Method of preparing superabsorbent polymer

Patent metadata

Field	Value
Publication number	US-10653812-B2
Application number	US-201615755340-A
Country	US
Kind code	B2
Filing date	Jun 13, 2016
Priority date	Mar 25, 2016
Publication date	May 19, 2020
Grant date	May 19, 2020

Abstract

Provided is a method of preparing a superabsorbent polymer which exhibits more improved liquid permeability and absorption rate while maintaining excellent absorption performance. The method of preparing the superabsorbent polymer may include the steps of: performing crosslinking polymerization of water-soluble ethylene-based unsaturated monomers having acidic groups which are at least partially neutralized in the presence of an internal crosslinking agent to form a water-containing gel polymer including a crosslinked polymer; drying, pulverizing, and size-sorting the water-containing gel polymer to form a base polymer powder; performing surface-crosslinking of the base polymer powder using a surface-crosslinking solution including one or more surface-crosslinking agents in the presence of first alumina particles; and adding second alumina particles to the surface-crosslinked base polymer powder and then mixing them with each other.

First claim

The invention claimed is:

1. A method of preparing a superabsorbent polymer, the method comprising the steps of:
performing crosslinking polymerization of water-soluble ethylene-based unsaturated monomers having acidic groups which are at least partially neutralized in the presence of an internal crosslinking agent to form a water-containing gel polymer including a crosslinked polymer;
drying, pulverizing, and size-sorting the water-containing gel polymer to form a base polymer powder;
performing surface-crosslinking of the base polymer powder using a surface-crosslinking solution including one or more surface-crosslinking agents selected from the group consisting of an alkylene carbonate having 2 to 5 carbon atoms, diol, triol, or polyol containing an alkyl group having 2 to 12 carbon atoms or polyethylene glycol having 2 to 12 carbon atoms, and diepoxy, triepoxy, or polyepoxy containing an alkyl group having 2 to 12 carbon atoms or polyethylene glycol having 2 to 12 carbon atoms, in the presence of first alumina particles; and
adding second alumina particles to the surface-crosslinked base polymer powder and then mixing them with each other,
wherein the first alumina is included in an amount of 0.01 to 0.2 parts by weight with respect to 100 parts by weight of the base polymer powder, and the second alumina is included in an amount of 0.05 to 0.3 parts by weight with respect to 100 parts by weight of the surface-crosslinked superabsorbent polymer powder.

2. The method of preparing the superabsorbent polymer of claim 1 , wherein the surface-crosslinking step includes the step of surface-crosslinking the base polymer powder by heat treatment in the presence of the surface-crosslinking solution including the first alumina particles and the surface-crosslinking agent.

3. The method of preparing the superabsorbent polymer of claim 1 , wherein the surface-crosslinking step includes the steps of treating the base polymer powder with the first alumina particles in a solid state, and
surface-crosslinking the base polymer powder by heat treatment in the presence of the surface-crosslinking solution including the surface-crosslinking agent.

4. The method of preparing the superabsorbent polymer of claim 1 , wherein the first alumina particles have a water contact angle of 10° to 150°.

5. The method of preparing the superabsorbent polymer of claim 1 , wherein the water-soluble ethylene-based unsaturated monomer includes one or more selected from the group consisting of an anionic monomer or salts thereof, a nonionic hydrophilic monomer, and an amino group-containing unsaturated monomer or a quaternary compound thereof, and in which the anionic monomer is acrylic acid, methacrylic acid, maleic anhydride, fumaric acid, crotonic acid, itaconic acid, 2-acryloylethane sulfonic acid, 2-methacryloylethane sulfonic acid, 2-(meth)acryloylpropane sulfonic acid, or 2-(meth)acrylamide-2-methyl propane sulfonic acid; the nonionic hydrophilic monomer is (meth)acrylamide, N-substituted (meth)acrylate, 2-hydroxyethyl(meth)acrylate, 2-hydroxypropyl(meth)acrylate, methoxy polyethylene glycol (meth)acrylate, or polyethylene glycol (meth)acrylate; and the amino group-containing unsaturated monomer is (N,N)-dimethylaminoethyl(meth)acrylate or (N,N)-dimethylaminopropyl(meth)acrylate.

6. The method of preparing the superabsorbent polymer of claim 1 , wherein the internal crosslinking agent includes one or more selected from the group consisting of bis(meth)acrylamide containing an alkyl group having 2 to 12 carbon atoms or polyethylene glycol having 2 to 12 carbon atoms, a poly(meth)acrylate of polyol containing an alkyl group having 2 to 12 carbon atoms or polyethylene glycol having 2 to 12 carbon atoms, and a poly(meth)allyl ether of polyol containing an alkyl group having 2 to 12 carbon atoms or polyethylene glycol having 2 to 12 carbon atoms.

7. The method of preparing the superabsorbent polymer of claim 1 , wherein the base polymer powder is pulverized and size-sorted such that it has a particle size of 150 μm to 850 μm.

8. The method of preparing the superabsorbent polymer of claim 1 , wherein the surface-crosslinking step is performed by heat treatment by raising an initial temperature of 20° C. to 130° C. to a maximum temperature of 140° C. to 200° C. for 10 min to 30 min and maintaining the maximum temperature for 5 min to 60 min.

9. The method of preparing the superabsorbent polymer of claim 1 , wherein the second alumina particles have a water contact angle of 10° to 150°.

10. The method of preparing the superabsorbent polymer of claim 1 , wherein mixing of the second alumina particles is performed at a speed of 100 to 3000 rpm.

11. The method of preparing the superabsorbent polymer of claim 1 , wherein mixing of the second alumina particles is performed for 2 s to 3 min.

12. The method of preparing the superabsorbent polymer of claim 1 , wherein the first alumina is included in an amount of 0.1 by weight with respect to 100 parts by weight of the base polymer powder, and the second alumina is included in an amount of 0.08 to 0.12 parts by weight with respect to 100 parts by weight of the surface-crosslinked superabsorbent polymer powder.

Assignees

• Lg Chemical Ltd

Inventors

• Hwang Min Ho
• Nam Hye Mi
• Lee Sang Gi
• Lee Soo Jin
• Jang Tae Hwan

Classifications

• B01J20/267

  Cross-linked polymers · CPC title

• A61L15/24

  Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds; Derivatives thereof {(A61L15/225 takes precedence)} · CPC title

• B01J20/28026

  Particles within, immobilised, dispersed, entrapped in or on a matrix, e.g. a resin · CPC title

• B01J20/3085

  Chemical treatments not covered by groups B01J20/3007 - B01J20/3078 · CPC title

• C08J2300/12

  Polymers characterised by physical features, e.g. anisotropy, viscosity or electrical conductivity · CPC title