Base film for producing a graphic film

Patent metadata

Field	Value
Publication number	US-10668692-B2
Application number	US-201414893192-A
Country	US
Kind code	B2
Filing date	May 28, 2014
Priority date	May 30, 2013
Publication date	Jun 2, 2020
Grant date	Jun 2, 2020

Abstract

The present invention provides a method of reducing lifting of a graphics film from a substrate, the graphic film having a polymeric film layer having on one major side thereof an adhesive layer, wherein lifting is reduced by applying the graphic film to the substrate with an intermediary base film, the base film comprising a backing layer having opposite first and second major sides, the first major side having an adhesive layer and the graphic film being adhered to the second major side of the base film.

First claim

What is claimed is:

1. A method of reducing pop-up of a graphic film from a complex substrate, the graphic film having a polymeric film layer having on one major side thereof a first adhesive layer, wherein popping up from recesses in the complex substrate is reduced by applying the graphic film to the complex substrate with an intermediary base film, the base film comprising a backing layer having opposite first and second major sides and comprising a layer of an aminoplast and a polyester and/or a condensation product thereof, the base film having a thickness of at least 15 micrometers, the first major side having a second adhesive layer and the graphic film being adhered to the second major side of the base film.

2. The method according to claim 1 wherein after elongating the base film and the graphic film by an applied force to a first elongation level of 30% at a temperature of 23° C., holding the base film and the graphic film at the first elongation level for 10 min. and removing the applied force, a time needed to reduce the first elongation level of the base film to a predetermined second elongation level is larger than a time needed to reduce the first elongation level of the graphic film to the same predetermined second elongation level.

3. The method according to claim 1 , wherein the graphic film comprises a polyvinyl chloride film layer as the polymeric film layer and wherein the backing layer of the base film comprises a layer having a polymer other than a vinyl chloride based polymer.

4. The method according to claim 1 , wherein the second adhesive layer comprises a series of channels across at least two in-plane directions and wherein the channels are interconnected thereby defining a series of raised adhesive plateaus.

5. The method according to claim 4 wherein the second adhesive layer is protected by a release liner and wherein the release liner has a first topologically structured surface that is an inverse of a second topologically structured surface of the second adhesive layer and wherein respective topological structures of the release liner and the second adhesive layer are mated.

6. The method according to claim 1 , wherein the backing layer of the base film comprises a layer having a polymer other than a vinyl chloride based polymer and wherein the base film has an elongation at break of at least 50% tested at 25° C. according to DIN 53455 at a test speed of 300 mm/min.

Assignees

• 3M Innovative Properties Co

Inventors

• Dannewitz Viktor

Classifications

• B29K2667/00

  Use of polyesters {or derivatives thereof} for preformed parts, e.g. for inserts · CPC title

• B32B2367/00

  Polyesters, e.g. PET, i.e. polyethylene terephthalate · CPC title

• B32B3/30

  characterised by a layer formed with recesses or projections, e.g. {hollows, grooves, protuberances, ribs (apertured layer B32B3/266; layer with cavities or internal voids B32B3/26)} · CPC title

• B32B2405/00

  Adhesive articles, e.g. adhesive tapes · CPC title

• C09J133/00

  Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers · CPC title