Epoxy resin composition

Patent metadata

Field	Value
Publication number	US-10696780-B2
Application number	US-201715631790-A
Country	US
Kind code	B2
Filing date	Jun 23, 2017
Priority date	Jun 28, 2016
Publication date	Jun 30, 2020
Grant date	Jun 30, 2020

Abstract

In developing epoxy resin compositions used as an adhesive for structure (structural adhesive) required to have adhesive properties, if each component is increased to further enhance the adhesive properties such as shear bond strength and peel strength, this causes problems, for example, as follows. The viscosity becomes so high that the workability deteriorates. Hence, the added amount has to be limited. Moreover, the cured product becomes excessively flexible, so that the shear bond strength deteriorates. An epoxy resin composition contains the following components (A) to (E), where the component (A) does not include the component (C): the component (A): an epoxy resin; the component (B): a blocked urethane resin; the component (C): a rubber-modified epoxy resin; the component (D): rubber particles; and the component (E): a latent curing agent.

First claim

The invention claimed is:

1. An epoxy resin composition comprising the following components (A) to (F), wherein the component (A) does not include the component (C):
the component (A): an epoxy resin selected from the group consisting of bisphenol A epoxy resins, bisphenol F epoxy resins, and naphthalene epoxy resins;
the component (B): a blocked urethane resin;
the component (C): a NBR-modified epoxy resin;
the component (D): rubber particles selected from the group consisting of acrylic rubbers and butadiene rubbers;
the component (E): a latent curing agent which is a mixture of an amine adduct compound with an agent selected from the group consisting of dicyandiamide, derivatives of dicyandiamide, urea compounds, and derivatives of urea compounds; and
the component (F): calcium carbonate,
wherein a content of the component (B) is 3 to 30 parts by mass relative to 100 parts by mass of a total of the component (A) and the component (C),
a content of the component (C) is 1 to 16% by mass of the total of the component (A) and the component (C),
a content of the component (D) is 3 to 30 parts by mass relative to 100 parts by mass of the total of the component (A) and the component (C),
a content of the component (E) is 3 to 20 parts by mass relative to 100 parts by mass of the total of the component (A) and the component (C), and
a content of the component (F) is 1 to 100 parts by mass relative to 100 parts by mass of the total of the component (A) and the component (C).

2. The epoxy resin composition according to claim 1 , comprising
3 to 20 parts by mass of the component (B) and 5 to 20 parts by mass of the component (D) relative to 100 parts by mass of the total of the components (A) and (C), and
1 to 9% by mass of the component (C) in the total of the components (A) and (C).

3. The epoxy resin composition according to claim 1 , wherein the component (B) is a blocked urethane resin obtained from a urethane resin formed by reacting a polyalkylene polyol with a polyisocyanate compound.

4. The epoxy resin composition according to claim 1 , wherein the component (A) is selected from the group consisting of the bisphenol A epoxy resins and the bisphenol F epoxy resins.

5. The epoxy resin composition according to claim 1 , wherein the rubber particles of the component (D) have an average particle diameter of 0.1 to 0.5 μm.

6. A thermosetting adhesive for structure comprising the epoxy resin composition according to claim 1 .

7. The thermosetting adhesive for structure according to claim 6 , wherein the rubber particles of the component (D) have an average particle diameter of 0.1 to 1 μm.

8. A cured product obtained by curing the epoxy resin composition according to claim 1 .

9. The cured product according to claim 8 , wherein the rubber particles of the component (D) have an average particle diameter of 0.1 to 1 μm.

10. An adherend adhesion method comprising the steps of:
disposing the epoxy resin composition according to claim 1 between a pair of adherends; and
curing the epoxy resin composition by heating.

11. The adhesion method according to claim 10 , wherein the heating is performed at 50° C. to 200° C.

12. The adhesion method according to claim 10 , wherein the rubber particles of the component (D) have an average particle diameter of 0.1 to 1 μm.

13. The epoxy resin composition according to claim 1 , wherein the rubber particles of the component (D) have an average particle diameter of 0.1 to 1 μm.

Assignees

• Three Bond Co Ltd

Inventors

• Mashima Miki
• MORITOKI Tatsuya
• Shimokawa Eiji

Classifications

• C08G59/4021

  Ureas; Thioureas; Guanidines; Dicyandiamides · CPC title

• C08G18/4825

  Polyethers containing two hydroxy groups (C08G18/4833 - C08G18/5096 take precedence) · CPC title

• C08G18/755

  and at least one isocyanate or isothiocyanate group linked to a secondary carbon atom of the cycloaliphatic ring, e.g. isophorone diisocyanate · CPC title

• C08L63/00

  Compositions of epoxy resins; Compositions of derivatives of epoxy resins · CPC title

• C08G18/58 Primary

  Epoxy resins {(C08G18/42, C08G18/48 take precedence; reaction products of epoxy resins with at least equivalent amounts of compounds containing active hydrogen C08G18/6407, with at least equivalent amounts of amines C08G18/6415; polymeric products of isocyanates or isothiocyanates with epoxy compounds having no active hydrogen C08G18/003)} · CPC title