Decarburized self-piercing rivet

Patent metadata

Field	Value
Publication number	US-10669599-B2
Application number	US-201715705474-A
Country	US
Kind code	B2
Filing date	Sep 15, 2017
Priority date	Sep 16, 2016
Publication date	Jun 2, 2020
Grant date	Jun 2, 2020

Abstract

A decarburized self-piercing rivet is provided that can join dissimilar sheets of material while reducing the likelihood of forming cracks during the riveting process. The decarburized self-piercing rivet has requisite hardness and column strength to pierce the sheets of material and also has a ferrite layer that improves ductility and performance of the rivet. The increase ductility reduces the likelihood of cracks forming during the riveting process. A manufacturing process is also provided that austentizing and decarburizes the rivet simultaneously in a salt pot furnace to reduce the need for any post-austentizing localized heat treatments.

First claim

The invention claimed is:

1. A method of manufacturing a self-piercing rivet, comprising:
providing a rivet having a grip body, a head portion, and a tail portion, wherein an outer layer of said tail portion has a first carbon content;
placing said rivet in a furnace at a predetermined temperature of between about 800 and 900° C.;
austentizing and decarburizing said rivet in said furnace at said predetermined temperature such that said outer layer of said tail portion has a second carbon content that is lower than said first carbon content;
removing said rivet from said furnace after a predetermined time of between about 20 and 240 minutes; and
quenching said rivet in a bath such that said outer layer of said rivet has a volume fraction of ferrite and a remaining bulk material of said rivet has a volume fraction of martensite that is greater than said volume fraction of ferrite.

2. The method of claim 1 , wherein said furnace is a salt pot furnace.

3. The method of claim 2 , wherein said salt pot furnace has a salt mixture of approximately 90% barium chloride and approximately 10% sodium chloride.

4. The method of claim 1 , further comprising:
tempering said rivet at a second predetermined temperature of between about 150 and 400° C. for a second predetermined time of between about 20 and 40 minutes.

5. The method of claim 1 , further comprising applying an acetone wash to said rivet to remove salt.

6. The method of claim 4 , wherein said bulk material and said outer layer of said rivet are at least one of a 10B37 steel and a 4340 steel, and said second predetermined temperature for tempering is between about 150 to 250° C., and said second predetermined time is approximately about 20 to 40 minutes.

7. The method of claim 4 , wherein said bulk material and said outer layer of said rivet is a 5160 steel, and said second predetermined temperature for tempering is approximately about 300 to 400° C., and said second predetermined time is approximately about 20 to 40 minutes.

8. The method of claim 1 , wherein said predetermined time for austentizing and decarburizing is between about 50 to 70 minutes.

Assignees

• Colorado School Of Mines

Inventors

• Van Hall Stephen N
• Findley Kip O

Classifications

• C21D1/18

  Hardening (C21D1/02 takes precedence); Quenching with or without subsequent tempering (quenching devices C21D1/62) · CPC title

• C21D1/63

  for bath quenching · CPC title

• B21J15/025

  Setting self-piercing rivets · CPC title

• C21D2211/001

  Austenite · CPC title

• F16B19/086

  Self-piercing rivets · CPC title