Aluminum alloy cladding material, manufacturing method therefor, and heat exchanger using said aluminum alloy cladding material

Patent metadata

Field	Value
Publication number	US-10625379-B2
Application number	US-201615742418-A
Country	US
Kind code	B2
Filing date	Jul 8, 2016
Priority date	Jul 8, 2015
Publication date	Apr 21, 2020
Grant date	Apr 21, 2020

Abstract

Provided is an aluminum alloy clad material including an aluminum alloy core material and a first brazing filler metal that is clad on one surface or both surfaces of the core material, wherein the core material and the first brazing filler metal each include an aluminum alloy having a predetermined composition, the existence density of Al—Mn based intermetallic compounds having a circle-equivalent diameter of at least 0.1 μm in the first brazing filler metal before brazing heating is at least 1.0×105 pieces/mm2, and the existence density of Al—Mn based intermetallic compounds having a circle-equivalent diameter of at least 2 μm in the first brazing filler metal after brazing heating is at least 300 pieces/mm2. Further provided are a method for producing the aluminum alloy clad material and a heat exchanger employing the aluminum alloy clad material.

First claim

The invention claimed is:

1. An aluminum alloy clad material comprising:
a core material comprising an aluminum alloy; and
a first brazing filler metal that is clad on one surface or both surfaces of the core material,
wherein the core material comprises an aluminum alloy containing Si: 0.05 to 1.50 mass %, Fe: 0.05 to 2.00 mass %, and Mn: 0.5 to 2.0 mass %, with a balance being Al and inevitable impurities,
wherein the first brazing filler metal comprises an aluminum alloy containing Si: 2.5 to 7.0 mass %, Fe: 0.05 to 1.20 mass %, Zn: 0.5 to 8.0 mass %, and Mn: 0.3 to 2.0 mass %, with the balance being Al and inevitable impurities,
wherein an existence density of Al—Mn based intermetallic compounds having a circle-equivalent diameter of at least 0.1 μm in the first brazing filler metal before brazing heating is at least 1.0×10 5 pieces/mm 2 , and
wherein an existence density of Al—Mn based intermetallic compounds having a circle-equivalent diameter of at least 2 μm in the first brazing filler metal after brazing heating is at least 300 pieces/mm 2 , wherein brazing heating is performed by heating the first brazing filler metal between 590 and 610 degrees Celsius for 2 to 10 minutes.

2. The aluminum alloy clad material according to claim 1 , wherein the first brazing filler metal comprises the aluminum alloy further containing at least one selected from Cu: 0.05 to 0.60 mass %, Ti: 0.05 to 0.30 mass %, Zr: 0.05 to 0.30 mass %, Cr: 0.05 to 0.30 mass %, and V: 0.05 to 0.30 mass %.

3. The aluminum alloy clad material according to claim 1 , wherein the first brazing filler metal comprises the aluminum alloy further containing at least one selected from Na: 0.001 to 0.050 mass % and Sr: 0.001 to 0.050 mass %.

4. The aluminum alloy clad material according to claim 1 , wherein the core material comprises the aluminum alloy further containing at least one selected from Mg: 0.05 to 0.50 mass %, Cu: 0.05 to 1.50 mass %, Ti: 0.05 to 0.30 mass %, Zr: 0.05 to 0.30 mass %, Cr: 0.05 to 0.30 mass %, and V: 0.05 to 0.30 mass %.

5. A method for producing the aluminum alloy clad material according to claim 1 , the method comprising:
a step of casting the aluminum alloys for the core material and the first brazing filler metal, respectively;
a hot rolling step of hot rolling an ingot of the cast first brazing filler metal to a predetermined thickness;
a cladding step of obtaining a clad material by cladding the first brazing filler metal that has been hot rolled to a predetermined thickness on one surface or both surfaces of an ingot of the core material;
a hot clad rolling step of hot rolling the clad material;
a cold rolling step of cold rolling the clad material that has been hot clad rolled; and
at least one annealing step of annealing the clad material carried out during or after the cold rolling step or during and after the cold rolling step,
wherein the step of hot rolling the first brazing filler metal comprises a heating stage, a holding stage, and a hot rolling stage,
wherein a rate of temperature rise until a temperature reaches 400° C. in the heating stage is 30° C./h or higher, and a rate of temperature rise from when the temperature reaches 400° C. until the temperature reaches a holding temperature in the holding stage is 60° C./h or lower,
wherein, in the holding stage, the holding temperature is between 450 and 560° C. inclusive and a holding time is at least one hour, and
wherein a time period during which the first brazing filler metal is at a temperature of at least 400° C. in the hot rolling stage is at least 5 minutes.

