Dispersants for colouration of ceramic tiles using ink jet inks

Patent metadata

Field	Value
Publication number	US-10675889-B2
Application number	US-201615735425-A
Country	US
Kind code	B2
Filing date	Jun 10, 2016
Priority date	Jun 12, 2015
Publication date	Jun 9, 2020
Grant date	Jun 9, 2020

Abstract

The invention provides dispersed inorganic mixed metal oxide pigment compositions in a non-aqueous media utilizing a dispersant having polyisobutylene succinic anhydride structure to disperse a mixed metal oxide pigment in the media. The metal oxide pigment is of the type used to colour ceramic or glass articles. A milling process using beads is also described to reduce the mixed metal oxide particle size to the desired range. A method of using the mixed metal oxide dispersion to digitally print an image on a ceramic or glass article using the dispersion jetted through a nozzle and subsequently firing the coloured article is also described.

First claim

What is claimed is:

1. A composition, wherein the composition is a pigment dispersion comprising:
a) 20-79 wt.% of a continuous phase liquid non-polar organic media having less than 7 wt.% water based on the weight of the dispersion;
b) 20-60 wt.% of a mixed metal oxide ceramic pigment in particulate form that develops its full color intensity and hue after firing at elevated temperatures; and
c) 1-20 wt.% of a dispersant comprising the reaction product of polyisobutylene with maleic acid and/or anhydride under reaction conditions to form a chemically coupled molecule;
wherein said reaction product of polyisobutylene with maleic acid and/or anhydride has a number average molecular weight from 500 and 2500 g/mole and an acid number from 40 to 200 mgKOH/g of dispersant;
wherein said non-polar organic continuous phase has a molecular weight from about 200 to about 20,000 g/mole and is comprised of mostly carbon and hydrogen with up to 10 wt.% of combined heteroatoms selected from nitrogen and oxygen based on the weight of said organic continuous phase; and
wherein the particulate solid is at least one ceramic pigment of mixed metal oxides which contain a combination of two or more elements in cationic form selected from Al, Mg, Ca, Cd, Co, Cr, Fe, In, Mn, Ni, Pr, Sb, Se, Si, Sn, Ti, V, Zn and Zr.

2. A process for milling an inorganic mixed metal oxide particulate, having a dry powder volume average particle diameter D 50 in excess of 2 micron, in a continuous organic medium to a D 50 particle size of less than 600 nanometers, said process comprising:
a) blending said continuous organic medium, said inorganic mixed metal oxide particulate, wherein said inorganic mixed metal oxide particulate is a mixed metal oxide pigment that develops its color intensity and hue after firing at elevated temperatures, optionally including a vitreous glaze material, having a dry powder volume average particle diameter in excess of 2 micron, and a dispersing agent comprising a reaction product of polyisobutylene with maleic acid and/or anhydride;
b) milling said mixed metal oxide pigment dispersed with said dispersing agent in said continuous medium using a bead mill for 5 minutes to 60 hours forming a dispersion of said mixed metal oxide in said continuous medium; and
c) confirming the volume average particle diameter D 50 is less than 600 nanometers;
wherein said reaction product of polyisobutylene with maleic acid and/or anhydride has a number average molecular weight from 500 and 2500 g/mole and an acid number from 40 to 200 mgKOH/g of dispersant;
wherein said continuous organic medium has a molecular weight from about 200 to about 20,000 g/mole and is comprised of mostly carbon and hydrogen with up to 10 wt.% of combined heteroatoms selected from nitrogen and oxygen based on the weight of said organic continuous phase; and
wherein the particulate is at least one ceramic pigment of mixed metal oxides which contain a combination of two or more elements in cationic form selected from Al, Mg, Ca, Cd, Co, Cr, Fe, In, Mn, Ni, Pr, Sb, Se, Si, Sn, Ti, V, Zn and Zr.

3. The process according to claim 2 , wherein the continuous organic medium comprises less than 7 wt.% water based on the weight of the dispersion.

4. The process according to claim 3 , wherein the continuous organic medium comprises an organic solvent with less than 5 wt.% water based on the weight of the dispersion.

5. A process for digitally printing on ceramic article or glass article substrate using an ink jetted through a nozzle;
a) providing a mixed metal oxide dispersed in a continuous nonpolar organic medium with a dispersing agent comprising a reaction product of polyisobutylene with maleic acid and/or anhydride;
b) jetting said mixed metal oxide dispersed in said continuous medium using said dispersing agent onto said substrate to form a pigmented digital image (optionally on a pre-glaze layer(s) on a ceramic surface), wherein said pigmented digital image on said substrate develops into a colored image upon firing said ceramic substrate or heating said glass substrate to provide tempering or annealing;
c) optionally applying a glaze over said digital image; and
d) heating said ceramic article at an elevated temperature or heating said glass article to anneal or temper it, wherein said image from mixed metal oxide develops optimal color intensity upon heating to its color;
wherein said reaction product of polyisobutylene with maleic acid and/or anhydride has a number average molecular weight from 500 and 2500 g/mole and an acid number from 40 to 200 mgKOH/g of dispersant;
wherein said continuous nonpolar organic medium has a molecular weight from about 200 to about 20,000 g/mole and is comprised of mostly carbon and hydrogen with up to 10 wt.% of combined heteroatoms selected from nitrogen and oxygen based on the weight of said organic continuous phase; and
wherein the mixed metal oxide is at least one ceramic pigment of mixed metal oxides which contain a combination of two or more elements in cationic form selected from Al, Mg, Ca, Cd, Co, Cr, Fe, In, Mn, Ni, Pr, Sb, Se, Si, Sn, Ti, V, Zn and Zr.

6. The process of claim 5 , wherein the mixed metal oxide pigment develops its color intensity and hue after firing at 600° C. or above for a ceramic substrate or 400° C. or above for a glass substrate.

Assignees

• Lubrizol Advanced Mat Inc

Inventors

• Thetford Dean

Classifications

• C03C17/02

  with glass (C03C17/34, C03C17/44 take precedence) · CPC title

• C04B41/5027

  Oxide ceramics in general; Specific oxide ceramics not covered by C04B41/5029 - C04B41/5051 · CPC title

• B41J2/01 Primary

  Ink jet · CPC title

• C09D17/002

  in organic medium (C09D17/003, C09D17/004 take precedence) · CPC title

• C09D11/106

  containing macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds · CPC title