Latex composition for dip molding and molded article manufactured therefrom

Patent metadata

Field	Value
Publication number	US-10669406-B2
Application number	US-201615751326-A
Country	US
Kind code	B2
Filing date	Oct 5, 2016
Priority date	Oct 21, 2015
Publication date	Jun 2, 2020
Grant date	Jun 2, 2020

Abstract

Disclosed is a latex composition for dip-molding and a dip-molded article produced therefrom. More specifically, by using a water-soluble polymer such as poly(N-isopropylacrylamide) or a copolymer thereof in combination with a carbonic acid-modified nitrile-based copolymer latex, the stability of the latex is improved through crosslinking by hydrogen bonding, it is possible to manufacture a molded article which has a slow syneresis and is excellent in workability and does not tear even at a thin thickness due to high tensile strength.

First claim

The invention claimed is:

1. A latex composition for dip-molding comprising: a carboxylic acid-modified nitrile-based copolymer latex; and an poly(N-isopropylacrylamide) or a copolymer thereof
wherein the poly(N-isopropylacrylamide) copolymer is prepared by copolymerization of 80 or more and less than 100 mol % of N-isopropylacrylamide monomer and more than 0 and not more than 20 mole % of an ethylenically unsaturated carboxylic acid monomer.

2. The composition according to claim 1 , wherein the carboxylic acid-modified nitrile-based copolymer latex has a glass transition temperature of −50 to −15° C. and an average particle diameter of 90 to 200 nm.

3. The composition according to claim 1 , the poly(N-isopropylacrylamide) or copolymer thereof has a number average molecular weight of 5,000 to 80,000 g/mol.

4. The composition according to claim 1 , the poly(N-isopropylacrylamide) or copolymer thereof is used as an aqueous solution having a concentration of 0.5 to 15% by weight.

5. The composition according to claim 1 , wherein the ethylenically unsaturated carboxylic acid monomer is selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, maleic acid, fumaric acid and combinations thereof.

6. The composition according to claim 1 , comprising 0.1 to 10 parts by weight of the poly (N-isopropylacrylamide) or copolymer thereof with respect to 100 parts by weight of the carboxylic acid-modified nitrile-based copolymer.

7. The composition according to claim 1 , wherein the carboxylic acid-modified nitrile-based copolymer is prepared by polymerization of monomers mixture comprising 40 to 89% by weight of a conjugated diene monomer, 10 to 50% by weight of an ethylenically unsaturated nitrile-based monomer and 0.1 to 10% by weight of an ethylenically unsaturated acid monomer.

8. The composition according to claim 7 , wherein the conjugated diene monomer includes one selected from the group consisting of 1,3-butadiene, 2,3-dimethyl-1,3-butadiene, 2-ethyl-1,3-butadiene, 1,3-pentadiene, isoprene, and combinations thereof.

9. The composition according to claim 7 , wherein the ethylenically unsaturated nitrile-based monomer includes one selected from the group consisting of acrylonitrile, methacrylonitrile, fumaronitrile, α-chloronitrile, α-cyanoethyl acrylonitrile, and combinations thereof.

10. The composition according to claim 7 , wherein the ethylenically unsaturated acid monomer includes one selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, maleic acid, fumaric acid, maleic anhydride, citraconic anhydride, styrene sulfonic acid, monobutyl fumarate, monobutyl maleate, mono-2-hydroxypropyl maleate, and combinations thereof.

11. The composition according to claim 1 , further comprising one additive selected from the group consisting of a vulcanizing agent, a vulcanization catalyst, a filler, a crosslinking agent, a pigment, a thickener, a pH adjusting agent and a combination thereof.

12. A dip-molded article produced by dip-molding of the latex composition for dip-molding according to claim 1 .

13. A method of preparing a dip-molded article, said method comprising:
A) applying a coagulant solution to a mold and drying;
B) applying a latex composition for dip-molding to a mold to which the coagulant has been applied to form a dip-molding layer;
C) crosslinking the dip molding layer; and
D) peeling off the cross-linked dip-molded layer from the mold to obtain a dip-molded article, wherein the latex composition for dip-molding is the latex composition for dip-molding according to claim 1 .

Assignees

• Lg Chemical Ltd

Inventors

• Kwon Won Sang
• Yeu Seung Uk
• Han Jung Su
• Yang Seung Hun

Classifications

• C08J5/02

  Direct processing of dispersions, e.g. latex, to articles · CPC title

• C08J2309/04

  Latex · CPC title

• B29C41/00

  Shaping by coating a mould, core or other substrate, i.e. by depositing material and stripping-off the shaped article; Apparatus therefor (with compacting pressure B29C43/00 {; by lay-up of reinforcement of substantial or continuous length B29C70/30}) · CPC title

• C08L9/04 Primary

  Latex · CPC title

• C08L33/26

  Homopolymers or copolymers of acrylamide or methacrylamide · CPC title