Thermoplastic prepreg intermediate material for fuel cell separation plate and method for manufacturing thermoplastic prepreg for fuel cell separation plate by using same

Patent metadata

Field	Value
Publication number	US-10703873-B2
Application number	US-201515512605-A
Country	US
Kind code	B2
Filing date	Sep 23, 2015
Priority date	Sep 29, 2014
Publication date	Jul 7, 2020
Grant date	Jul 7, 2020

Abstract

An intermediate material of a thermoplastic prepreg for a fuel cell separation plate comprises a hydrophobic thermoplastic resin film and a fiber base. The hydrophobic thermoplastic resin film has a degree of crystallization of 1 to 20%, a thickness of 3 to 50 μm, and (iii) a content of an electroconductive material of 1 to 20 wt. %. The film is laminated on at least one surface of the fiber base. The thermoplastic prepreg for a fuel cell separation plate is manufactured by pressurizing the thermoplastic prepreg intermediate material at a temperature higher than the melting point of the hydrophobic thermoplastic resin film. A fuel cell separation membrane manufactured using the thermoplastic prepreg intermediate material and thermoplastic prepreg is thin and light-weight, and have a good durability.

First claim

The invention claimed is:

1. A thermoplastic prepreg intermediate material for a fuel cell separation plate, consisting of
a fiber base; and
a hydrophobic thermoplastic resin film, of which (i) a degree of crystallization is 1 to 20%, (ii) a thickness is 3 to 50 μm and (iii) a content of an electroconductive material is 1 to 20% by weight (wt. %),
wherein said hydrophobic thermoplastic resin film is laminated on at least one surface of the fiber base and wherein the laminated hydrophobic thermoplastic resin film is a single layer.

2. The thermoplastic prepreg intermediate material for a fuel cell separation plate according to claim 1 , wherein the electroconductive material is one selected from the group consisting of silver nanowire, carbon nanotube, graphene and carbon black.

3. The thermoplastic prepreg intermediate material for a fuel cell separation plate according to claim 1 , wherein the degree of crystallization of the hydrophobic thermoplastic resin film is 3 to 12%.

4. The thermoplastic prepreg intermediate material for a fuel cell separation plate according to claim 1 , wherein the thickness of the hydrophobic thermoplastic resin is 7 to 40 μm.

5. The thermoplastic prepreg intermediate material for a fuel cell separation plate according to claim 1 , wherein a weight ratio of the fiber base:the hydrophobic thermoplastic resin film is 65 to 90 wt. %: 10 to 35 wt. %.

6. The thermoplastic prepreg intermediate material for a fuel cell separation plate according to claim 1 , wherein the fiber base is a fiber sheet in which fibers on a filament are arranged in one direction.

7. The thermoplastic prepreg intermediate material for a fuel cell separation plate according to claim 1 , wherein the hydrophobic thermoplastic resin film is one selected from the group consisting of a polypropylene resin film, polyester resin film, thermoplastic polyurethane film, polyethylene resin film, polybutylene terephthalate resin film, polyamide resin film, polyethylene terephthalate resin film, polyphenylene sulfide film, polytetrafluoroethylene resin film, and polyetherether ketone resin film.

8. A method for manufacturing a thermoplastic prepreg for a fuel cell separation plate, comprising:
laminating a hydrophobic thermoplastic resin film, of which (i) a degree of crystallization is 1 to 20%, (ii) a thickness is 3 to 50 pm and (iii) a content of an electroconductive material is 1 to 20 wt. %, on at least one surface of a fiber base to prepare a thermoplastic prepreg intermediate material for a fuel cell separation plate; and
pressurizing the prepared thermoplastic prepreg intermediate material for a fuel cell separation plate at a temperature higher than a melting point of the hydrophobic thermoplastic resin film,
wherein the thermoplastic prepreg intermediate material consists of the hydrophobic thermoplastic resin film laminated on at least one surface of the fiber base, and wherein the laminated hydrophobic thermoplastic resin film is a single layer.

9. The method according to claim 8 , the pressurizing process is performed with a pressure of 50 to 1,500 kgf/cm at a temperature 30 to 100° C. higher than the melting point of the hydrophobic thermoplastic resin.

Assignees

• Kolon Inc

Inventors

• Yi Jee Sung
• Lee Hyun Chul
• Yoon Joon Young
• Cho Eun Jeong
• Kang Chung Seock

Classifications

• H01M8/0221 Primary

  Organic resins; Organic polymers · CPC title

• C08J5/249

  characterised by the additives used in the prepolymer mixture · CPC title

• C08J5/246

  using polymer based synthetic fibres · CPC title

• C08J5/243

  using carbon fibres · CPC title

• B32B37/182 Primary

  one or more of the layers being plastic · CPC title