Method for recovering valuable metals and simultaneously preparing ceramsite by roasting cyanide tailing

Patent metadata

Field	Value
Publication number	US-10626053-B2
Application number	US-201816485121-A
Country	US
Kind code	B2
Filing date	May 28, 2018
Priority date	Dec 13, 2017
Publication date	Apr 21, 2020
Grant date	Apr 21, 2020

Abstract

A method for recovering valuable metals and simultaneously preparing ceramsite by roasting cyanide tailing belongs to the area of comprehensive recovery and high value utilization of metallurgical waste residue. In this method, cyanide tailings, bentonite, calcium chloride, coal powder and albite are mixed by ball milling according to certain weight ratio to get a mixture. After drying and roasting twice, dust is collected from the roasted ash, the obtained polymetallic ash is collected and treated. The secondary calcined material is cooled to obtain ceramsite. The invention volatilizes and recovers the valuable metal in the roasting and sintering process of cyanide tailings and directly prepares the ceramsite through reasonable batching, which achieves the effect of recycling cyanide tailings and high-value utilization, can create good economic and environmental benefits, and has significant effect of energy saving and consumption reduction.

First claim

What is claimed is:

1. A method for recovering valuable metals and simultaneously preparing ceramsite by roasting cyanide tailing, comprising the following steps:
(1) ball milling: a mixture of the cyanide tailing, bentonite, calcium chloride, pulverized coal and albite with a weight ratio of 100:(5-10):(4-10):(1-7):(5-20) is obtained via ball milling;
(2) prilling: the mixture obtained in step (1) is fed into a disc granulator for granulation, and raw material balls with particle size of 2-5 cm are obtained;
(3) drying: the raw material balls obtained in step (2) are dried at 100-200° C. for 3-5 hours to obtain dried raw material balls;
(4) primary roasting: the dried material balls obtained in step (3) are roasted at 700-900° C. for 0.5-3 hours to obtain primary calcined material and ash;
(5) secondary roasting: the primary calcined material obtain in step (4) is roasted at 1050-1200° C. for 0.5-3 hours, secondary calcined material and ash is obtained;
(6) dust collection: the ash obtained in steps (4) and (5) which contains polymetallic ash is collected and treated;
(7) cooling: the secondary calcined material obtained in step (5) is cooled to obtain the ceramsite.

2. The method for recovering valuable metals and simultaneously preparing ceramsite by roasting cyanide tailing according to claim 1 , wherein steps (4), (5) and (7) are carried out in the same roasting equipment.

Assignees

• Univ Beijing Technology

Inventors

• Wu Yufeng
• Pan Dean
• Sun Xudong
• Zuo Tieyong

Classifications

• C04B2235/606

  Drying · CPC title

• C04B35/62204

  using waste materials or refuse (clay-wares containing waste materials C04B33/132) · CPC title

• C04B35/6261

  Milling · CPC title

• C22B1/2406

  pelletizing · CPC title

• C22B1/02

  Roasting processes (C22B1/16 takes precedence) · CPC title