Abstract

Devices, systems, and methods are directed to applying magnetohydrodynamic forces to liquid metal to eject liquid metal along a controlled pattern, such as a controlled three-dimensional pattern as part of additive manufacturing of an object. Porosity of one or more predetermined portions of objects fabricated from an accumulation of liquid metal droplets ejected using magnetohydrodynamic force can be controlled to form interfaces between support structures and parts within the object. Higher porosity along the interfaces, as compared to porosity along the support structures and the parts, can be useful for facilitating separation of the parts from the support structures.

First claim

What is claimed is:

1. A method of additive manufacturing, the method comprising:
providing a liquid metal in a fluid chamber at least partially defined by a housing, the fluid chamber having an inlet region and a discharge region;
directing a magnetic field through the housing;
moving the discharge region in a controlled three-dimensional pattern; and
delivering electric current between electrodes at least partially defining a firing chamber within the fluid chamber between the inlet region and the discharge region, the electric current intersecting the magnetic field in the liquid metal in the firing chamber to eject the liquid metal from the discharge region; and
changing a velocity of the liquid metal ejected from the discharge region therein controlling porosity of one or more predetermined portions of an accumulation of the ejected liquid metal on a build plate or on a previously deposited layer of metal.

2. The method of claim 1 , wherein controlling porosity of the one or more predetermined portions of the accumulation of the ejected liquid metal includes forming an interface between a support structure and a three-dimensional object in the accumulation, the support structure and the three-dimensional object having lower porosity than the interface.

3. The method of claim 2 , wherein the interface, the support structure and the three-dimensional object are formed of the same material.

4. The method of claim 2 , wherein the interface is frangible relative to the three-dimensional object.

5. The method of claim 4 , further comprising separating the three-dimensional object from the support structure through application of one or more of a compressive force and a shear force to the interface.

6. The method of claim 1 wherein changing the velocity of the liquid metal ejected from the discharge region includes changing a magnitude of the electric current delivered into the liquid metal in the firing chamber.

7. The method of claim 1 , wherein delivering electric current into the liquid metal in the firing chamber includes pulsing the electric current.

8. The method of claim 1 , wherein changing the velocity of the liquid metal ejected from the discharge region includes changing at least one of a magnitude and a duration of a pulse of the electric current.

9. A method of additive manufacturing, the method comprising:
providing a liquid metal in a fluid chamber at least partially defined by a housing, the fluid chamber having an inlet region and a discharge region;
directing a magnetic field through the housing;
moving the discharge region in a controlled three-dimensional pattern; and
delivering electric current between electrodes at least partially defining a firing chamber within the fluid chamber between the inlet region and the discharge region, the electric current intersecting the magnetic field in the liquid metal in the firing chamber to eject the liquid metal from the discharge region; and
changing a temperature of the liquid metal ejected from the discharge region therein controlling porosity of one or more predetermined portions of an accumulation of the ejected liquid metal on a build plate or on a previously deposited layer of metal.

10. The method of claim 9 , wherein changing the temperature of the liquid metal ejected from the discharge region includes reducing the temperature of the ejected liquid metal to increase porosity of a predetermined portion of the accumulation of the ejected liquid metal on the build plate or on the previously deposited layer of metal.

11. The method of claim 9 , wherein controlling porosity of the one or more predetermined portions of the accumulation of the ejected liquid metal includes forming an interface between a support structure and a three-dimensional object in the accumulation, the support structure and the three-dimensional object having lower porosity than the interface.

12. The method of claim 11 , wherein the interface, the support structure and the three-dimensional object are formed of the same material.

13. The method of claim 11 , wherein the interface is frangible relative to the three-dimensional object.

14. The method of claim 13 , further comprising separating the three-dimensional object from the support structure through application of one or more of a compressive force and a shear force to the interface.

15. The method of claim 9 , wherein delivering electric current into the liquid metal in the firing chamber includes pulsing the electric current.

Assignees

• Desktop Metal Inc

Inventors

• Fontana Richard Remo
• Gibson Michael Andrew

Classifications

• B33Y50/02

  for controlling or regulating additive manufacturing processes · CPC title

• B33Y10/00

  Processes of additive manufacturing · CPC title

• B22F3/115 Primary

  by spraying molten metal, i.e. spray sintering, spray casting · CPC title

• B33Y30/00

  Apparatus for additive manufacturing; Details thereof or accessories therefor · CPC title

• B22F2999/00

  Aspects linked to processes or compositions used in powder metallurgy · CPC title