Ambient cure, fast dry automotive refinish primer surfacer compositions and methods of use

Patent metadata

Field	Value
Publication number	US-10723889-B2
Application number	US-201514721438-A
Country	US
Kind code	B2
Filing date	May 26, 2015
Priority date	May 29, 2014
Publication date	Jul 28, 2020
Grant date	Jul 28, 2020

Abstract

The present invention provides substantially isocyanate-free multicomponent compositions useful in making rapid dry automotive primer compositions and coatings, the compositions having a % PVC of from 20 to 60, or preferably, from 25 to 50, and comprising one or more pigment, extender or filler, one or more a) polycarbamates from alkyd polyol or acrylic polyol and one or more b) a polyaldehydes or the acetal or hemiacetal thereof as a second component. The multicomponent compositions cure quickly at a temperature of from 0° C. to less than 80° C. to form a crosslinked polyurethane which dries to enable sanding after only 15 to 45 minutes.

First claim

We claim:

1. A substantially isocyanate free, ambient temperature curable, multicomponent, sandable, automotive primer composition having a pigment volume concentration (% PVC) of from 20 to 60 comprising:
one or more pigments, extenders and/or fillers,
one or more a) polycarbamates of an alkyd polyol, an acrylic polyol, or their mixtures, and
one or more b) polyaldehydes or acetals or hemiacetals thereof in a component separate from the one or more polycarbamates,
wherein the composition has from 0 to 5 mole percent (mol %) of isocyanate groups, based on total moles of carbamate groups plus isocyanate groups in the composition; and
wherein the composition has a dry to sand time of less than or equal to 60 minutes when cured at a temperature of from ambient to 30° C., according to ASTM D-5895 (2013).

2. The multicomponent composition as claimed in claim 1 , wherein the composition further comprises one or more acid catalyst or metal drier.

3. The multicomponent composition as claimed in claim 1 , wherein the one or more a) polycarbamates is a polycarbamate of an alkyd polyol and the alkyd polyol has a hydroxyl number of from 50 to 250.

4. The multicomponent composition as claimed in claim 3 , wherein the alkyd polyol is a short or medium oil alkyd polyol.

5. The multicomponent composition as claimed in claim 1 , wherein the alkyd polyol is the reaction product of one or more monocarboxylic acid oil, one or more polycarboxylic acid having two or more carboxylic acid, salt or halide groups, and one or more polyalcohol having three or more hydroxyl groups.

6. The multicomponent composition as claimed in claim 1 , wherein the one or more a) polycarbamates is a polycarbamate of an acrylic polyol and the acrylic polyol has a hydroxyl number of from 50 to 250.

7. The multicomponent composition as claimed in claim 1 , wherein the one or more a) polycarbamates has an average of 2 or more carbamate groups.

8. The multicomponent composition as claimed in claim 1 , wherein the composition comprises one or more pigment and one or more extender.

9. The multicomponent composition as claimed in claim 1 , wherein the composition has a % PVC of from 25 to 50.

10. The multicomponent composition as claimed in claim 1 , wherein the composition comprises, based on total polycarbamate and polyaldehyde solids,
20 to 90 wt. % of the one or more a) polycarbamates, and
10 to 80 wt. % of the one or more b) polyaldehydes or acetals or hemiacetals thereof.

11. A method for using the composition as claimed in claim 1 , comprising applying the composition to an automotive substrate, to form a primer coating layer, curing the primer coating layer to form a crosslinked polyurethane at a temperature of from ambient to 80° C., for a period long enough to enable sanding of the coating layer, and sanding the primer coating layer to form a smooth primer coating layer.

12. An automotive finish comprising:
an automotive substrate;
one or more crosslinked polyurethane smooth primer coating layers disposed on the automotive substrate, obtained by applying the automotive primer composition of claim 1 to at least a portion of a surface of the automotive substrate and curing the automotive primer composition;
a cured pigmented basecoat or colorcoat layer disposed on the one or more smooth primer coating layers;
and a cured clearcoat layer disposed on the cured pigmented basecoat or colorcoat layer.

Assignees

• Dow Global Technologies Llc

Inventors

• Anderson Jeff R
• Argyropoulos John N
• Kamber Nahrain E
• Ortiz Rebecca S
• Rainey Christopher D
• Spilman Gary E

Classifications

• B05D3/007

  After-treatment · CPC title

• C08G71/04

  Polyurethanes · CPC title

• C09D175/12

  from compounds containing nitrogen and active hydrogen, the nitrogen atom not being part of an isocyanate group · CPC title

• C09D7/61 Primary

  inorganic · CPC title

• C09D175/16

  having terminal carbon-to-carbon unsaturated bonds · CPC title