6. An aluminum alloy clad material comprising:
a core material comprising an aluminum alloy;
a first brazing metal that is clad on one surface of the core material; and
a second brazing filler metal that is clad on another surface of the core material,
wherein the core material comprises an aluminum alloy containing Si: 0.05 to 1.50 mass %, Fe: 0.05 to 2.00 mass %, and Mn: 0.5 to 2.0 mass %, with a balance being Al and inevitable impurities,
wherein the first brazing filler metal comprises an aluminum alloy containing Si: 2.5 to 7.0 mass %, Fe: 0.05 to 1.20 mass %, Zn: 0.5 to 8.0 mass %, and Mn: 0.3 to 2.0 mass %, with the balance being Al and inevitable impurities,
wherein the second brazing filler metal comprises an aluminum alloy containing Si: 2.5 to 13.0 mass % and Fe: 0.05 to 1.20 mass %, with the balance being Al and inevitable impurities,
wherein an existence density of Al—Mn based intermetallic compounds having a circle-equivalent diameter of at least 0.1 μm in the first brazing filler metal before brazing heating is at least 1.0×10 5 pieces/mm 2 , and
wherein an existence density of Al—Mn based intermetallic compounds having a circle-equivalent diameter of at least 2 μm in the first brazing filler after brazing heating is at least 300 pieces/mm 2 , wherein brazing heating is performed by heating the first brazing filler metal between 590 and 610 degrees Celsius for 2 to 10 minutes.

7. The aluminum alloy clad material according to claim 6 , wherein the first brazing filler metal comprises the aluminum alloy further containing at least one selected from Cu: 0.05 to 0.60 mass %, Ti: 0.05 to 0.30 mass %, Zr: 0.05 to 0.30 mass %, Cr: 0.05 to 0.30 mass %, and V: 0.05 to 0.30 mass %.

8. The aluminum alloy clad material according to claim 6 , wherein the first brazing filler metal comprises the aluminum alloy further containing at least one selected from Na: 0.001 to 0.050 mass % and Sr: 0.001 to 0.050 mass %.

9. The aluminum alloy clad material according to claim 6 , wherein the core material comprises the aluminum alloy further containing at least one selected from Mg: 0.05 to 0.50 mass %, Cu: 0.05 to 1.50 mass %, Ti: 0.05 to 0.30 mass %, Zr: 0.05 to 0.30 mass %, Cr: 0.05 to 0.30 mass %, and V: 0.05 to 0.30 mass %.

10. The aluminum alloy clad material according to claim 6 , wherein the second brazing filler metal comprises the aluminum alloy further containing at least one selected from Mn: 0.05 to 2.00 mass %, Cu: 0.05 to 1.50 mass %, Ti: 0.05 to 0.30 mass %, Zr: 0.05 to 0.30 mass %, Cr: 0.05 to 0.30 mass %, and V: 0.05 to 0.30 mass %.

11. The aluminum alloy clad material according to claim 6 , wherein the second brazing filler metal comprises the aluminum alloy further containing at least one selected from Na: 0.001 to 0.050 mass % and Sr: 0.001 to 0.050 mass %.

12. A method for producing the aluminum alloy clad material according to claim 6 , the method comprising:
a step of casting the aluminum alloys for the core material, the first brazing filler metal, and the second brazing filler metal, respectively;
a hot rolling step of hot rolling each of ingots of the cast first brazing filler metal and the cast second brazing filler metal to a predetermined thickness;
a cladding step of obtaining a clad material by cladding the first brazing filler metal that has been hot rolled to a predetermined thickness on one surface of the ingot of the core material, and by cladding the second brazing filler metal that has been hot rolled to a predetermined thickness on the other surface of the ingot of the core material;
a hot clad rolling step of hot rolling the clad material;
a cold rolling step of cold rolling the clad material that has been hot clad rolled; and
at least one annealing step of annealing the clad material carried out during or after the cold rolling step or during and after the cold rolling step,
wherein the step of hot rolling the first brazing filler metal comprises a heating stage, a holding stage, and a hot rolling stage,
wherein a rate of temperature rise until a temperature reaches 400° C. in the heating stage

Assignees

• Uacj Corp

Inventors

• Asano Taichi
• Harada Masaki
• Teshima Shoei
• Ando Makoto
• Narita Wataru
• Yamashita Naoki

Classifications

• B23K35/288 Primary

  with Sn or Zn · CPC title

• F28F21/089

  Coatings, claddings or bonding layers made from metals or metal alloys (F28F19/06 takes precedence) · CPC title

• F28D1/0325

  the plates having lateral openings therein for circulation of the heat-exchange medium from one conduit to another · CPC title

• F28D9/0025

  the conduits being formed by zig-zag bend plates · CPC title

• C23F2201/02

  Concrete, e.g. reinforced · CPC title