Fire-resistant calcium sulphate-based products

Patent metadata

Field	Value
Publication number	US-10662113-B2
Application number	US-201515525467-A
Country	US
Kind code	B2
Filing date	Nov 17, 2015
Priority date	Nov 21, 2014
Publication date	May 26, 2020
Grant date	May 26, 2020

Abstract

The present invention provides calcium sulphate-based product having reduced shrinkage after exposure to high temperatures, the product comprising gypsum, a pozzolan source (e.g. in an amount between 4-27 wt %) and a metal salt additive (in an amount between 0.5 and 10 wt %). The pozzolan source may be selected from a kaolinitic clay material, fly ash, rice husk ash, diatomaceous earths, volcanic ashes and pumices, micro-silica, silica fume and silicone oil. The metal salt additive may be a metal salt which decomposes between a temperature of 300-500° C. to yield a metal oxide, e.g. magnesium nitrate.

First claim

The invention claimed is:

1. A gypsum wallboard comprising:
gypsum, a pozzolan source, and a metal salt, wherein:
the gypsum is provided in an amount of 40% or greater based on a total weight of the gypsum wallboard,
the metal salt is selected from nitrate and hydrogen carbonate salts of calcium, magnesium, copper, zinc, iron and aluminum, and carbonate and chloride salts of copper, zinc, iron or aluminum; and
the metal salt is provided in an amount of between 0.5 wt % and 10 wt % based on the weight of the gypsum, the pozzolan source and the metal salt.

2. The gypsum wallboard according to claim 1 , wherein the pozzolan source is included in an amount between 4 wt % and 27 wt % (based on the weight of the gypsum, the pozzolan source and the metal salt).

3. The gypsum wallboard according to claim 1 , wherein the wt % of pozzolan source and wt % metal salt are equal.

4. The gypsum wallboard according to claim 1 , wherein the pozzolan source is selected from a kaolinitic clay material, fly ash, rice husk ash, diatomaceous earths, volcanic ashes and pumices, micro-silica, silica fume and silicone oil.

5. The gypsum wallboard according to claim 1 , wherein the metal salt decomposes between a temperature of 300° C.-500° C. to yield a metal oxide.

6. The gypsum wallboard according to claim 1 , wherein the metal salt is a magnesium salt.

7. A gypsum wallboard formed by a process comprising:
drying an aqueous slurry containing gypsum, a pozzolan source, and a metal salt additive, wherein:
the gypsum is provided in the gypsum wallboard in an amount of 40% or greater based on a total weight of the gypsum, the pozzolan source and the metal salt additive,
the metal salt additive is selected from nitrate and hydrogen carbonate salts of calcium, magnesium, copper, zinc, iron and aluminum and carbonate and chloride salts of copper, zinc, iron or aluminum, and
the metal salt additive is included in the slurry in an amount between 1 wt % and 15 wt %.

8. The gypsum wallboard according to claim 7 , wherein the pozzolan source is included in the slurry in an amount between 5 wt % and 30 wt %.

9. A calcium sulphate-based composition for use in forming a gypsum wallboard by drying an aqueous slurry of the calcium sulphate-based composition, the calcium sulphate-based composition comprising:
gypsum, a pozzolan source, and a metal salt, wherein:
the gypsum is provided in the gypsum wallboard in an amount of 40% or greater based on a total weight of the gypsum wallboard,
the metal salt is selected from nitrate and hydrogen carbonate salts of calcium, magnesium, copper, zinc, iron and aluminum and carbonate and chloride salts of copper, zinc, iron or aluminum, and
the metal salt is included in the slurry in an amount between 1 wt % and 15 wt %.

10. The calcium sulphate-based composition according to claim 9 , wherein the pozzolan source is included in an amount between 5 wt % and 30 wt %.

11. The calcium sulphate-based composition according to claim 9 , wherein the wt % of pozzolan source and wt % metal salt are equal.

12. The calcium sulphate-based composition according to claim 9 , wherein the pozzolan source is selected from a kaolinitic clay material, fly ash, rice husk ash, diatomaceous earths, volcanic ashes and pumices, micro-silica, silica fume and silicone oil.

13. The calcium sulphate-based composition according to claim 9 , wherein the metal salt decomposes between a temperature of 300° C.-500° C. to yield a metal oxide.

14. The calcium sulphate-based composition according to claim 13 , wherein the metal salt is a magnesium salt.

15. A method of forming a gypsum wallboard by drying an aqueous slurry comprising the composition according to claim 9 .

16. A gypsum wallboard comprising:
gypsum, a pozzolan source, and a metal salt additive, wherein:
the gypsum is provided in an amount of 40% or greater based on a total weight of the gypsum wallboard,
the metal salt additive is selected from calcium nitrate and salts of magnesium, copper, zinc, or iron, and
the wt % of pozzolan source and wt % metal salt additive are equal.

17. The gypsum wallboard according to claim 16 , wherein the pozzolan source is selected from a kaolinitic clay material, fly ash, rice husk ash, diatomaceous earths, volcanic ashes and pumices, micro-silica, silica fume and silicone oil.

18. The gypsum wallboard according to claim 16 , wherein the metal salt decomposes between a temperature of 300-500° C. to yield a metal oxide.

19. The gypsum wallboard according to claim 18 , wherein the metal salt is a magnesium salt.

Assignees

• Saint Gobain Placo

Inventors

• Brooks Laura
• Fisher Robin
• Rideout Jan

Classifications

• C04B2111/34

  Non-shrinking or non-cracking materials · CPC title

• C04B22/10

  containing carbon in the anion, e.g. carbonates · CPC title

• C04B2111/00551

  Refractory coatings, e.g. for tamping · CPC title

• C04B28/14 Primary

  containing calcium sulfate cements {(gypsum-paper plates E04C)} · CPC title

• C04B2111/28

  Fire resistance, i.e. materials resistant to accidental fires or high temperatures · CPC title