amount of the auxiliary agent is from 0.1 to 5 mol % per 1 mol of the sulfur source; and
wherein step 3 is performed in the presence of from 4.1 to 14 mol of water per 1 kg of the organic amide solvent.

2. The method according to claim 1 , wherein the auxiliary agent is a carboxylate.

3. A method for increasing an average particle size of granular polyarylene sulfide, the method comprising:
step 1: a preparation step of preparing a mixture containing an organic amide solvent, a sulfur source, water, a dihalo aromatic compound, and an alkali metal hydroxide;
step 2: a pre-stage polymerization step of initiating a polymerization reaction by heating the mixture to produce a prepolymer having a dihalo aromatic compound conversion ratio of not less than 50% in the presence of less than an equimolar amount of an alkali metal hydroxide per 1 mol of the sulfur source;
step 3: a post-stage polymerization step of continuing the polymerization reaction in the presence of not less than an equimolar amount of an alkali metal hydroxide per 1 mol of the sulfur source to obtain a reaction product mixture; and
step 4: a cooling step of cooling the reaction product mixture after the post-stage polymerization step;
wherein step 4 is performed in the presence of at least one type of auxiliary agent selected from the group consisting of carboxylates, alkali metal chlorides, organic sulfonates, alkali metal sulfates, alkali earth metal oxides, alkali metal phosphates, and alkali earth metal phosphates;
wherein an amount of the auxiliary agent is from 0.1 to 5 mol % per 1 mol of the sulfur source, and
wherein step 3 is performed in the presence of from 4.1 to 14 mol of water per 1 kg of the organic amide solvent.

4. A method for enhancing a particle strength of granular polyarylene sulfide, the method comprising:
step 1: a preparation step of preparing a mixture containing an organic amide solvent, a sulfur source, water, a dihalo aromatic compound, and an alkali metal hydroxide;
step 2: a pre-stage polymerization step of initiating a polymerization reaction by heating the mixture to produce a prepolymer having a dihalo aromatic compound conversion ratio of not less than 50% in the presence of less than an equimolar amount of an alkali metal hydroxide per 1 mol of the sulfur source;
step 3: a post-stage polymerization step of continuing the polymerization reaction in the presence of not less than an equimolar amount of an alkali metal hydroxide per 1 mol of the sulfur source to obtain a reaction product mixture; and
step 4: a cooling step of cooling the reaction product mixture after the post-stage polymerization step;
wherein step 4 is performed in the presence of at least one type of auxiliary agent selected from the group consisting of carboxylates, alkali metal chlorides, organic sulfonates, alkali metal sulfates, alkali earth metal oxides, alkali metal phosphates, and alkali earth metal phosphates;
an amount of the auxiliary agent is from 0.1 to 5 mol % per 1 mol of the sulfur source, and step 3 is performed in the presence of from 4.1 to 14 mol of water per 1 kg of the organic amide solvent.

5. The method according to claim 1 , wherein the average particle size of the granular polyarylene sulfide is not less than 300 μm.

6. The method according to claim 1 , wherein the particle strength of the granular polyarylene sulfide is not less than 92%.

7. The method according to claim 1 , wherein a melt viscosity of the granular polyarylene sulfide measured at a temperature of 310° C. and a shear rate of 1216 sec −1 is not greater than 50 Pa·s.

Assignees

• Kureha Corp

Inventors

• Konno Akihiro
• Sato Hiroyuki

Classifications

• C08G75/0259 Primary

  metal hydrogensulfides · CPC title

• C08G75/0254

  using metal sulfides · CPC title

• C08G75/0209 Primary

  derived from monomers containing one aromatic ring · CPC title

• C08G75/0263

  using elemental sulfur · CPC title

• C08G75/0277

  Post-polymerisation treatment (chemical after-treatment C08G75/0286) · CPC title