Silver promoted catalysts for oxidative coupling of methane

Patent metadata

Field	Value
Publication number	US-10625244-B2
Application number	US-201615208862-A
Country	US
Kind code	B2
Filing date	Jul 13, 2016
Priority date	Jul 15, 2015
Publication date	Apr 21, 2020
Grant date	Apr 21, 2020

Abstract

An oxidative coupling of methane (OCM) catalyst composition comprising one or more oxides doped with Ag; wherein one or more oxides comprises a single metal oxide, mixtures of single metal oxides, a mixed metal oxide, mixtures of mixed metal oxides, or combinations thereof; and wherein one or more oxides is not La2O3 alone. A method of making an OCM catalyst composition comprising calcining one or more oxides and/or oxide precursors to form one or more calcined oxides, wherein the one or more oxides comprises a single metal oxide, mixtures of single metal oxides, a mixed metal oxide, mixtures of mixed metal oxides, or combinations thereof, wherein the one or more oxides is not La2O3 alone, and wherein the oxide precursors comprise oxides, nitrates, carbonates, hydroxides, or combinations thereof; doping the one or more calcined oxides with Ag to form the OCM catalyst composition; and thermally treating the OCM catalyst composition.

First claim

What is claimed is:

1. An oxidative coupling of methane (OCM) catalyst composition comprising a La—Ce oxide doped with silver (Ag), wherein the Ag comprises Ag nanoparticles, Ag microparticles, Ag nanowires, or combinations thereof; wherein at least a portion of the Ag nanoparticles, Ag microparticles, Ag nanowires, or combinations thereof are retained onto the La—Ce oxide; wherein the Ag nanoparticles are characterized by an average size of from about 1 nm to about 500 nm; wherein the Ag microparticles are characterized by an average size of from about 0.5 microns to about 50 microns; wherein the Ag nanowires are characterized by an average diameter of from about 1 nm to about 500 nm, and by an average length of from about 0.5 microns to about 50 microns; wherein the La—Ce oxide comprises a single metal oxide of lanthanum (III) and a single metal oxide of cerium (IV); and wherein the OCM catalyst composition is characterized by a lanthanum (III) amount of from about 85.0 wt. % to about 95.0 wt. % and by a Ag amount of from about 1.0 wt. % to about 5.0 wt. %, based on the total weight of the OCM catalyst composition.

2. The OCM catalyst composition of claim 1 further comprising one or more additional oxides, wherein the one or more additional oxides comprises a single metal oxide, mixtures of single metal oxides, a mixed metal oxide, mixtures of mixed metal oxides, or combinations thereof.

3. The OCM catalyst composition of claim 2 , wherein the one or more additional oxides comprises (i) a single metal oxide having one metal cation selected from the group consisting of alkali metal cations, alkaline earth metal cations, rare earth element cations other than lanthanum (III) or cerium (IV), and cations of elements that can form oxides with redox properties; or (ii) a mixture of single metal oxides.

4. The OCM catalyst composition of claim 2 , wherein the one or more additional oxides comprises (a) a mixed metal oxide having two or more different metal cations, wherein each metal cation can be independently selected from the group consisting of alkali metal cations, alkaline earth metal cations, rare earth element cations, and cations of elements that can form oxides with redox properties; or (b) a mixture of mixed metal oxides.

5. The OCM catalyst composition of claim 2 , wherein the one or more additional oxides comprises alkali metal oxides, alkaline earth metal oxides, oxides of elements that can form oxides with redox properties, rare earth element oxides other than La 2 O 3 and/or CeO 2 , or combinations thereof.

6. The OCM catalyst composition of claim 5 , wherein the alkali metal oxides comprise cations of lithium (Li), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), or combinations thereof.

7. The OCM catalyst composition of claim 5 , wherein the alkaline earth metal oxides comprise cations of magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), or combinations thereof.

8. The OCM catalyst composition of claim 5 , wherein the rare earth element oxides other than La 2 O 3 and/or CeO 2 further comprise cations of lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), samarium (Sm), europium (Eu), dysprosium (Dy), holmium (Ho), erbium (Er), ytterbium (Yb), or combinations thereof.

9. The OCM catalyst composition of claim 5 , wherein the oxides of elements that can form oxides with redox properties comprise cations of manganese (Mn), tungsten (W), vanadium (V), tin (Sn), antimony (Sb), phosphorus (P), arsenic (As), chromium (Cr), bismuth (Bi), gallium (Ga), rhenium (Re), lead (Pb), iron (Fe), cobalt (Co), nickel (Ni), copper (Cu), niobium (Nb), molybdenum (Mo), or combinations thereof.

10. The OCM catalyst composition of claim 1 further comprising a support, wherein at least a portion of the OCM catalyst composition contacts, coats, is embedded in, is supported by, and/or is distributed throughout at least a portion of the support; wherein the support comprises MgO, Al 2 O 3 , SiO 2 , ZrO 2 , or combinations thereof; and wherein the support is in the form of particles, pellets, monoliths, foams, honeycombs, or combinations thereof.

