Block copolymers having semi-crystalline blocks and compositions and articles made therefrom

Patent metadata

Field	Value
Publication number	US-10633465-B2
Application number	US-201715466207-A
Country	US
Kind code	B2
Filing date	Mar 22, 2017
Priority date	Mar 24, 2016
Publication date	Apr 28, 2020
Grant date	Apr 28, 2020

Abstract

Selectively hydrogenated block copolymers having semi-crystalline blocks hard blocks and copolymer soft blocks having a combination of excellent physical properties and solvent resistance have been discovered. The block copolymer comprises at least one A block of hydrogenated, polymerized 1,3-butadiene and at least one B block which is a random copolymer or a controlled distribution copolymer of conjugated diene and mono vinyl aromatic monomers in which the conjugated diene monomer units are selectively hydrogenated. Polar functionalized block embodiments of the block copolymers are also disclosed. Compositions comprising the block copolymer and articles made from the block copolymer have also been discovered. A method is disclosed which provides highly isotropic, high strength melt cast films of block copolymers.

First claim

The invention claimed is:

1. A selectively hydrogenated, semi-crystalline block copolymer consisting of at least one A block and at least one B block,
wherein the block copolymer has a structure of A-B, (A-B) n X, (A-B) n X-(A) m , or (A-B) n X-(B) m wherein n is from 2 to 10, m is from 1 to 10 and X is a coupling agent residue,
wherein the A block is a hydrogenated block of polymerized 1,3-butadiene having a vinyl content of 20 mol % or less, and the B block is a copolymer block of conjugated diene and mono vinyl aromatic monomer units,
wherein the vinyl aromatic monomer units are derived from mono vinyl aromatic monomers selected from the group consisting of styrene, methylstyrene, p-tert-butylstyrene, dimethylstyrene, alpha-methylstyrene, diphenyl ethylenes, and combinations thereof;
wherein the total amount of mono vinyl aromatic monomer in the block copolymer is from 10 to 55 wt. %; and
wherein the A block has a melting point in the range of 50° C. to 120° C. and a molecular weight from greater than 15 kg/mol to 80 kg/mol.

2. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 wherein the B block is a controlled distribution copolymer block of conjugated diene and mono vinyl aromatic monomer units wherein
i. the polymerized conjugated diene monomer units are hydrogenated;
ii. the amount of polymerized mono vinyl aromatic is between about 10 wt % and about 55 wt.; and
iii. the mono vinyl aromatic blockiness is less than 40%.

3. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 wherein the B block is a random copolymer block having a weight ratio of conjugated diene to mono vinyl aromatic monomer units from 90/10 to 60/40.

4. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 wherein the vinyl content of the conjugated diene units in the B block is from 30 to 90 mol %.

5. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 wherein the polymerized 1,3-butadiene in the A block is hydrogenated to a level of 90 mol % or greater.

6. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 wherein the conjugated diene monomer units of the B block are hydrogenated to a level of 90 mol % or greater.

7. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 wherein the mono vinyl aromatic monomer units of the B block are hydrogenated to a level of less than 10 mol %.

8. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 wherein the molecular weight of the A block is from 22 kg/mol to 50 kg/mol.

9. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 wherein the molecular weight of the B block is from 20 kg/mol to 200 kg/mol.

10. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 , wherein the copolymer has an order-disorder transition temperature of 150° C. or lower.

11. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 , wherein the copolymer has a tensile strength of at least 6 MPa.

12. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 , wherein the copolymer has an elongation at break of at least 300%.

13. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 , wherein the copolymer has a tensile strength of 6 MPa or greater and a degree of swelling in toluene after 8 hours immersion of less than 150 wt. %.

14. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 , wherein the copolymer exhibited a degree of swelling in cyclohexane after 8 hours immersion of less than 150 wt. %.

15. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 , wherein the copolymer has a degree of swelling in paraffinic oil after immersion for 2 weeks of less than 40 wt. %.

16. The selectively hydrogenated, semi-crystalline block copolymer of claim 1 , wherein the copolymer is free of chemical cross-links.

17. A composition comprising the selectively hydrogenated, semi-crystalline block copolymer of claim 1 and at least one component selected from the group consisting of thermoplastic resins, tackifiers, plasticizers, and waxes.

18. The composition of claim 17 wherein the selectively hydrogenated, semi-crystalline block copolymer comprises from 2 to 98 wt. % of the composition.

19. An article comprising the selectively hydrogenated, semi-crystalline block copolymer of claim 1 which is a melt extruded or solvent cast film, coextruded multilayer films, melt blown films, melt blown multilayer films, an injection molded piece, a coating, a foamed shape, a fiber, a bicomponent, a multi-component fiber, a melt-blown fiber, a fibrous mat, a bundle of fibers, a powder, a gel of various shapes, extruded tubes, extruded profiles, injection molded pieces, a slush molded piece, or a rotationally molded piece.

20. A method for preparing a drawn film of the selectively hydrogenated, semi-crystalline block copolymer of claim 1 , the method comprising:
a. melt extruding a film of the block copolymer at an extrusion rate,
b. stretching the extruded film by drawing the film at a draw rate greater than the extrusion rate, and
c. cooling the stretched film to room temperature to form the drawn film.

21. The method of claim 20 , wherein the drawn film has a ratio of tensile strength in a machine direction to transverse direction of less than 1.1.

22. The method of claim 20 , wherein the drawn film has a ratio of elastic modulus in a machine direction to transverse direction at elongations of up to 500% of less than 1.05.

23. The method of claim 20 , wherein a ratio of the draw rate to the extrusion rate is from 1.0 to 30.

Assignees

• Kraton Polymers Us Llc

Inventors

• Flood John E
• Willis Carl L
• Bening Robert C
• De Groot Hendrik
• Muyldermans Xavier D D J
• Williamson David T
• Handlin Jr Dale L
• Dossett Robert

Classifications

• C08J5/18

  Manufacture of films or sheets · CPC title

• C08J2353/02

  of vinyl aromatic monomers and conjugated dienes · CPC title

• C08L2205/02

  containing two or more polymers of the same C08L -group · CPC title

• C08L23/06

  Polyethylene · CPC title

• C08L2205/03

  containing three or more polymers in a blend · CPC title