Storage-stable one-component polyurethane prepregs and shaped bodies composed of polyurethane composition that have been produced therefrom

Patent metadata

Field	Value
Publication number	US-10626236-B2
Application number	US-201715816354-A
Country	US
Kind code	B2
Filing date	Nov 17, 2017
Priority date	Dec 2, 2016
Publication date	Apr 21, 2020
Grant date	Apr 21, 2020

Abstract

The invention relates to storage-stable one-component (1K) polyurethane prepregs and to shaped bodies produced therefrom.

First claim

The invention claimed is:

1. A prepreg comprising
A) a fibrous carrier, and
B) a storage stable one component polyurethane composition having a Tg of equal to or less than 38° C., as determined by in accordance with DIN EN ISO 11357-1 and the polyurethane composition comprises an internally blocked and/or blocking agent blocked di- and/or polyisocyanates and/or polyaddition compounds thereof.

2. The prepreg according to claim 1 , wherein the fibrous carrier is selected from the group consisting of glass, carbon, plastics, natural fibers, or mineral fiber materials.

3. The prepreg according to claim 1 , wherein the fibrous carrier present are textile structures made from nonwoven fabric, knitted fabric including loop-formed and loop-drawn knits, or non-knitted fabrics.

4. The prepreg according to claim 1 , wherein the di- and/or polyisocyanates are selected from the group consisting of isophorone diisocyanate (IPDI), hexamethylene diisocyanate (HDI), 4,4′-diisocyanatodicyclohexylmethane, 2,4′-diisocyanatodicyclohexylmethane, 2,2′-diisocyanatodicyclohexylmethane, alone or in mixtures of the isomers (H 12 MDI), 2-methylpentane diisocyanate (MPDI), 2,2,4-trimethylhexamethylene diisocyanate, 2,4,4-trimethylhexamethylene diisocyanate and mixtures thereof (TMDI), and norbornane diisocyanate (NBDI).

5. The prepreg according to claim 1 , wherein external blocking agents are selected from the group consisting of ethyl acetoacetate, diisopropylamine, methyl ethyl ketoxime, diethyl malonate, ε-caprolactam, 1,2,4-triazole, phenol or substituted phenols and 3,5-dimethylpyrazole.

6. The prepreg according to claim 1 , wherein the polyurethane composition B) comprises catalysts selected from the group consisting of dibutyltin dilaurate, zinc octoate, bismuth neodecanoate, tertiary amines, and 1,4-diazabicyclo[2.2.2]octane, in amounts of 0.001%-1% by weight.

7. The prepreg according to claim 1 , comprising a polyurethane composition B) containing uretdione groups and having a Tg of equal to or less than 38° C., comprising
a) at least one polyaddition compound containing uretdione groups, based on the polyaddition reaction of polyisocyanates containing aliphatic, (cyclo)aliphatic or cycloaliphatic uretdione groups and hydroxyl-containing compounds, where the polyaddition compound has a free NCO content of less than 5% by weight and a uretdione content of 3%-25% by weight, and
c) a catalyst.

8. The prepreg according to claim 7 , wherein the di- and/or polyisocyanates selected from isophorone diisocyanate (IPDI), hexamethylene diisocyanate (HDI), 4,4′-diisocyanatodicyclohexylmethane, 2,4′-diisocyanatodicyclohexylmethane, 2,2′-diisocyanatodicyclohexylmethane, alone or in mixtures of the isomers (H 12 MDI), 2-methylpentane diisocyanate (MPDI), 2,2,4-trimethylhexamethylene diisocyanate, 2,4,4-trimethylhexamethylene diisocyanate and mixtures thereof (TMDI), norbornane diisocyanate (NBDI).

9. The prepreg according to claim 8 , wherein di- and/or polyisocyanates selected from the group consisting of IPDI, HDI, TMDI and H 12 MDI for preparation of the uretdiones.

10. The prepreg according to claim 7 , comprising
B) at least one polyurethane composition containing uretdione groups and having Tg of equal to or less than 38° C., comprising
a) at least one polyaddition compound containing uretdione groups and
b) optionally at least one PUR catalyst,
c) optionally auxiliaries and additives known from polyurethane chemistry,
d) from 0.1% to 5% by weight of at least one catalyst selected from quaternary ammonium salts and/or quaternary phosphonium salts with halogens, hydroxides, alkoxides or organic or inorganic acid anions as counterion,
and
e) from 0.1% to 5% by weight of a cocatalyst selected from
e1) at least one epoxide
and/or
e2) at least one metal acetylacetonate and/or quaternary ammonium acetylacetonate and/or quaternary phosphonium acetylacetonate.