11. The OCM catalyst composition of claim 2 , wherein the one or more additional oxides comprises Ca/CeO 2 , Mn/Na 2 WO 4 , Li 2 O, Na 2 O, Cs 2 O, WO 3 , Mn 3 O 4 , CaO, MgO, SrO, BaO, CaO—MgO, CaO—BaO, Li/MgO, MnO, W 2 O 3 , SnO 2 , Yb 2 O 3 , Sm 2 O 3 , MnO—W 2 O 3 , MnO—W 2 O 3 —Na 2 O, MnO—W 2 O 3 —Li 2 O, SrO/La 2 O 3 , Ce 2 O 3 , La/MgO, La 2 O 3 —CeO 2 —Na 2 O, La 2 O 3 —CeO 2 —CaO, Na 2 O—MnO—WO 3 —La 2 O 3 , La 2 O 3 —CeO 2 —MnO—WO 3 —SrO, Na—Mn—La 2 O 3 /Al 2 O 3 , Na—Mn—O/SiO 2 , Na 2 WO 4 —Mn/SiO 2 , Na 2 WO 4 —Mn—O/SiO 2 , Na/Mn/O, Na 2 WO 4 , Mn 2 O 3 /Na 2 WO 4 , Mn 3 O 4 /Na 2 WO 4 , MnWO 4 /Na 2 WO 4 , MnWO 4 /Na 2 WO 4 , Mn/WO 4 , Na 2 WO 4 /Mn, Sr/Mn—Na 2 WO 4 , or combinations thereof.

12. An oxidative coupling of methane (OCM) catalyst composition comprising a lanthanum (III) and cerium (IV) mixture doped with silver (Ag); wherein the lanthanum (III) and cerium (IV) mixture comprises two or more oxides; wherein the Ag comprises Ag nanoparticles, Ag microparticles, Ag nanowires, or combinations thereof; wherein at least a portion of the Ag nanoparticles, Ag microparticles, Ag nanowires, or combinations thereof are retained onto the two or more oxides; wherein the Ag nanoparticles are characterized by an average size of from about 1 nm to about 500 nm; wherein the Ag microparticles are characterized by an average size of from about 0.5 microns to about 50 microns; wherein the Ag nanowires are characterized by an average diameter of from about 1 nm to about 500 nm, and by an average length of from about 0.5 microns to about 50 microns; and wherein the OCM catalyst composition is characterized by a lanthanum (III) amount of from about 75.0 wt. % to about 98.0 wt. % and by a Ag amount of from about 0.5 wt. % to about 10.0 wt. %, based on the total weight of the OCM catalyst composition.

13. The OCM catalyst composition of claim 12 , wherein lanthanum (III) comprises La 2 O 3 , and optionally La(OH) 3 ; and wherein cerium (IV) comprises CeO 2 .

14. The OCM catalyst composition of claim 12 comprising (i) from about 1 wt. % to about 5 wt. % Ag; (ii) from about 85.0 wt. % to about 95.0 wt. % lanthanum (III); and (iii) from about 4.0 wt. % to about 10.0 wt. % cerium (IV).

15. A supported oxidative coupling of methane (OCM) catalyst capable of catalyzing an OCM reaction, the supported OCM catalyst comprising silver (Ag) doped Mn/Na 2 WO 4 and a metal oxide support, wherein the supported OCM catalyst has greater CH 4 conversion and C 2+ hydrocarbon selectivity as compared to the CH 4 conversion and C 2+ hydrocarbon selectivity, respectively, of an otherwise similar Mn/Na 2 WO 4 metal oxide supported OCM catalyst that has not been doped with Ag.

16. The supported OCM catalyst of claim 15 , wherein the supported OCM catalyst's selectivity for C 2+ hydrocarbons is greater than a theoretical selectivity limit for C 2+ hydrocarbons for the oxidative coupling of methane reaction; and wherein the supported OCM catalyst's life is greater than the life of an otherwise similar Mn/Na 2 WO 4 metal oxide supported OCM catalyst that has not been doped with Ag.

17. The OCM catalyst composition of claim 1 , wherein at least a portion of an outer surface of the Ag nanoparticles, Ag microparticles, Ag nanowires, or combinations thereof is unobstructed by the one or more oxides from contact with methane.

18. The OCM catalyst composition of claim 1 , wherein the Ag comprises Ag nanoparticles, and wherein the Ag nanoparticles are

Assignees

• Sabic Global Technologies Bv

Inventors

• Liang Wugeng
• SARSANI Vidya Sagar Reddy
• West David
• Perez Hector
• Mamedov Aghaddin
• Lengyel Istvan
• Lowrey James

Classifications

• B01J23/66

  Silver or gold · CPC title

• B01J23/002

  Mixed oxides other than spinels, e.g. perovskite · CPC title

• C07C2523/68

  with arsenic, antimony, bismuth, vanadium, niobium, tatalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium · CPC title

• B01J37/0236

  Drying, e.g. preparing a suspension, adding a soluble salt and drying · CPC title

• B01J37/0205

  in several steps · CPC title