Hollow fiber membrane for dehydration of organic solvents via pervaporation process and a method of fabricating the same

Patent metadata

Field	Value
Publication number	US-10722850-B2
Application number	US-201414203185-A
Country	US
Kind code	B2
Filing date	Mar 10, 2014
Priority date	Mar 12, 2013
Publication date	Jul 28, 2020
Grant date	Jul 28, 2020

Abstract

Disclosed is a hollow fiber that contains an outer layer made of a first polymer and an inner layer made of a second polymer, the inner layer including at its outer surface a macrovoid-free thin interface sublayer in contact with the inner surface of the outer layer. The first polymer is immiscible with the second polymer. Also disclosed is a process of preparing the above-described hollow fiber.

First claim

What is claimed is:

1. A process for preparing a hollow fiber membrane configured to effect pervaporative dehydration of an organic solvent, the process comprising:
dissolving a first polymer in a first solvent to prepare a first spinning dope;
dissolving a second polymer in a second solvent to prepare a second spinning dope, the first polymer being immiscible with the second polymer;
mixing 10-99 wt % N-methyl-2-pyrrolidone (NMP) in a third solvent to prepare a bore fluid;
providing a triple orifice spinneret that has an external orifice, a middle orifice, and an internal orifice; and
co-extruding the first spinning dope at a flow rate of 0.01 to 10 ml/min and the second spinning dope at a flow rate of 0.01 to 20 ml/min respectively through the external orifice and the middle orifice via a dry-jet wet-spinning process into a coagulation bath and at the same time passing the bore fluid at a flow rate of 0.01 to 20 ml/min through the internal orifice, to form a hollow fiber having an inner layer and an outer layer, wherein the inner layer is a selective layer formed of the second spinning dope, the outer layer is a protective layer formed of the first spinning dope, and the inner layer includes an interface sublayer at its outer surface, in which the interface sublayer, being free of macrovoids and the first polymer, is in contact with the inner surface of the outer layer without delamination, wherein the first polymer is cellulose triacetate and the second polymer is polyether-imide.

2. The process of claim 1 , wherein the first polymer is polyimide, polyamide-imide, polyether-imide, cellulose acetate, cellulose diacetate, cellulose triacetate, polyamides, polysulfone, polyethersulfone, polyphenylsulfone, polyacrylonitrile, polyvinylidene fluoride, polycarbonate, polybenzimidazole, polyvinyl alcohol, alginates, chitosan, or polyvinylpyridine.

3. The process of claim 2 , wherein the first polymer is polyvinylidene fluoride, polyimide, or cellulose triacetate.

4. The process of claim 1 , wherein the second polymer is polyimide, co-polyimide, polyamide-imide, polyether-imide, cellulose acetate, cellulose diacetate, cellulose triacetate, polyamides, polysulfone, polyethersulfone, polyphenylsulfone, polyacrylonitrile, polyvinylidene fluoride, polycarbonate, polybenzimidazole, polyvinyl alcohol, alginates, chitosan, or polyvinylpyridine.

5. The process of claim 2 , wherein the second polymer is polyimide, co-polyimide, polyamide-imide, polyether-imide, cellulose acetate, cellulose diacetate, cellulose triacetate, polyamides, polysulfone, polyethersulfone, polyphenylsulfone, polyacrylonitrile, polyvinylidene fluoride, polycarbonate, polybenzimidazole, polyvinyl alcohol, alginates, chitosan, or polyvinylpyridine.

6. The process of claim 4 , wherein the second polymer is polyether-imide, polysulfone, or co-polyimide.

7. The process of claim 3 , wherein the second polymer is polyether-imide, polysulfone, or co-polyimide.

8. The process of claim 1 , wherein the first solvent is NMP, tetrahydrofuran, methanol, dimethylacetamide, dioxane, dichloromethane, dimethylformamide, dimethyl sulfoxide, acetone, ethanol, propanol, butanol, glycols, or water; the second solvent is NMP, tetrahydrofuran, methanol, dimethylacetamide, dioxane, dichloromethane, dimethylformamide, dimethyl sulfoxide, acetone, ethanol, propanol, butanol, glycols, or water; and the third solvent is water, n-hexane, kerosene, dimethylacetamide, dioxane, dichloromethane, dimethylformamide, dimethyl sulfoxide, acetone, ethanol, propanol, butanol, or glycol.