11. The prepreg according to claim 7 , further comprising
c) optionally auxiliaries and additives known from polyurethane chemistry,
d) from 0.1% to 5% by weight of at least one catalyst selected from quaternary ammonium salts and/or quaternary phosphonium salts with halogens, hydroxides, alkoxides or organic or inorganic acid anions as counterion,
and
e) from 0.1% to 5% by weight of at least one cocatalyst selected from
e1) at least one epoxide
and/or
e2) at least one metal acetylacetonate and/or quaternary ammonium acetylacetonate and/or quaternary phosphonium acetylacetonate.

12. The prepreg according to claim 7 , wherein the catalyst is selected from the group consisting of tetramethylammonium formate, tetramethylammonium acetate, tetramethylammonium propionate, tetramethylammonium butyrate, tetramethylammonium benzoate, tetraethylammonium formate, tetraethylammonium acetate, tetraethylammonium propionate, tetraethylammonium butyrate, tetraethylammonium benzoate, tetrapropylammonium formate, tetrapropylammonium acetate, tetrapropylammonium propionate, tetrapropylammonium butyrate, tetrapropylammonium benzoate, tetrabutylammonium formate, tetrabutylammonium acetate, tetrabutylammonium propionate, tetrabutylammonium butyrate and tetrabutylammonium benzoate, and tetrabutylphosphonium acetate, tetrabutylphosphonium formate and ethyltriphenylphosphonium acetate, tetrabutylphosphonium benzotriazolate, tetraphenylphosphonium phenolate and trihexyltetradecylphosphonium decanoate, methyltributylammonium hydroxide, methyltriethylammonium hydroxide, tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, tetrapentylammonium hydroxide, tetrahexylammonium hydroxide, tetraoctylammonium hydroxide, tetradecylammonium hydroxide, tetradecyltrihexylammonium hydroxide, tetraoctadecylammonium hydroxide, benzyltrimethylammonium hydroxide, benzyltriethylammonium hydroxide, trimethylphenylammonium hydroxide, triethylmethylammonium hydroxide, trimethylvinylammonium hydroxide, methyltributylammonium methoxide, methyltriethylammonium methoxide, tetramethylammonium methoxide, tetraethylammonium methoxide, tetrapropylammonium methoxide, tetrabutylammonium methoxide, tetrapentylammonium methoxide, tetrahexylammonium methoxide, tetraoctylammonium methoxide, tetradecylammonium methoxide, tetradecyltrihexylammonium methoxide, tetraoctadecylammonium methoxide, benzyltrimethylammonium methoxide, benzyltriethylammonium methoxide, trimethylphenylammonium methoxide, triethylmethylammonium methoxide, trimethylvinylammonium methoxide, methyltributylammonium ethoxide, methyltriethylammonium ethoxide, tetramethylammonium ethoxide, tetraethylammonium ethoxide, tetrapropylammonium ethoxide, tetrabutylammonium ethoxide, tetrapentylammonium ethoxide, tetrahexylammonium ethoxide, tetraoctylammonium methoxide, tetradecylammonium ethoxide, tetradecyltrihexylammonium ethoxide, tetraoctadecylammonium ethoxide, benzyltrimethylammonium ethoxide, benzyltriethylammonium ethoxide, trimethylphenylammonium ethoxide, triethylmethylammonium ethoxide, trimethylvinylammonium ethoxide, methyltributylammonium benzylate, methyltriethylammonium benzylate, tetramethylammonium benzylate, tetraethylammonium benzylate, tetrapropylammonium benzylate, tetrabutylammonium benzylate, tetrapentylammonium benzylate, tetrahexylammonium benzylate, tetraoctylammonium benzylate, tetradecylammonium benzylate, tetradecyltrihexylammonium benzylate, tetraoctadecylammonium benzylate, benzyltrimethylammonium benzylate, benzyltriethylammonium benzylate, trimethylphenylammonium benzylate, triethylmethylammonium benzylate, trimethylvinylammonium benzylate, tetramethylammonium fluoride, tetraethylammonium fluoride, tetrabutylammonium fluoride, tetraoctylammoni

Assignees

• Evonik Degussa Gmbh
• Evonik Operations Gmbh

Inventors

• Spyrou Emmanouil
• Loesch Holger
• Diesveld Andrea
• Kreischer Susanne
• Langkabel Eike
• Aldridge Ralph
• Gollan Elke

Classifications

• C08G18/246

  containing also tin-carbon bonds · CPC title

• C08G18/755

  and at least one isocyanate or isothiocyanate group linked to a secondary carbon atom of the cycloaliphatic ring, e.g. isophorone diisocyanate · CPC title

• C08K7/14 Primary

  Glass · CPC title

• C08G18/1875

  containing ammonium salts or mixtures of secondary of tertiary amines and acids · CPC title

• C08G18/242

  organometallic compounds containing tin-carbon bonds · CPC title