Organic zinc catalyst, preparation method thereof, and method for preparing polyalkylene carbonate resin using the catalyst

Patent metadata

Field	Value
Publication number	US-10633488-B2
Application number	US-201715761323-A
Country	US
Kind code	B2
Filing date	Mar 8, 2017
Priority date	Mar 9, 2016
Publication date	Apr 28, 2020
Grant date	Apr 28, 2020

Abstract

The method for preparing an organic zinc catalyst includes the step of reacting a zinc precursor with a dicarboxylic acid in the presence of a polyether derivative to form a zinc dicarboxylate-based catalyst.

First claim

The invention claimed is:

1. A method for preparing an organic zinc catalyst, the method comprising a step of reacting a zinc precursor with a dicarboxylic acid having 3 to 20 carbon atoms in the presence of an aliphatic or aromatic polyether derivative having a functional group at a terminus thereof to form a zinc dicarboxylic acid-based catalyst,
wherein the polyether derivative includes an aliphatic or aromatic polyether derivative having a functional group at a terminus thereof which is substituted with an alkyl group having 1 to 18 carbon atoms, an aryl group having 6 to 18 carbon atoms, a vinyl group, an alkyl acrylate, a phosphate, or a sulfonyl group, and
wherein the polyether derivative is at least one compound selected from the group consisting of tetraethylene glycol dimethyl ether, diethylene glycol dibutyl ether, tetraethylene glycol dimethacrylate, benzyl-PEG (polyethylene glycol), a PEG aldehyde, and a PEG-phospholipid.

2. The method for preparing an organic zinc catalyst according to claim 1 , wherein the polyether derivative has a weight average molecular weight of 100 to 10,000.

3. The method for preparing an organic zinc catalyst according to claim 1 , wherein the polyether derivative is present in an amount of 0.1 to 10% by weight based on the zinc precursor.

4. The method for preparing an organic zinc catalyst according to claim 1 , wherein the zinc precursor is at least one zinc compound selected from the group consisting of zinc oxide (ZnO), zinc sulfate (ZnSO 4 ), zinc chlorate (Zn (ClO 3 ) 2 ), zinc nitrate (Zn(NO 3 )), and zinc hydroxide (Zn(OH) 2 ).

5. The method for preparing an organic zinc catalyst according to claim 1 , wherein the dicarboxylic acid is at least one selected from the group consisting of malonic acid, glutaric acid, succinic acid, adipic acid, terephthalic acid, isophthalic acid, homophthalic acid, and phenylglutaric acid.

6. The method for preparing an organic zinc catalyst according to claim 1 , wherein the reaction between the zinc precursor and the dicarhoxylic acid is present in an amount of about 1 to 1.5 mol based on 1 mol of the zinc precursor.

7. The method for preparing an organic zinc catalyst according to claim 1 , wherein the reaction between the zinc precursor and the dicarhoxylic acid is carried out under at least one liquid medium selected from the group consisting of toluene, hexane, dimethylformamide, ethanol, and water.

8. The method for preparing an organic zinc catalyst according to claim 1 , wherein the reaction between the zinc precursor and the dicarboxylic acid is carried out at a temperature of 50 to 1300° C. for 1 to 10 hours.

9. The method for preparing an organic zinc catalyst according to claim 1 , wherein the reaction between the zinc precursor and the dicarboxylic acid is carried out without addition of monocarboxylic acid.

Assignees

• Lg Chemical Ltd

Inventors

• Kim Sung-Kyoung
• Park Seung Young

Classifications

• B01J27/20

  Carbon compounds · CPC title

• B01J23/06

  of zinc, cadmium or mercury · CPC title

• B01J31/068

  Polyalkylene glycols · CPC title

• B01J31/04

  containing carboxylic acids or their salts {(B01J31/0277 - B01J31/0298 take precedence; multi-metal carboxylate complexes like Pd (II) acetate, i.e. Pd3 (OAc) 6 or Cr(II)acetate, i.e. Cr2(OAc)4 B01J31/2226)} · CPC title

• B01J31/0204

  Ethers · CPC title