9. The process of claim 1 , wherein the first polymer has a critical concentration lower than that of the second polymer.

10. The process of claim 1 , wherein there is an air gap of up to 100 cm between the coagulation bath and the spinneret during the co-extruding step.

11. The process of claim 1 , wherein the co-extruding step is performed at 10° C. to 70° C. and the coagulation bath is kept at 5° C. to 70° C.

12. The process of claim 8 , wherein there is an air gap of up to 100 cm between the coagulation bath and the spinneret during the co-extruding step, the co-extruding step is performed at 10° C. to 70° C., and the coagulation bath is kept at 5° C. to 70° C.

13. The process of claim 1 , wherein the first solvent is NMP, the second solvent is NMP, the third solvent is water, the first spinning dope has a flow rate of 0.2 ml/min, the second spinning dope has a flow rate of 1.5 ml/min, the bore fluid has a flow rate of 1 ml/min, there is an air gap of 1.5 cm between the coagulation bath and the spinneret during the co-extruding step, the co-extruding step is performed at 25° C., and the coagulation bath is kept at 25° C.

14. A hollow fiber membrane prepared according to claim 1 , the hollow fiber membrane comprising:
an outer layer formed of the first polymer, and
an inner layer formed of the second polymer, the outer surface of which is in contact with the inner surface of the outer layer,

wherein the inner layer is a selective layer, the outer layer is a protective layer, the inner layer includes an interface sublayer at its outer surface, in which the interface sublayer being free of macrovoids and the first polymer, is in contact with the inner surface of the outer layer, and the first polymer is immiscible with the second polymer.

15. The hollow fiber membrane of claim 14 , wherein the first polymer is polyimide, polyamide-imide, polyether-imide, cellulose acetate, cellulose diacetate, cellulose triacetate, polyamides, polysulfone, polyethersulfone, polyphenylsulfone, polyacrylonitrile, polyvinylidene fluoride, polycarbonate, polybenzimidazole, polyvinyl alcohol, alginates, chitosan, or polyvinylpyridine.

16. The hollow fiber membrane of claim 15 , wherein the first polymer is polyvinylidene fluoride, polyimide, or cellulose triacetate.

17. The hollow fiber membrane of claim 14 , wherein the second polymer is polyimide, co-polyimide, polyamide-imide, polyether-imide, cellulose acetate, cellulose diacetate, cellulose triacetate, polyamides, polysulfone, polyethersulfone, polyphenylsulfone, polyacrylonitrile, polyvinylidene fluoride, polycarbonate, polybenzimidazole, polyvinyl alcohol, alginates, chitosan, or polyvinylpyridine.

18. The hollow fiber membrane of claim 15 , wherein the second polymer is polyimide, co-polyimide, polyamide-imide, polyether-imide, cellulose acetate, cellulose diacetate, cellulose triacetate, polyamides, polysulfone, polyethersulfone, polyphenylsulfone, polyacrylonitrile, polyvinylidene fluoride, polycarbonate, polybenzimidazole, polyvinyl alcohol, alginates, chitosan, or polyvinylpyridine.

19. The hollow fiber membrane of claim 17 , wherein the second polymer is polyether-imide, polysulfone, or co-polyimide.

20. The hollow fiber membrane of claim 16 , wherein the second polymer is polyether-imide, polysulfone, or co-polyimide.

Assignees

• Nat Univ Singapore

Inventors

• Ong Yee Kang
• Chung Tai-Shung

Classifications

• B01D71/641

  Polyamide-imides · CPC title

• B01D71/643

  Polyether-imides · CPC title

• B01D71/5211

  Polyethylene glycol or polyethyleneoxide · CPC title

• B01D61/362

  Pervaporation · CPC title

• B01D71/68 Primary

  Polysulfones; Polyethersulfones · CPC title