Vehicle underbody structure comprising a reinforcement element between a longitudinal beam and a lowerside sill part

Patent metadata

Field	Value
Publication number	US-10676138-B2
Application number	US-201615780079-A
Country	US
Kind code	B2
Filing date	Dec 9, 2016
Priority date	Dec 9, 2015
Publication date	Jun 9, 2020
Grant date	Jun 9, 2020

Abstract

A vehicle underbody structure containing a floor panel, at least one longitudinal beam extending in a longitudinal direction of the vehicle under said floor panel and at least one lowerside sill part extending in the longitudinal direction adjacent to the floor panel, and at least one reinforcement element extending in a transversal direction, substantially perpendicular to the longitudinal direction, said reinforcement element made of a press hardened steel part having a tensile strength higher or equal to 1200 MPa and extending under the floor panel and being attached at one of its transversal ends to the longitudinal beam and at the other of its transversal ends to the lowerside sill part is provided. A vehicle body including the vehicle underbody structure is also provided.

First claim

What is claimed is:

1. A vehicle underbody structure, comprising
a floor panel,
at least one longitudinal beam extending in a longitudinal direction of the vehicle under said floor panel and
at least one lowerside sill part extending in the longitudinal direction adjacent to the floor panel,
the vehicle underbody structure further comprising at least one reinforcement element extending in a transversal direction, substantially perpendicular to the longitudinal direction, said reinforcement element extending under the floor panel and being attached at one of its transversal ends to said longitudinal beam and at the other of its transversal ends to said lowerside sill part, wherein:
said reinforcement element is made of a press-hardened steel part having a tensile strength higher or equal to 1200 MPa, and
said reinforcement element comprises a first flank extending in a plane substantially parallel to the floor panel and a second flank extending in a plane perpendicular to the first flank, said first and second flanks both joining said longitudinal beam to said lowerside sill part, the second flank extending in a plane forming a non-zero angle with the longitudinal direction,
wherein the first flank has a substantially triangular shape, a first side of said triangular shape extending along said longitudinal beam, a second side of said triangle shape joining said longitudinal beam to the said lowerside sill part, and a third side of said triangular shape extending along the second flank.

2. The vehicle underbody structure according to claim 1 , wherein said reinforcement element has a martensitic microstructure, and wherein either said longitudinal beam or said lowerside sill part has a structure which is not fully martensitic.

3. The vehicle underbody structure according to claim 2 , wherein both said longitudinal beam and said lowerside sill part have structures which are not fully martensitic.

4. The vehicle underbody structure according to claim 1 , wherein said reinforcement element is attached to said lowerside sill part at a front longitudinal end of said lowerside sill part.

5. The vehicle underbody structure according to claim 1 , wherein said reinforcement element is welded to said longitudinal beam and to said lowerside sill part.

6. The vehicle underbody structure according to claim 5 , wherein the welding of said reinforcement element to said one longitudinal beam and to said lowerside sill part is a resistance spot welding or an arc welding or a laser welding.

7. The vehicle underbody structure according to claim 1 , wherein the composition of the press-hardened steel comprises in % weight:
0.15%≤C≤0.5%,
0.5%≤Mn≤3%,
0.1%≤Si≤1%,
0.005%≤Cr≤1%,
Ti≤0.2%,
Al≤0.1%,
S≤0.05%,
P≤0.1%,
B≤0.010%, the remainder being iron and unavoidable impurities resulting from the elaboration, or
0.20%≤C≤0.25%,
1.1%≤Mn≤1.4%,
0.15%≤Si≤0.35%,
≤Cr≤0.30%,
0.020%≤Ti≤0.060%,
0.020%≤Al≤0.060%,
S≤0.005%,
P≤0.025%,
0.002%≤B≤0.004%, the remainder being iron and unavoidable impurities resulting from the elaboration; or
0.24%≤C≤0.38%,
0.40%≤Mn≤3%,
0.10%≤Si≤0.70%,
0.015%≤Al≤0.070%,
Cr≤2%,
0.25%≤Ni≤2%,
0.015%≤Ti≤0.10%,
Nb≤0.060%,
0.0005%≤B≤0.0040%, 0.003%≤N≤0.010%, S≤0.005%, P≤0.025%, %, the remainder being iron and unavoidable impurities resulting from the elaboration.

8. The vehicle underbody structure according to claim 1 , wherein the press hardened steel part is coated.

9. The vehicle underbody structure according to claim 1 , further comprising a front pillar attached to said lowerside sill part and extending in an elevation direction substantially perpendicular to the longitudinal and transversal directions, said front pillar extending from a longitudinal front end of said lowerside sill part.

10. The vehicle underbody structure according to claim 1 , wherein
the at least one longitudinal beam includes a left longitudinal beam and a right longitudinal beam, both extending in the longitudinal direction under said floor panel, and
the at least one lowerside sill includes a left lowerside sill part and a right lowerside sill part, extending in the longitudinal direction on either side of the floor panel,
the at least one reinforcement element includes a left reinforcement element extending between the left longitudinal beam and the left lowerside sill part, and
a right reinforcement element extending between the right longitudinal beam and the right lowerside sill part,
said left and right reinforcement elements being made of a press hardened steel part having a tensile strength higher or equal to 1200 MPa.

11. The vehicle underbody structure according to claim 10 , further comprising a transversal beam extending between the left longitudinal beam and the right longitudinal beam, said transversal beam extending along the same transversal axis as the left and right reinforcement elements; said transversal beam being made of a press hardened steel part having a tensile strength higher or equal to 1200 MPa.

12. A vehicle body comprising a vehicle underbody structure according to claim 1 .

Assignees

• Arcelormittal

Inventors

• Viaux Ivan
• Arnautu Florin

Classifications

• C22C38/002

  containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60 · CPC title

• B62D29/007

  predominantly of special steel or specially treated steel, e.g. stainless steel or locally surface hardened steel · CPC title

• C22C38/48

  with niobium or tantalum · CPC title

• C22C38/06

  containing aluminium · CPC title

• C22C38/58

  with more than 1.5% by weight of manganese · CPC title