Method of manufacturing rolling bearing ring

Patent metadata

Field	Value
Publication number	US-10730098-B2
Application number	US-201615758223-A
Country	US
Kind code	B2
Filing date	Aug 23, 2016
Priority date	Sep 8, 2015
Publication date	Aug 4, 2020
Grant date	Aug 4, 2020

Abstract

A first step of setting a steel material heated to a temperature not lower than an A1 transformation point on a forming table and a second step of punching a ring-form member from the steel material and thereafter forming and quenching the ring-form member on the forming table are included. A press die is constructed to be dividable into an inner cylinder and an outer cylinder. In the second step, the ring-form member is punched from a coil material by pressing a tip end portion of the inner cylinder and a tip end portion of the outer cylinder against the coil material. The punched ring-form member is formed and quenched by further pressing a tip end of the inner cylinder against the ring-form member while the ring-form member is held between the outer cylinder and a forming die.

First claim

The invention claimed is:

1. A method of manufacturing a rolling bearing ring comprising:
a first step of setting a steel material heated to a temperature not lower than an A 1 transformation point on a forming table; and
a second step of punching a ring-form member from the steel material and thereafter forming and quenching the ring-form member on the forming table,
the forming table including a first die and a second die,
the second die being constructed to have an inner cylinder and an outer cylinder movable relative to each other, wherein
in the second step, the ring-form member is punched from the steel material by arranging the steel material between the first die and the second die and pressing a tip end portion of the inner cylinder and a tip end portion of the outer cylinder against the steel material, and
the ring-form member is formed and quenched by further pressing a tip end of either cylinder against the punched ring-form member while the punched ring-form member is held between the other cylinder and the first die such that one cylinder moves relative to the other cylinder.

2. The method of manufacturing a rolling bearing ring according to claim 1 , wherein
in the second step, punching is performed in a first stage and drawing as forming is performed together with quenching in a second stage.

3. The method of manufacturing a rolling bearing ring according to claim 2 , wherein
in the second step, a time period from start of the punching of the ring-form member until completion of the forming is within 0.1 second.

4. The method of manufacturing a rolling bearing ring according to claim 1 , wherein
holding force with which the ring-form member is held between any one of the inner cylinder and the outer cylinder and the first die in the second step is not lower than 0.2 MPa.

5. The method of manufacturing a rolling bearing ring according to claim 1 , wherein
the steel material contains at least 0.4 mass % of carbon and has a thickness not greater than 2 mm, and a ring form is punched from the steel material in a direction of thickness.

6. The method of manufacturing a rolling bearing ring according to claim 1 , wherein
the manufactured rolling bearing ring has a hardness not lower than 700 HV.

Assignees

• Ntn Toyo Bearing Co Ltd

Inventors

• Mizuta Kohei
• Ohki Chikara

Classifications

• F16C19/46

  with one row or needles · CPC title

• B21D28/14

  Dies (ejecting or stripping-off devices arranged in punching machines or tools B21D45/00) · CPC title

• C21D9/40

  for rings; for bearing races · CPC title

• B21D25/00

  Working sheet metal of limited length by stretching, e.g. for straightening · CPC title

• B21D28/02

  Punching blanks or articles with or without obtaining scrap (cutting nails or pins from strips or sheet material B21G3/26); Notching · CPC title