Adhesive sheet and method for producing adhesive sheet

Patent metadata

Field	Value
Publication number	US-10696873-B2
Application number	US-201615763365-A
Country	US
Kind code	B2
Filing date	Sep 27, 2016
Priority date	Sep 28, 2015
Publication date	Jun 30, 2020
Grant date	Jun 30, 2020

Abstract

Provided is a pressure sensitive adhesive sheet including a resin layer that is a multilayer structure containing at least a layer (Xβ), a layer (Y1), and a layer (Xα) laminated in this order, a surface (α) of the layer (Xα) of the resin layer having pressure sensitive adhesiveness, at least a constitutional component contained in the layer (Y1) being different from constitutional components contained in the layer (Xα) and the layer (Xβ), on the prescribed cross section (P1) of the pressure sensitive adhesive sheet, in a range of 250 μm in a horizontal direction freely-selected, a difference between a maximum value and a minimum value of the layer (Xα) being 3.00 μm or more, and a difference between a maximum value and a minimum value of the layer (Y1) being 5.00 μm or more.

First claim

The invention claimed is:

1. A pressure sensitive adhesive sheet, comprising:
a substrate or a release material;
a resin layer on the substrate or the release material, the resin layer having a multilayered structure comprising a layer (Xβ), a layer (Y 1 ), and a layer (Xα) laminated in this order,
wherein
at least a surface (α) of the layer (Xα) of the resin layer has pressure sensitive adhesiveness,
the layer (Y 1 ) comprises a constitutional component different from a constitutional component in the layer (Xα) and a constitutional component in the layer (Xβ), and
when a 5 mm×5 mm square region (P) is randomly selected on the surface (α) and the pressure sensitive adhesive sheet is cut along each of two diagonal lines of the region (P) in a thickness direction perpendicular to the region (P) on the surface (α) to expose two cross sections of the pressure sensitive adhesive sheet, and a region having a width of 250 μm in a horizontal direction is randomly selected on at least one cross section (P 1 ) of the two cross sections, a thickness of the layer (Xα) and a thickness of the layer (Y 1 ) in the cross section (P 1 ) satisfy (Xα-I) and (Y 1 -I):
(Xα-I): a difference [H MAX (Xα)−H MIN (Xα)] between a maximum value (H MAX (Xα)) of the thickness of the layer (Xα) and a minimum value (H MIN (Xα)) of the thickness of the layer (Xα) is 3.00 μm or more, and
(Y 1 -I): a difference [H MAX (Y 1 )−H MIN (Y 1 )] between a maximum value (H MAX (Y 1 )) of the thickness of the layer (Y 1 ) and a minimum value (H MIN (Y 1 )) of the thickness of the layer (Y 1 ) is 5.00 μm or more.

2. The pressure sensitive adhesive sheet according to claim 1 , wherein
the resin layer comprises a resin part (X) comprising a resin and a particle part (Y) consisting of particles,
the layer (Xβ) mainly comprises the resin part (X),
the layer (Y 1 ) comprises the particle part (Y), and
the layer (Xα) mainly comprises the resin part (X).

3. The pressure sensitive adhesive sheet according to claim 1 , wherein the thickness of the layer (Xα) and the thickness of the layer (Y 1 ) in the region having the width of 250 μm on the cross section (P 1 ) further satisfy (Xα-II) and (Y 1 -II):
(Xα-II): a standard deviation of the thickness of the layer (Xα) with respect to an average value is 1.00 or more, and
(Y 1 -II): a standard deviation of the thickness of the layer (Y 1 ) with respect to an average value is 2.00 or more.

4. The pressure sensitive adhesive sheet according to claim 1 , wherein a thickness of the layer (Xβ) in the region having the width of 250 μm on the cross section (P 1 ) satisfies (Xβ-I):
(Xβ-I): a difference [H MAX (Xβ)−H MIN (Xβ)] between a maximum value (H MAX (Xβ)) of the thickness of the layer (Xβ) and a minimum value (H MIN (Xβ)) of the thickness of the layer (Xβ) is 3.00 μm or more.

5. The pressure sensitive adhesive sheet according to claim 1 , wherein a thickness of the layer (Xβ) in the region having the width of 250 μm on the cross section (P 1 ) satisfies (Xβ-II):
(Xβ-II): a standard deviation of the thickness of the layer (Xβ) with respect to an average value is 1.00 or more.

