Method for producing a tube skirt decorated with an aesthetic lateral weld

Patent metadata

Field	Value
Publication number	US-10723084-B2
Application number	US-201615578223-A
Country	US
Kind code	B2
Filing date	May 26, 2016
Priority date	May 29, 2015
Publication date	Jul 28, 2020
Grant date	Jul 28, 2020

Abstract

A method for producing a tube skirt for a flexible tube, said tube skirt being manufactured from a flat strip 1 comprising a decorative film 15 superimposed on a primary film 16 , said primary film 16 comprising a sealable inner layer 14 at the lower surface 20 of the strip 1 as well as two stabilizing layers 11, 13 , said decorative film 15 comprising a sealable outer layer 7 at the upper surface 19 of the strip 1 , and a decorative layer 8, 9.
This method comprises the following steps:
winding the flat strip 1 into the form of a sleeve to shape the tube skirt; superimposing a first side border 2 of the strip 1 on a second side border 2 ′ of the strip 1 to form an overlapping area 3 , the sealable inner layer 14 of the primary film 16 of the first side border 2 overlapping the sealable outer layer 7 ′ of the decorative film 15 ′ of the second side border 2′; applying a heating temperature T 2 to the inside of the tube skirt at the inner face 22 of the overlapping area 3 to produce the side weld of the tube skirt; simultaneously with the application of the heating temperature T 2 , applying compression between the outer 21 and inner 22 faces of the overlapping area 3 so as to finalize the side weld of the tube skirt.

First claim

The invention claimed is:

1. A method for producing a tube skirt for a flexible tube, said tube skirt being manufactured from a flat strip comprising a decorative film superimposed on a primary film, said primary film comprising a sealable inner layer at the lower surface of the strip as well as two stabilizing layers which import rigidity to a seam area and act as a reinforcement, said decorative film comprising a sealable outer layer at the upper surface of the strip, and a decorative layer, said method comprising:
winding the flat strip into a form of a sleeve to shape the tube skirt;
superimposing a first side border of the strip on a second side border 2 ′ of the strip to form an overlapping area, the sealable inner layer of the primary film of the first side border overlapping the sealable outer layer 7 ′ of the decorative film 15 ′ of the second side border 2 ′;
applying a heating temperature to the inside of the tube skirt at the inner face of the overlapping area to produce the side weld of the tube skirt;
simultaneously with the application of the heating temperature, applying compression between the outer and inner faces of the overlapping area so as to finalize the side weld of the tube skirt, wherein a different heating temperature is applied, simultaneously with the heating temperature applied to the inside of the tube skirt, on the outer face of the overlapping area, the different heating temperature being lower than the heating temperature applied to the inside of the tube skirt.

2. The method according to claim 1 , wherein the heating temperature is higher than a melting temperature of the sealable inner layer of the primary film and the sealable outer layer of the decorative film, and lower than a melting temperature of the decorative layer of the decorative film and the two stabilizing layers of the primary film.

3. The method according to claim 1 , wherein the different heating temperature is lower than a melting temperature of material making up the sealable outer layer.

4. The method according to claim 3 , wherein the material making up the sealable outer layer comprises polyethylene, and wherein the melting temperature of the material is above 120° C., and the different heating temperature is lower than 120° C.

5. The method according to claim 4 , wherein the different heating temperature is less than 100° C.

6. The method according to claim 1 , further comprising preheating the overlapping area before superimposing the side borders.

7. The method according to claim 6 , wherein the preheating comprises blowing hot air into an interstitial space separating the first side border from the second side border 2 ′ before the superimposition of the first side border on the second side border.

8. The method according to claim 1 , further comprising cooling the overlapping area after the application of the compression.

9. The method according to claim 8 , wherein the cooling comprises cooling the inner face of the overlapping area.

10. The method according to claim 1 , wherein the overlapping area has a width between 1.5 and 2.5 mm.

Assignees

• Albea Services

Inventors

• Hintz Martin
• Suvarna Sudheer

Classifications

• B29C66/3474

  perpendicular to the plane of the joint · CPC title

• B29C66/83421

  band or belt types (B29C66/83431 takes precedence) · CPC title

• B29C66/723

  being multi-layered (B29C66/7292, B29C66/72941 take precedence) · CPC title

• B29C66/919

  characterised by specific temperature, heat or thermal flux values or ranges (specific electrical resistance values B29C66/81262) · CPC title

• B29L2023/20

  Flexible squeeze tubes, e.g. for cosmetics · CPC title