Coated tool

Patent metadata

Field	Value
Publication number	US-10717135-B2
Application number	US-201716079581-A
Country	US
Kind code	B2
Filing date	Feb 24, 2017
Priority date	Feb 24, 2016
Publication date	Jul 21, 2020
Grant date	Jul 21, 2020

Abstract

A coated tool may include a substrate and a coating layer located on a surface of the substrate. The coating layer includes: a first titanium carbonitride layer located on the substrate; a second titanium carbonitride layer located on the first titanium carbonitride layer; and an aluminum oxide layer located on the second titanium carbonitride layer. The first titanium carbonitride layer includes a plurality of first protrusions protruding toward a side of the aluminum oxide layer. The second titanium carbonitride layer includes a plurality of second protrusions protruding toward a side of the aluminum oxide layer. A number of second protrusions is greater than that of the first protrusions.

First claim

The invention claimed is:

1. A coated tool, comprising:
a substrate; and
a coating layer located on a surface of the substrate,
wherein the coating layer comprises:
a first titanium carbonitride layer located on the substrate;
a second titanium carbonitride layer located on the first titanium carbonitride layer; and
an aluminum oxide layer located on the second titanium carbonitride layer,

wherein the first titanium carbonitride layer comprises a plurality of first protrusions protruding toward a side of the aluminum oxide layer,
wherein the second titanium carbonitride layer comprises a plurality of second protrusions protruding toward a side of the aluminum oxide layer, and
wherein a number of the second protrusions is greater than a number of the first protrusions.

2. The coated tool according to claim 1 ,
wherein a tip angle of the second protrusion is smaller than a tip angle of the first protrusion in a cross section orthogonal to the surface of the substrate.

3. The coated tool according to claim 1 ,
wherein the first titanium carbonitride layer comprises a gap in valleys located between adjacent first protrusions, and
wherein the second protrusion is located right above the gap.

4. The coated tool according to claim 3 ,
wherein the first titanium carbonitride layer comprises a plurality of the gaps, and an average area of the gaps corresponds to an area of a circle having a diameter of 32 to 100 nm in a cross section orthogonal to the surface of the substrate.

5. The coated tool according to claim 1 , to
wherein when a ratio of a content of carbon to a total content of carbon and nitrogen in the first titanium carbonitride layer is defined as a first ratio, and a ratio of a content of carbon to a total content of carbon and nitrogen in the second titanium carbonitride layer is defined as a second ratio, the second ratio is smaller than the first ratio.

6. The coated tool according to claim 5 ,
wherein the first ratio is from 0.3 to 0.57 and the second ratio is from 0.27 to 0.51.

7. The coated tool according to claim 5 ,
wherein the content of carbon in the first titanium carbonitride layer is from 15 to 29 atomic percent, and the content of nitrogen in the first titanium carbonitride layer is from 22 to 35 atomic percent, and
wherein the content of carbon in the second titanium carbonitride layer is from 13 to 24 atomic percent, and the content of nitrogen in the second titanium carbonitride layer is from 23 to 35 atomic percent.

8. The coated tool according to claim 1 ,
wherein the first titanium carbonitride layer comprises columnar crystals of carbonitride titanium nitride comprising an average aspect ratio of 2 or more.

9. The coated tool according to claim 1 ,
wherein the first titanium carbonitride layer comprises a thickness of 2 to 15 μm.

10. The coated tool according to claim 1 ,
wherein the second titanium carbonitride layer comprises a thickness of 30 to 900 nm.

11. The coated tool according to claim 1 ,
wherein the coating layer further comprises an intermediate layer located between the first titanium carbonitride layer and the second titanium carbonitride layer, and
wherein the intermediate layer comprises 30 to 70 atomic percent of titanium, 24 to 30 atomic percent of carbon, 16 to 23 atomic percent of nitrogen and 2 to 5 atomic percent of oxygen.

12. The coated tool according to claim 1 ,
wherein the coating layer further comprises an intermediate layer located between the second titanium carbonitride layer and the aluminum oxide layer, and
wherein the intermediate layer comprises 30 to 70 atomic percent of titanium, 0 to 70 atomic percent of carbon, 0 to 35 atomic percent of nitrogen and 3 to 20 atomic percent of oxygen.

13. The coated tool according to claim 12 ,
wherein the intermediate layer comprises a needle-like crystal projecting toward the aluminum oxide layer.

14. The coated tool according to claim 13 ,
wherein a thickness of a part of the intermediate layer excluding the needle-like crystal is 10 to 40 nm.

15. The coated tool according to claim 1 ,
wherein in the first titanium carbonitride layer comprises oxygen.

16. The coated tool according to claim 15 ,
wherein in the second titanium carbonitride layer further comprises oxygen, and
wherein an oxygen content present in the second titanium carbonitride layer is greater than an oxygen content present in the first titanium carbonitride layer.

Assignees

• Kyocera Corp

Inventors

• Kubo Hayato
• Kodama Yoshikazu
• Itoh Hirotoshi

Classifications

• C23C30/005

  on hard metal substrates · CPC title

• C23C28/044

  coatings specially adapted for cutting tools or wear applications · CPC title

• C23C28/042 Primary

  including a refractory ceramic layer, e.g. refractory metal oxides, ZrO2, rare earth oxides · CPC title

• C23C28/04

  only coatings of inorganic non-metallic material · CPC title

• C23C16/36 Primary

  Carbonitrides · CPC title