6. The pressure sensitive adhesive sheet according to claim 1 , wherein in a graph showing the thickness of the layer (Y 1 ) at positions varying from 0 μm to 250 μm along the horizontal direction in the region having the width of 250 μm on the cross section (P 1 ), at least one range including a maximum value (Q) satisfying (III) exists:
(III): in the at least one range in the graph, along the horizontal direction, the thickness of the layer (Y 1 ) exceeds Ra (μm), subsequently exceeds Ra+3 (μm) to reach the maximum value (Q), then underruns Ra+3 (μm), and further underruns Ra (μm),
wherein Ra (μm) is an arithmetic average value of the thickness of the layer (Y 1 ) in the region.

7. The pressure sensitive adhesive sheet according to claim 1 , wherein in the region having the width of 250 μm on the cross section (P 1 ), the surface (α) of the layer (Xα) has a concave portion at a position vertically above a position at which the layer (Y 1 ) has the minimum value (H MIN (Y 1 )) of the thickness.

8. The pressure sensitive adhesive sheet according to claim 2 , wherein a mass retention rate after heating the resin layer at 800° C. for 30 minutes is 3 to 90% by mass.

9. The pressure sensitive adhesive sheet according to claim 2 , wherein the resin included in the resin part (X) comprises a pressure sensitive adhesive resin.

10. The pressure sensitive adhesive sheet according to claim 2 , wherein the resin part (X) further comprises at least one crosslinking agent selected from the group consisting of a metal chelate crosslinking agent and an epoxy crosslinking agent.

11. The pressure sensitive adhesive sheet according to claim 2 , wherein the particles are at least one selected from the group consisting of silica particles, metal oxide particles, and smectite.

12. The pressure sensitive adhesive sheet according to claim 1 , wherein a surface (β) of the resin layer on a side on which the substrate or the release material is provided has pressure sensitive adhesiveness.

13. The pressure sensitive adhesive sheet according to claim 1 , wherein
the layer (Xβ) is formed from a composition (xβ) comprising a resin and less than 15% by mass of fine particles,
the layer (Y 1 ) is formed from a composition (y) comprising 15% by mass or more of fine particles, and
the layer (Xα) formed from a composition (xα) comprising a resin and less than 15% by mass of fine particles.

14. The pressure sensitive adhesive sheet according to claim 1 , wherein
the resin layer has a thickness of 10 to 75 μm,
the difference [H MAX (Xα)−H MIN (Xα)] in the (Xα-I) is 8.00 μm or more, and
the difference [H MAX (Y 1 )−H MIN (Y 1 )] in the (Y 1 -I) is 9.00 μm or more.

15. A method for producing the pressure sensitive adhesive sheet according to claim 1 , the method comprising:
laminating, on the substrate or the release material, a coating film (xβ′) formed by a composition (xβ) comprising a resin and less than 15% by mass of fine particles, a coating film (y′) formed by a composition (y) comprising 15% by mass or more of fine particles, and a coating film (xα′) formed by a composition (xα) comprising a resin and less than 15% by mass of fine particles, in this order, and
simultaneously drying the coating film (xβ′), the coating film (y′), and the coating film (xα′), such that the layer (Xβ) is formed from the coating film (xβ′), the layer (Y 1 ) is formed from the coating film (y′), and the layer (Xα) is formed from the coating film (xα′).

16. A method for producing the pressure sensitive adhesive sheet according to claim 1 , the method comprising:
laminating, on the layer (Xβ) provided on the substrate or the release material, a coating film (y′) formed by a composition (y) comprising 15% by mass or more of fine particles and a coating film (xα′) formed by a composition (xα) comprising a resin and less than 15% by mass of fine particles in this order, and
simultaneously drying the coating film (y′) and the coating film (xα′) such that the layer (Y 1 ) is formed from the coating film (y′) and the layer (Xα) is formed from the coating film (xα′).

Assignees

• Lintec Corp

Inventors

• Uemura Kazue
• Yanagimoto Kaisuke
• Kato Kiichiro

Classifications

• B32B5/142 Primary

  Variation across the area of the layer · CPC title

• C09J2301/414

  presence of a copolymer · CPC title

• C09J2301/408

  additives as essential feature of the adhesive layer · CPC title

• C08K3/22

  of metals · CPC title

• B32B27/10

  of paper or cardboard · CPC title